Dental cement composition comprising poly(carboxylic acid) and chelating agent

Claim 2

A cement-forming liquid for use as a component of a poly(carboxylate) cement, consisting essentially of an aqueous solution of (i) from 20 to 65% by weight, based on the total composition, of a water soluble poly(carboxylic acid) having a relative viscosity of from 1.05 to 2.00 measured with a capillary viscometer of a 1% by weight to volume solution of the poly(carboxylic acid) in twice molar sodium hydroxide solution at 25° C. relative to the viscosity of the twice molar sodium hydroxide solution together with (ii) a water soluble chelating agent.

Claim 3

A cement-forming liquid according to claim 1, in which said chelating agent is selected from the group consisting of compounds containing both chelating hydroxyl and carboxyl groups and metal chelates.

Claim 4

A cement-forming liquid according to claim 1, in which the poly(carboxylic acid) is a homopolymer of acrylic acid or a copolymer of acrylic acid and at least one comonomer selected from the group consisting of 2-chloroacrylic acid, 3-chloroacrylic acid, 2-bromoacrylic acid, 3-bromoacrylic acid, methacrylic acid, itaconic acid, maleic acid, glutaconic acid, aconitic acid, citraconic acid, mesaconic acid, fumaric acid, tiglicinic acid, acrylamide, acrylonitrile, vinyl chloride, allyl chloride, vinyl acetate and 2-hydroxymethyl methacrylate.

Claim 5

A cement-forming liquid according to claim 1, in which said chelating agent is a compound containing both chelating hydroxyl and carboxyl groups, and which contains from 20 to 65% of the poly(carboxylic acid), based on the total composition and from 0.01 to about 20% by weight of said chelating agent, based on the weight of said poly(carboxylic acid).

Claim 6

A cement-forming liquid according to claim 4, wherein the chelating agent is tartaric acid or citric acid.

Claim 7

A cement forming liquid according to claim 1 that contains from 0.01 to 10% by weight of the chelating agent based on the weight of the poly(carboxylic acid).

Claim 8

A cement-forming liquid according to claim 1 in which the chelating agent is a compound containing chelating hydroxy or carboxyl groups.

Claim 9

A cement-forming liquid according to claim 7 in which the chelating agent is tartaric acid or citric acid.

Claim 10

A cement-forming liquid according to claim 1 in which the chelating agent is a di- or tri-valent metal chelate.

Claim 11

An aqueous setting solution for poly(carboxylate) dental cements consisting essentially of: (A) 20 to 65% of a polymer having a relative viscosity of from 1.05 to 2.00 measured with a capillary viscometer of a 1% by weight to volume solution of the polymer in twice molar sodium hydroxide solution at 25° C. relative to the viscosity of the twice molar sodium hydroxide solution and selected from the group consisting of polyacrylic acid and a copolymer of acrylic acid and at least one monomer selected from the group consisting of 2-chloroacrylic acid, 2-bromoacrylic acid, maleic acid, fumaric acid, itaconic acid, methacrylic acid, mesaconic acid, acrylonitrile, vinyl acetate, and 2-hydroxylethyl methacrylate; and (B) from 0.01 to about 20% by weight based on the weight of said polymer of polybasic carboxylic acid selected from the group consisting of citric acid and tartaric acid.

Claim 12

An aqueous setting solution for poly(carboxylate) dental cements consisting essentially of: (A) 20 to 65% of a polymer having a relative viscosity of from 1.05 to 2.00 measured with a capillary viscometer of a 1% by weight to volume solution of the polymer in twice molar sodium hydroxide solution at 25° C. relative to the viscosity of the twice molar sodium hydroxide solution and selected from the group consisting of polyacrylic acid and a copolymer of acrylic acid and at least one monomer selected from the group consisting of 2-chloroacrylic acid, 2-bromoacrylic acid, maleic acid, fumaric acid, itaconic acid, methacrylic acid, mesaconic acid, acrylonitrile, vinyl acetate, and 2-hydroxylethyl methacrylate; and (B) from 0.01 to about 20% by weight based on the weight of said polymer of polybasic carboxylic acid selected from the group consisting of citric acid and tartaric acid.

Claim 13

The solution according to claim 10, which contains from 40 to 65% by weight of said polymer, based on the total composition.

Claim 14

The solution according to claim 10, which contains from 44 to 55% by weight of said polymer, based on the total composition.

Claim 15

The solution according to claim 12, wherein the relative viscosity of said polymer is from 1.10 to 1.60.

Claim 16

A cement-forming liquid according to claim 10, wherein said polymer is polyacrylic acid and said polybasic carboxylic acid is tartaric acid.

Claim 17

A cement-forming liquid according to claim 1, wherein said poly(carboxylic acid) is a homopolymer of acrylic acid and said chelating agent is tartaric acid.