Optical fibre manufacture
Assignee: STC PLC
•
Filing: 1985-06-21
•
Granted: 1986-02-04
•
Expires: 2005-06-21
Abstract
Abstract An optical fibre is provided with a moisture barrier layer by exposing a plastics coating on the fibre to a pulsed plasma in order to modify the surface, for instance by implantation of silicon and/or by the deposition on the plastics layer an inorganic layer such as a non-stoichiometric composition of silicon and carbon or silicon and nitrogen.
Inventors
- 👤 Thomas M. Jackson
- 👤 Rudolf A. H. Heinecke
- 👤 Sureshchandra M. Ojha
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:27
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/44; G02B6/4401; G02B6/4415; G02B6/4427; C; C03; C03C; C03C25/00; C03C25/10; C03C25/24; C03C25/40; C03C25/104; G02B6/4402
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
55 words
A method of providing a coating with low water permeability upon a glass optical fibre, which method includes the step of using a pulsed plasma at reduced pressure and at a power level providing dissociation down to atomic species to modify the surface of a plastics coating with which the optical fibre has been provided.
Claim 2
Independent Claim
55 words
A method of providing a coating with low water permeability upon a glass optical fibre, which method includes the step of using a pulsed plasma at reduced pressure and at a power level providing dissociation down to atomic species to modify the surface of a plastics coating with which the optical fibre has been provided.
Claim 3
Dependent Claim
33 words
A method as claimed in claim 1, wherein at least one aspect of the pulsed plasma induced modification takes the form of changing the structure of the surface region of material already present.
Claim 4
Dependent Claim
25 words
A method as claimed in claim 2, wherein the pulsed plasma induced modification also involves an etching away of some of the material already present.
Claim 5
Dependent Claim
30 words
A method as claimed in claim 1, wherein at least one aspect of the pulsed plasma induced modification takes the form of adding fresh material to the material already present.
Claim 6
Dependent Claim
34 words
A method as claimed in claim 1, wherein the pulsed plasma induced modification involves both the changing of the structure of the surface region of material already present and the adding of fresh material.
Claim 7
Dependent Claim
37 words
A method as claimed in claim 1, which method includes the step of using pulsed plasma in an atomosphere consisting of or including a mixture of argon and hydrogen to modify the surface of the plastics coating.
Claim 8
Dependent Claim
36 words
A method as claimed in claim 1, which method includes the step of using pulsed plasma to implant material into the surface of the plastics coating to chemically bond with the material of the plastics coating.
Claim 9
Dependent Claim
13 words
A method as claimed in claim 7, wherein said implanted material is silicon.
Claim 10
Dependent Claim
34 words
A method as claimed in claim 8, wherein the implantation of silicon is succeeded by the step of using pulsed plasma to coat the modified surface with an inorganic layer whose composition includes silicon.
Claim 11
Dependent Claim
20 words
A method as claimed in claim 9, wherein said inorganic layer is a generally non-stoichiometric composition of silicon and carbon.
Claim 12
Dependent Claim
20 words
A method as claimed in claim 9, wherein said inorganic layer is a generally non-stoichiometric composition of silicon and nitrogen.
Claim 13
Dependent Claim
36 words
A method as claimed in claim 1, which method includes the step of using pulsed plasma to cause liquid absorbed into the surface of the plastics coating to react chemically with the material of that coating.
Claim 14
Dependent Claim
28 words
A method as claimed in claim 12, wherein said chemical reaction is such as to cause silicon to be chemically bonded with the material of the plastics coating.
Claim 15
Dependent Claim
45 words
A method as claimed in claim 13, wherein the step of causing silicon to be chemically bonded with the material of plastics coating is succeeded by the step of using pulsed plasma to coat the modified surface with an inorganic layer whose composition includes silicon.
Claim 16
Dependent Claim
23 words
A method as claimed in claim 14, wherein the composition of the deposited layer is a generally non-stoichiometric composition of silicon and carbon.
Claim 17
Dependent Claim
23 words
A method as claimed in claim 14, wherein the composition of the deposited layer is a generally non-stoichiometric composition of silicon and nitrogen.
Claim 18
Dependent Claim
79 words
A method as claimed in claim 1, wherein pulsed plasma is used to modify the surface of the plastics coating by the promotion of crosslinking, wherein pulse plasma is used to deposit material matching the crosslinked material, whereby a grading is provided between the bulk material of the coating and the deposited material, and wherein the atmosphere to which the coating is exposed in the pulsed plasma is changed to grade the deposit from organic material to inorganic material.
Claim 19
Dependent Claim
16 words
A method as claimed in claim 17, wherein the inorganic material is a compound of silicon.
Claim 20
Dependent Claim
16 words
A method as claimed in claim 17, wherein the inorganic material is a compound of titanium.
Claim 21
Dependent Claim
14 words
A method as claimed in claim 17, wherein the inorganic material is a nitride.
Claim 22
Dependent Claim
14 words
A method as claimed in claim 17, wherein the inorganic material is a carbide.
Claim 23
Dependent Claim
13 words
A method as claimed in claim 17, wherein the inorganic material is alumina.
Claim 24
Dependent Claim
37 words
A method as claimed in claim 17, wherein the atmosphere is further changed to grade the deposit back from the inorganic layer to a further organic layer which further organic layer is a layer of hydrophobic material.
Claim 25
Dependent Claim
15 words
A method as claimed in claim 23, wherein the hydrophobic material is a fluorocarbon polymer.
Claim 26
Dependent Claim
22 words
A method as claimed in claim 1, wherein the coating is exposed to pulsed plasma in a cascaded arrangement of reaction chambers.
References Cited (Backward Citations)
US313029A
Cited
US3288638A
Cited
US3471316A
Cited
USB313029I5
Cited
US3677799A
Cited
DE2444926A1
Cited
US4091166A
Cited
US4410567A
Cited
US4227907A
Cited
US4396641A
Cited
US4402993A
Cited
GB2105371A
Cited
GB2105729A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-02-03 | 1989-08-05 | 1990-02-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-02-03 | 1993-08-05 | 1994-02-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-02-03 | 1997-08-05 | 1998-02-04 | $7700.00 | Window Closed / Lapsed |