Reduced build-up pressure-sensitive adhesives
Assignee: Avery Dennison Corp
•
Filing: 1983-04-21
•
Granted: 1985-10-22
•
Expires: 2003-04-21
Abstract
Abstract A water-insoluble, normally tacky, pressure-sensitive adhesive is disclosed having reduced build up on a knife blade when that knife blade is utilized to shear a plurality of webs including a layer of the adhesive. The adhesive contains a mixture of non-volatile components including (a) a water-insoluble elastomeric polymer, (b) a tackifier and (c) a polyoxyalkylene polyol present in amount of about 3 to about 45 percent of the total non-volatile weights of components (a), (b) and (c). The adhesive components (a), (b) and (c) are dispersed substantially homogeneously when the adhesive is applied to a substrate.
Inventors
- 👤 Robert E. Parsons
- 👤 Martha L. Westcott
- 👤 Susan L. Johnson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:54
CPC Classifications
C; C09; C09J; C09J121/00; C09J7/00; C09J7/30; C09J7/38; C09J7/381; C09J7/383; C09J7/387; C08; C08L; C08L2666/00; C08L2666/02; Y; Y10; Y10S; Y10S428/00; Y10S428/914; Y10T; Y10T428/00; Y10T428/14; Y10T428/1452; Y10T428/28; Y10T428/2852; Y10T428/2857; Y10T428/2878; Y10T428/2883; Y10T428/2891
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
97 words
A normally tacky, pressure-sensitive adhesive comprising, when deposited on a substrate a mixture of non-volatile components including (a) a water-insoluble elastomeric polymer, (b) a tackifier and (c) a polyoxyalkylene polyol having a molecular weight of about 200 to about 20,000 present at about 3 to about 45 percent of the total non-volatile weight of components (a), (b) and (c), said adhesive components being substantially homogeneously dispersed when applied upon a substrate, said adhesive being water-insoluble and having improved resistance to build-up upon a knife blade when a plurality of adhesive-bearing substrates are sheared with said knife blade.
Claim 2
Dependent Claim
97 words
A normally tacky, pressure-sensitive adhesive comprising, when deposited on a substrate a mixture of non-volatile components including (a) a water-insoluble elastomeric polymer, (b) a tackifier and (c) a polyoxyalkylene polyol having a molecular weight of about 200 to about 20,000 present at about 3 to about 45 percent of the total non-volatile weight of components (a), (b) and (c), said adhesive components being substantially homogeneously dispersed when applied upon a substrate, said adhesive being water-insoluble and having improved resistance to build-up upon a knife blade when a plurality of adhesive-bearing substrates are sheared with said knife blade.
Claim 3
Dependent Claim
31 words
The pressure-sensitive adhesive according to claim 1 wherein said polyoxyalkylene polyol is present at about 5 to about 25 percent of the total non-volatile weight of components (a), (b) and (c).
Claim 4
Dependent Claim
29 words
The pressure-sensitive adhesive according to claim 1 wherein said polyoxyalkylene polyol has a molecular weight of about 200 to about 2000 and said elastomeric polymer is a synthetic rubber.
Claim 5
Dependent Claim
12 words
The pressure-sensitive adhesive according to claim 3 dispersed in an organic solvent.
Claim 6
Dependent Claim
12 words
The pressure-sensitive adhesive according to claim 1 dispersed in an aqueous medium.
Claim 7
Dependent Claim
31 words
The pressure-sensitive adhesive according to claim 5 wherein said polyoxyalkylene polyol has a molecular weight of about 600 to about 20,000 and said elastomeric polymer is an emulsified, carboxylated synthetic rubber.
Claim 8
Dependent Claim
14 words
The pressure-sensitive adhesive according to claim 1 wherein said polyoxyalkylene polyol is polyethylene glycol.
Claim 9
Dependent Claim
39 words
The pressure-sensitive adhesive according to claim 1 wherein said elastomeric polymer is a synthetic rubber selected from the group consisting of a block copolymer of styrene-butadiene, styrene-isoprene, styrene-butadiene-styrene, or styrene-isoprene-styrene, a styrene-butadiene random copolymer, homopolyisoprene, homopolybutadiene, and mixtures thereof.
Claim 10
Dependent Claim
52 words
The pressure-sensitive adhesive according to claim 1 wherein said polyoxyalkylene polyol is selected from the group consisting of polyethylene glycol, polypropylene glycol, a random polyoxyethyleneoxypropylene glycol, a polyoxyethylene adduct of glycerol or trimethylol propane or pentaerythritol or sorbitol, a polyoxypropylene adduct of glycerol or trimethylopropane or pentaerythritol or sorbitol, and mixtures thereof.
Claim 11
Dependent Claim
130 words
A normally tacky, pressure-sensitive adhesive composition comprising an organic solvent having a pressure-sensitive adhesive dispersed therein, said adhesive containing a mixture of non-volatile components including (a) a water-insoluble synthetic rubber elastomeric polymer present at about 20 to about 65 non-volatile weight percent, (b) a tackifier present at about 20 to about 70 non-volatile weight percent and (c) about 5 to about 25 non-volatile weight percent of a polyoxyalkylene polyol having a molecular weight of about 200 to about 2000, said adhesive composition being substantially homogenous at the time of application to a substrate, and after application to a substrate and removal of said solvent, said adhesive being water-insoluble and having improved resistance to build-up upon a knife blade when a plurality of adhesive-bearing substrates are sheared with said knife blade.
Claim 12
Dependent Claim
130 words
A normally tacky, pressure-sensitive adhesive composition comprising an organic solvent having a pressure-sensitive adhesive dispersed therein, said adhesive containing a mixture of non-volatile components including (a) a water-insoluble synthetic rubber elastomeric polymer present at about 20 to about 65 non-volatile weight percent, (b) a tackifier present at about 20 to about 70 non-volatile weight percent and (c) about 5 to about 25 non-volatile weight percent of a polyoxyalkylene polyol having a molecular weight of about 200 to about 2000, said adhesive composition being substantially homogenous at the time of application to a substrate, and after application to a substrate and removal of said solvent, said adhesive being water-insoluble and having improved resistance to build-up upon a knife blade when a plurality of adhesive-bearing substrates are sheared with said knife blade.
Claim 13
Dependent Claim
15 words
The pressure-sensitive adhesive composition according to claim 10 wherein said polyoxyalkylene is a polyethylene glycol.
Claim 14
Dependent Claim
23 words
The pressure-sensitive adhesive composition according to claim 11 wherein said polyethylene glycol is present at about 5 to about 15 non-volatile weight percent.
Claim 15
Dependent Claim
21 words
The pressure-sensitive adhesive composition according to claim 11 wherein said polyethylene glycol has a molecular weight of about 400 to 1000.
Claim 16
Dependent Claim
118 words
A normally tacky, pressure-sensitive adhesive composition comprising an aqueous dispersion of a pressure-sensitive adhesive, said pressure-sensitive adhesive containing a mixture of non-volatile components including (a) an internally tackified water-insoluble, acrylic emulsion elastomeric polymer present at about 55 to about 95 non-volatile weight percent, and (b) about 5 to about 45 non-volatile weight percent of a polyoxyalkylene polyol having a molecular weight of about 2000 to about 20,000, said adhesive composition being substantially homogenous at the time of application to a substrate, and after application to a substrate and removal of said solvent, said adhesive being water-insoluble and having improved resistance to build-up upon a knife blade when a plurality of adhesive-bearing substrates are sheared with said knife blade.
Claim 17
Dependent Claim
118 words
A normally tacky, pressure-sensitive adhesive composition comprising an aqueous dispersion of a pressure-sensitive adhesive, said pressure-sensitive adhesive containing a mixture of non-volatile components including (a) an internally tackified water-insoluble, acrylic emulsion elastomeric polymer present at about 55 to about 95 non-volatile weight percent, and (b) about 5 to about 45 non-volatile weight percent of a polyoxyalkylene polyol having a molecular weight of about 2000 to about 20,000, said adhesive composition being substantially homogenous at the time of application to a substrate, and after application to a substrate and removal of said solvent, said adhesive being water-insoluble and having improved resistance to build-up upon a knife blade when a plurality of adhesive-bearing substrates are sheared with said knife blade.
Claim 18
Dependent Claim
15 words
The pressure-sensitive adhesive compositon according to claim 14 wherein said polyoxyalkylene polyol is polyethylene glycol.
Claim 19
Dependent Claim
133 words
A normally tacky, pressure-sensitive hot melt adhesive composition comprising a mixture of non-volatile components including (a) a water-insoluble synthetic rubber elastomeric polymer present at about 20 to about 65 non-volatile weight percent, (b) a tackifier present at about 20 to about 70 non-volatile weight percent and (c) about 5 to about 25 non-volatile weight percent of a polyoxyalkylene polyol having a molecular weight of about 200 to about 2000, said adhesive composition being substantially homogeneous when in a molten state at a temperature above room temperature and at the time of application to a substrate, and after application to a substrate and cooling to about room temperature, said adhesive being water-insoluble and having improved resistance to build-up upon a knife blade when a plurality of adhesive-bearing substrates are sheared with said knife blade.
Claim 20
Dependent Claim
133 words
A normally tacky, pressure-sensitive hot melt adhesive composition comprising a mixture of non-volatile components including (a) a water-insoluble synthetic rubber elastomeric polymer present at about 20 to about 65 non-volatile weight percent, (b) a tackifier present at about 20 to about 70 non-volatile weight percent and (c) about 5 to about 25 non-volatile weight percent of a polyoxyalkylene polyol having a molecular weight of about 200 to about 2000, said adhesive composition being substantially homogeneous when in a molten state at a temperature above room temperature and at the time of application to a substrate, and after application to a substrate and cooling to about room temperature, said adhesive being water-insoluble and having improved resistance to build-up upon a knife blade when a plurality of adhesive-bearing substrates are sheared with said knife blade.
Claim 21
Dependent Claim
15 words
The pressure-sensitive adhesive composition according to claim 16 wherein said polyoxyalkylene polyol is polyethylene glycol.
Claim 22
Dependent Claim
129 words
An adhesive web including a backing member defining a top surface and a bottom surface, said backing member having a layer of water-insoluble, normally tacky, pressure-sensitive adhesive adhered to at least one of said surfaces, said adhesive comprising as non-volatile components (a) a water-insoluble elastomeric polymer, (b) a tackifier, and (c) a polyoxyalkylene polyol having a molecular weight of about 200 to about 20,000 present at about 3 to about 45 percent of the total, non-volatile weight of components (a), (b) and (c) of said adhesive, said adhesive components being substantially homogeneously dispersed at the time of application of said adhesive to said backing member, and said adhesive having improved resistance to build-up upon a knife blade when a plurality of said webs are sheared with said knife blade.
Claim 23
Dependent Claim
129 words
An adhesive web including a backing member defining a top surface and a bottom surface, said backing member having a layer of water-insoluble, normally tacky, pressure-sensitive adhesive adhered to at least one of said surfaces, said adhesive comprising as non-volatile components (a) a water-insoluble elastomeric polymer, (b) a tackifier, and (c) a polyoxyalkylene polyol having a molecular weight of about 200 to about 20,000 present at about 3 to about 45 percent of the total, non-volatile weight of components (a), (b) and (c) of said adhesive, said adhesive components being substantially homogeneously dispersed at the time of application of said adhesive to said backing member, and said adhesive having improved resistance to build-up upon a knife blade when a plurality of said webs are sheared with said knife blade.
Claim 24
Dependent Claim
18 words
The adhesive web according to claim 18 further including a release sheet removably adhered to said adhesive layer.
Claim 25
Dependent Claim
162 words
A label including (1) a release sheet defining a top surface and a bottom surface, one of said surfaces being removably adhered to (2) a layer of a water-insoluble, normally tacky, pressure-sensitive adhesive, said adhesive comprising as non-volatile components (a) a water-insoluble elastomeric polymer, (b) a tackifier and (c) a polyoxyalkylene polyol having a molecular weight of about 200 to about 20,000 present at about 3 to about 45 percent of the total non-volatile weight of components (a), (b) and (c), said adhesive components being substantially homogeneously dispersed at the time of application of said adhesive to said backing member, and said adhesive having improved resistance to build-up upon a knife blade when a plurality of said labels are sheared with said knife blade, and (3) a backing member defining a top surface and a bottom surface, the bottom surface of said backing member being adapted for receiving indicia and the top surface of said backing member being adhered to said adhesive.
Claim 26
Dependent Claim
162 words
A label including (1) a release sheet defining a top surface and a bottom surface, one of said surfaces being removably adhered to (2) a layer of a water-insoluble, normally tacky, pressure-sensitive adhesive, said adhesive comprising as non-volatile components (a) a water-insoluble elastomeric polymer, (b) a tackifier and (c) a polyoxyalkylene polyol having a molecular weight of about 200 to about 20,000 present at about 3 to about 45 percent of the total non-volatile weight of components (a), (b) and (c), said adhesive components being substantially homogeneously dispersed at the time of application of said adhesive to said backing member, and said adhesive having improved resistance to build-up upon a knife blade when a plurality of said labels are sheared with said knife blade, and (3) a backing member defining a top surface and a bottom surface, the bottom surface of said backing member being adapted for receiving indicia and the top surface of said backing member being adhered to said adhesive.
Claim 27
Independent Claim
130 words
A method of forming a shearable adhesive web having a reduced amount of build-up of a water-insoluble, normally tacky, pressure-sensitive adhesive upon a knife blade when a plurality of said webs bearing said adhesive are sheared with said knife blade comprising the steps of: providing a water-insoluble elastomeric, polymer and a tackifier; admixing a polyoxyalkylene polyol having a molecular weight of about 200 to about 20,000 with polymer and said tackifier to form a substantially homogenous, water-insoluble normally tacky, pressure-sensitive adhesive, said polyol being admixed in an amount of about 3 to about 45 percent of the total non-volatile weights of said polymer, said tackifier and said polyol; coating said substantially homogenous adhesive upon at least one surface of a shearable web to form a layer of said adhesive thereon.
Claim 28
Independent Claim
130 words
A method of forming a shearable adhesive web having a reduced amount of build-up of a water-insoluble, normally tacky, pressure-sensitive adhesive upon a knife blade when a plurality of said webs bearing said adhesive are sheared with said knife blade comprising the steps of: providing a water-insoluble elastomeric, polymer and a tackifier; admixing a polyoxyalkylene polyol having a molecular weight of about 200 to about 20,000 with polymer and said tackifier to form a substantially homogenous, water-insoluble normally tacky, pressure-sensitive adhesive, said polyol being admixed in an amount of about 3 to about 45 percent of the total non-volatile weights of said polymer, said tackifier and said polyol; coating said substantially homogenous adhesive upon at least one surface of a shearable web to form a layer of said adhesive thereon.
Claim 29
Dependent Claim
13 words
The method according to claim 21 wherein said polyoxyalkylene polyol is polyethylene glycol.
Claim 30
Dependent Claim
19 words
The method according to claim 22 wherein said water-insoluble, normally tacky, pressure-sensitive adhesive is coated from an organic solvent.
Claim 31
Dependent Claim
19 words
The method according to claim 21 wherein said water-insoluble, normally tacky, pressure-sensitive adhesive is coated from an aqueous medium.
Claim 32
Dependent Claim
20 words
The method according to claim 21 wherein said water-insoluble, normally tacky, pressure-sensitive adhesive is coated while in a molten state.
References Cited (Backward Citations)
US3162611A
Cited
US3413250A
Cited
US3492258A
Cited
DE1809124A1
Cited
US3775146A
Cited
US4104218A
Cited
US4129539A
Cited
US4442258A
Cited
US4379095A
Cited
US4346189A
Cited
US4413082A
Cited
US4427737A
Cited
GB2115431A
Cited
US4413080A
Cited
US4492724A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-21 | 1989-04-22 | 1989-10-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-21 | 1993-04-22 | 1993-10-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-21 | 1997-04-22 | 1997-10-22 | $7700.00 | Window Closed / Lapsed |