Method of producing monolithic catalyst for purification of exhaust gas
Assignee: Nissan Motor Co Ltd
•
Filing: 1984-11-15
•
Granted: 1986-05-06
•
Expires: 2004-11-15
Abstract
Abstract A method of producing a monolithic three-way catalyst for the purification of exhaust gases of internal combustion engines. First, a mixed oxide coating is provided to a monolithic carrier by treating the carrier with a coating slip in which an active alumina powder containing cerium in oxide form is dispersed together with a ceria powder and then baking the treated carrier. Next, Pt, Rh and/or Pd are deposited on the oxide coating by a known thermal decomposition process. The addition of the ceria powder to the coating slip is effective in enhancing the CO, HC and NO x conversions and durability of the produced catalyst at high temperatures. Preferably the content of Ce in the active alumina powder is 1-5 wt %, and, in the coating after baking, Ce of the ceria powder amounts to 5-50 wt % of the coating. Optionally a zirconia powder too may be added to the coating slip such that Zr of the zirconia powder amounts to 1-10 wt % of the coating.
Inventors
- 👤 Keiichi Sawamura
- 👤 Yoshiyuki Eto
- 👤 Junichi Mine
- 👤 Koji Masuda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 17:04
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/34; B01D53/92; B01D53/94; B01D53/9445; B01D53/945; B01J; B01J23/00; B01J23/38; B01J23/54; B01J23/56; B01J23/63; B01J37/00; B01J37/02; B01J37/024; Y; Y02; Y02T; Y02T10/00; Y02T10/10; Y02T10/12
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
187 words
A method of producing a monolithic catalyst for simultaneous oxidation of carbon monoxide and hydrocarbons and reduction of nitrogen oxides in exhaust gases of internal combustion engines, the method including the steps of providing an active alumina base coating to a monolithic carrier by treating the monolithic carrier with a coating slip in which an active alumina powder containing cerium oxide, which is formed by thermal decomposition of a cerium salt applied to said active alumina as a solution, is dispersed and then baking the treated carrier, and depositing at least one noble metal selected from the group consisting of Pt, Rh and Pd on said coating by thermal decomposition of an aqueous solution of a compound of each selected noble metal on said coating, characterized in that a ceria powder is additionally dispersed in said coating slip; wherein the amount of said ceria powder is such that, in said coating, Ce of said ceria powder amounts to 5 to 50% by weight of said coating, and wherein the content of Ce in said active alumina powder is in the range from 1 to 5% by weight.
Claim 2
Independent Claim
187 words
A method of producing a monolithic catalyst for simultaneous oxidation of carbon monoxide and hydrocarbons and reduction of nitrogen oxides in exhaust gases of internal combustion engines, the method including the steps of providing an active alumina base coating to a monolithic carrier by treating the monolithic carrier with a coating slip in which an active alumina powder containing cerium oxide, which is formed by thermal decomposition of a cerium salt applied to said active alumina as a solution, is dispersed and then baking the treated carrier, and depositing at least one noble metal selected from the group consisting of Pt, Rh and Pd on said coating by thermal decomposition of an aqueous solution of a compound of each selected noble metal on said coating, characterized in that a ceria powder is additionally dispersed in said coating slip; wherein the amount of said ceria powder is such that, in said coating, Ce of said ceria powder amounts to 5 to 50% by weight of said coating, and wherein the content of Ce in said active alumina powder is in the range from 1 to 5% by weight.
Claim 3
Dependent Claim
43 words
A method according to claim 1, further comprising the step of additionally dispersing such an amount of a zirconia powder in said coating slip that, in said coating, Zr of said zirconia powder amounts to 1 to 10% by weight of said coating.
Claim 4
Dependent Claim
27 words
A method according to claim 1, wherein the baking for producing said coating is carried out at a temperature in the range from 500° to 700° C.
Claim 5
Dependent Claim
23 words
A method according to claim 1, wherein said coating slip is an aqueous suspension and comprises hydrated alumina besides said active alumina powder.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-05-05 | 1989-11-04 | 1990-05-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-05-05 | 1993-11-04 | 1994-05-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-05-05 | 1997-11-04 | 1998-05-06 | $7700.00 | Window Closed / Lapsed |