Substantially pore-free shaped articles of polycrystalline silicon carbide, and a process for their manufacture by isostatic hot-pressing
Assignee: Elektroschmelzwerk Kempten GmbH
•
Filing: 1984-09-07
•
Granted: 1985-12-24
•
Expires: 2004-09-07
Abstract
Abstract The invention is substantially pore-free shaped articles consisting essentially of polycrystalline silicon nitride and polycrystalline silicon carbide in the form of a homogeneous microstructure having grain sizes of not more than 10 μm manufactured from mixtures of Si 3 N 4 powder and SiC powder in a weight ratio of from 5:95 to 95:5 without the concomitant use of sintering aids by isostatic hot pressing in a vacuum-sealed casing at temperatures of from 1800° to 2200° C. and a pressure of from 100 to 400 MPa.
Inventors
- 👤 Klaus Hunold
- 👤 Alfred Lipp
- 👤 Klaus Reinmuth
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 13:47
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/565; C04B35/575; C04B35/58; C04B35/584; C04B35/593
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
130 words
A substantially pore-free shaped article consisting essentially of polycrystalline silicon nitride and polycrystalline silicon carbide in the form of a homogenous microstructure having a total content of metallic impurities of not more than 0.2% by weight and having a grain size of not more than 10 μm which are manufactured without a sintering aid from mixtures of Si 3 N 4 powder and SiC powder in a weight ratio of from 5:95 to 95:5 having a total content of metallic impurities of not more than 0.2% by weight, based on the total weight of the pulverulent mixture, by isostatic hot pressing in a vacuum-sealed casing at a temperature of from 1800° to 2200° C. and a pressure of from 100 to 400 MPa in an inert gas as pressure-transfer medium.
Claim 2
Dependent Claim
130 words
A substantially pore-free shaped article consisting essentially of polycrystalline silicon nitride and polycrystalline silicon carbide in the form of a homogenous microstructure having a total content of metallic impurities of not more than 0.2% by weight and having a grain size of not more than 10 μm which are manufactured without a sintering aid from mixtures of Si 3 N 4 powder and SiC powder in a weight ratio of from 5:95 to 95:5 having a total content of metallic impurities of not more than 0.2% by weight, based on the total weight of the pulverulent mixture, by isostatic hot pressing in a vacuum-sealed casing at a temperature of from 1800° to 2200° C. and a pressure of from 100 to 400 MPa in an inert gas as pressure-transfer medium.
Claim 3
Dependent Claim
69 words
Shaped articles according to claim 1 which have been manufactured using a pulverulent mixture without a sintering aid consisting essentially of at least 97.0% by weight of Si 3 N 4 +SiC up to 1.8% by weight of SiO 2 up to 1.0% by weight of C+N up to 0.2% by weight, in total, of metallic impurities said pulverulent mixture having a particle size of 10 μm and finer.
Claim 4
Dependent Claim
132 words
A process for the manufacture of a shaped article of claim 1 or 2 by isostatic hot pressing in a high pressure autoclave using an inert gas as a pressure transfer medium which comprises: (a) introducing a pulverulent mixture without a sinter aid consisting essentially of silicon nitride and silicon carbide into prefabricated casings said casings being plastically deformable at a temperature of from 1800° to 2200° C.; (b) compacting the pulverulent mixture; (c) encasing the mixture by gas tightly sealing the containers under vacuum; (d) heating the encased mixture to a temperature in the range of 1800° to 2200° C. while slowly increasing the gas pressure to from 100 to 400 MPa for a time sufficient to form a pore-free shaped article; and (e) recovering the shaped article from the autoclave.
Claim 5
Dependent Claim
148 words
A process for the manufacture of a shaped article according to claim 1 or 2 by isostatic hot pressing in a high pressure autoclave using an inert gas as a pressure transfer medium comprising: (a) forming a preshaped article having pores open to the surface from a mixture without a sintering aid consisting essentially of silicon nitride and silicon carbide, wherein the preshaped article has a density at least 50% of the theoretical density of the mixture; (b) encasing the preshaped article in a gas tight casing under vacuum said casing being plastically deformable at a temperature of from 1800° to 2200° C.; (c) heating the encased article to a temperature in the range of 1800° to 2200° C. while slowly increasing the gas pressure to from 100 to 400 MPa until a substantially pore-free shaped article is formed; and (d) recovering the shaped article from the autoclave.
Claim 6
Dependent Claim
15 words
The process of claim 4 wherein the preshaped article is encased in a prefabricated casing.
Claim 7
Dependent Claim
29 words
The process of claim 4 wherein the preshaped article is coated with a material which forms a gas tight casing at a temperature below the hot isostatic pressing temperature.
Claim 8
Dependent Claim
84 words
The process of claim 6 wherein the preshaped article is coated with a material which forms a gas tight casing at a temperature below the isostatic hot pressing temperature and heating the coated preshaped article under vacuum to a temperature at which the gas tight casing forms, to gas tightly encase the preshaped article, and heating the gas tightly encased article to a temperature in the range of 1800° to 2200° C. while slowly increasing the gas pressure to from 100 to 400 MPa.
Claim 9
Dependent Claim
25 words
The process of claim 4 wherein a binder is used in forming the preshaped article and the binder is removed before encasing the preshaped article.
Claim 10
Dependent Claim
26 words
The process of claim 5 wherein a binder is used to form the preshaped article and the binder is removed before the preshaped article is encased.
Claim 11
Dependent Claim
26 words
The process of claim 6 wherein a binder is used to form the preshaped article and the binder is removed before the preshaped article is encased.
Claim 12
Dependent Claim
26 words
The process of claim 7 wherein a binder is used to form the preshaped article and the binder is removed before the preshaped article is encased.
Claim 13
Dependent Claim
14 words
The process of claim 3 wherein the pulverulent mixture is compacted by vibrating means.
Claim 14
Dependent Claim
48 words
A process accoridng to claim 3, 4, 5, 6, 7, 8, 9, 10, 11 or 12 wherein the shaped article is recovered by decreasing the temperature and gas pressure within the autoclave, removing the encased shaped article from the autoclave and freeing the shaped article from the casing.
References Cited (Backward Citations)
US3890250A
Cited
US3895219A
Cited
US3974106A
Cited
GB1522705A
Cited
FR2327836A1
Cited
US4184882A
Cited
US4187116A
Cited
FR2376089A1
Cited
GB2066800A
Cited
US4381931A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-12-23 | 1989-06-24 | 1989-12-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-12-23 | 1993-06-24 | 1993-12-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-12-23 | 1997-06-24 | 1997-12-24 | $7700.00 | Window Closed / Lapsed |