Method for making poly(ethylene terephthalate) article

Claim 1

A method for making a high density, partially crystalline, biaxially oriented, heat set, polyethylene terephthalate hollow container, the container having a body with oriented sidewalls, the method comprising the steps of: A. providing by blow molding a hollow article with oriented sidewalls, B. while the article is still under a shrinkage reducing pressure, increasing the density of the oriented sidewalls to at least about 1.391 g/cc by heating the sidewalls to a heat setting temperature equivalent to a temperature of about 220° C. to 250° C. to provide the density of at least about 1.391 g/cc, C. quenching the sidewalls while still under a shrinkage reducing pressure to provide the article with a shrinkage of less than about 5% of the volume and an onset of shrinkage temperature of at least about 105° C., the quenching being done at a temperature equivalent to that of about room temperature to 180° C. at a high heat setting temperature of 240° C., about 85° to 160° C. for a heat setting temperature of about 230° C., and about 120° C. to 150° C. for a lower heat setting temperature of about 220° C.

Claim 2

A method for making a high density, partially crystalline, biaxially oriented, heat set, polyethylene terephthalate hollow container, the container having a body with oriented sidewalls, the method comprising the steps of: A. providing by blow molding a hollow article with oriented sidewalls, B. while the article is still under a shrinkage reducing pressure, increasing the density of the oriented sidewalls to at least about 1.391 g/cc by heating the sidewalls to a heat setting temperature equivalent to a temperature of about 220° C. to 250° C. to provide the density of at least about 1.391 g/cc, C. quenching the sidewalls while still under a shrinkage reducing pressure to provide the article with a shrinkage of less than about 5% of the volume and an onset of shrinkage temperature of at least about 105° C., the quenching being done at a temperature equivalent to that of about room temperature to 180° C. at a high heat setting temperature of 240° C., about 85° to 160° C. for a heat setting temperature of about 230° C., and about 120° C. to 150° C. for a lower heat setting temperature of about 220° C.

Claim 8

A method of making a high density, partially crystalline, biaxially oriented, heat set, hollow poly(ethylene terephthalate) plastic article comprising (1) enclosing a tubular parison of said poly(ethylene terephthalate), having a closed end and an open end destined to form the neck or finish of the hollow article, within a blow mold which parison is at a first temperature range, which first temperature range is conducive to orientation during stretching; (2) while said parison is still at said first temperature range expanding said parison into contact and conformance with the blow mold walls by inflation with a gas under pressure to make a hollow blown article with oriented sidewalls, said stretching and expanding under the resulting strain conditions resulting in biaxial orientation and concomitant partial crystallization, and then while the article walls are still inflated in contact with said mold walls; (3) increasing the density of the oriented sidewalls to at least about 1.391 g/cc by raising the temperature of the article to a heat setting temperature in the range of about 220° to 250° C. to provide the density of at least about 1.391 g/cc, except for the neck or finish portion of said article which is kept at a low temperature such that crystallization is minimized or eliminated so that the neck or finish portion remains transparent, wherein the heating in said heat setting temperature range heat sets the body of said article by causing further crystallization thereof as indicated by density increase; (4) reducing the pressure to a pressure above atmospheric that will maintain said hollow article at essentially the same volume and resist shrinkage and then opening the mold; (5) and while said hollow article is still at a shrinkage-resisting pressure exceeding atmospheric, cooling said article to a quenching temperature sufficient to provide an onset of shrinkage temperature of at least about 105° C. and a volume shrinkage of less than about 5%, the quenching temperature being equivalent to about room temperature to 180° C. for a 240° C. heat setting temperature and about 85° C. to 160° C. for a heat setting temperature of about 230° C., and about 120° C. to 150° C. for a heat setting temperature of about 220° C., and (6) thereafter reducing the gas pressure within said article to essentially ambient pressure.

Claim 9

A method of making a high density, partially crystalline, biaxially oriented, heat set, hollow poly(ethylene terephthalate) plastic article comprising (1) enclosing a tubular parison of said poly(ethylene terephthalate), having a closed end and an open end destined to form the neck or finish of the hollow article, within a blow mold which parison is at a first temperature range, which first temperature range is conducive to orientation during stretching; (2) while said parison is still at said first temperature range expanding said parison into contact and conformance with the blow mold walls by inflation with a gas under pressure to make a hollow blown article with oriented sidewalls, said stretching and expanding under the resulting strain conditions resulting in biaxial orientation and concomitant partial crystallization, and then while the article walls are still inflated in contact with said mold walls; (3) increasing the density of the oriented sidewalls to at least about 1.391 g/cc by raising the temperature of the article to a heat setting temperature in the range of about 220° to 250° C. to provide the density of at least about 1.391 g/cc, except for the neck or finish portion of said article which is kept at a low temperature such that crystallization is minimized or eliminated so that the neck or finish portion remains transparent, wherein the heating in said heat setting temperature range heat sets the body of said article by causing further crystallization thereof as indicated by density increase; (4) reducing the pressure to a pressure above atmospheric that will maintain said hollow article at essentially the same volume and resist shrinkage and then opening the mold; (5) and while said hollow article is still at a shrinkage-resisting pressure exceeding atmospheric, cooling said article to a quenching temperature sufficient to provide an onset of shrinkage temperature of at least about 105° C. and a volume shrinkage of less than about 5%, the quenching temperature being equivalent to about room temperature to 180° C. for a 240° C. heat setting temperature and about 85° C. to 160° C. for a heat setting temperature of about 230° C., and about 120° C. to 150° C. for a heat setting temperature of about 220° C., and (6) thereafter reducing the gas pressure within said article to essentially ambient pressure.