Solvent-free hotmelt adhesive comprising a polyester polyurethane containing carboxyl and sulfonate groups
Assignee: Beiersdorf AG
•
Filing: 1985-03-07
•
Granted: 1986-04-01
•
Expires: 2005-03-07
Abstract
Abstract The invention relates to a solvent-free hotmelt adhesive based on polyester polyurethanes which are suitable for the production of composite structures and, in particular, laminated parts for the interior finishing of motor vehicles. The hotmelt adhesive is based on polyester polyurethanes which are obtained by reacting organic polyester polyols and low molecular weight diols as chain-extending agents and which are modified by the incorporation of carboxyl and sulfonate groups. In addition to these modified polyester polyurethanes, the hotmelt adhesive may also contain unmodified polyester polyurethanes and crosslinking agents. The hotmelt adhesive is preferably in the form of a film or an in situ coating on a substrate. The hotmelt adhesive is produced by known processes of the type normally used for producing the known, unmodified polyester polyurethanes.
Inventors
- 👤 Jurgen Kramer
- 👤 Horst Muller-Albrecht
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 20:07
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/0804; C08G18/0819; C08G18/28; C08G18/40; C08G18/42; C08G18/4236; C08G18/4238; C08G18/65; C08G18/66; C08G18/6633; C08G18/6637; C08G18/664; C09; C09J; C09J175/00; C09J175/04; C09J175/06; C08G2170/00; C08G2170/20; Y; Y10; Y10S; Y10S528/00; Y10S528/905
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
142 words
A solvent-free hotmelt adhesive comprising a polyester polyurethane characterized in that said polyester polyurethane: (i) when mixed with methyl-ethyl-ketone in a weight ratio of 85 parts of a methyl-ethyl-ketone to 15 parts of polyester polyurethane does not form a solution at 20° C.; (ii) is prepared by reacting an organic diisocyanate, a polyester polyol, from 1 to 4 moles of low molecular weight diol per mole of polyester, from 0.025 to 0.3 moles of dimethylol propionic acid per mole of polyester, and from 0.025 to 0.2 moles of sulfonate diols per mole of polyester, at an NCO:OH equivalent ratio of from 0.9:1 to 1.05:1; (iii) contains from 0.01 to 1% by weight of carboxyl groups; (iv) contains from 0.1 to 10 milliequivalent of sulfonate groups per 100 grams of polyurethane, and (v) contains from 4 to 20% by weight of urethane groups.
Claim 2
Dependent Claim
142 words
A solvent-free hotmelt adhesive comprising a polyester polyurethane characterized in that said polyester polyurethane: (i) when mixed with methyl-ethyl-ketone in a weight ratio of 85 parts of a methyl-ethyl-ketone to 15 parts of polyester polyurethane does not form a solution at 20° C.; (ii) is prepared by reacting an organic diisocyanate, a polyester polyol, from 1 to 4 moles of low molecular weight diol per mole of polyester, from 0.025 to 0.3 moles of dimethylol propionic acid per mole of polyester, and from 0.025 to 0.2 moles of sulfonate diols per mole of polyester, at an NCO:OH equivalent ratio of from 0.9:1 to 1.05:1; (iii) contains from 0.01 to 1% by weight of carboxyl groups; (iv) contains from 0.1 to 10 milliequivalent of sulfonate groups per 100 grams of polyurethane, and (v) contains from 4 to 20% by weight of urethane groups.
Claim 3
Dependent Claim
23 words
The adhesive of claim 1 wherein the polyester polyol used to prepare the polyester polyurethane is a polyester diol containing alcoholic hydroxyl groups.
Claim 4
Dependent Claim
45 words
The adhesive of claim 1 where (iii) the amount of carboxyl groups is from 0.02 to 0.6% by weight, (iv) the amount of sulfonate groups is from 0.5 to 5 milliequivalents, and (v) the amount of urethane groups is from 6 to 16% by weight.
Claim 5
Dependent Claim
84 words
The adhesive of claim 1 further comprising a polyester polyurethane free from carboxyl and sulfonate groups produced by reacting organic diisocyanates with polyester polyols and low molecular weight diols at an NCO:OH equivalent ratio of from 0.9:1 to 1.05:1, with from 0.2 to 1.5 moles of diol being used per mole of polyester polyol, with said adhesive further characterized in that the weight ratio of polyester polyurethanes containing carboxyl and sulfonate groups to polyester polyurethane free from such groups is from 10:1 to 1:10.
Claim 6
Dependent Claim
17 words
The adhesive of claim 4 wherein the weight ratio of said polyurethanes is from 4:1 to 1:4.
Claim 7
Dependent Claim
11 words
The adhesive of claim 1 in the form of a film.
Claim 8
Dependent Claim
16 words
The adhesive of claim 1 in the form of an in situ coating on a substrate.
Claim 9
Dependent Claim
21 words
In the production of composite structures using a hotmelt adhesive, the improvement wherein the adhesive is the adhesive of claim 1.
Claim 10
Dependent Claim
31 words
In the production of composite structures using a hotmelt adhesive by vacuum deep drawing, deep-draw forming or vacuum deep-draw forming, the improvement wherein the adhesive is the adhesive of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-03-31 | 1989-09-30 | 1990-04-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-03-31 | 1993-09-30 | 1994-04-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-03-31 | 1997-09-30 | 1998-04-01 | $7700.00 | Window Closed / Lapsed |