US4475972A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Implantable material
Assignee: ONTARIO RESEARCH FOUNDATION SHERIDAN PARK RESEARCH COMMUNITY A CORP OF PROVINCE OF ONTARIO
•
Filing: 1982-04-22
•
Granted: 1984-10-09
•
Expires: 2002-04-22
Abstract
Abstract Porous polymeric material, which, in tubular form, is suitable for use as a vascular graft, is made by a procedure wherein polymeric fibres are wound on a mandrel while overlying fibres are simultaneously bonded together. In one preferred embodiment, a viscous solution of a biocompatible polymer is extruded from a spinnaret to form a plurality of filaments which are wound on a rotating mandrel as the spinnaret reciprocates relative to the mandrel. The filaments are wet as they contact each other, so that on evaporation of the solvent the fibres become bonded to each other.
Inventors
- 👤 Edward W. C. Wong
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 12:25
CPC Classifications
B; B29; B29C; B29C53/00; B29C53/56; B29C53/58; B29C53/583; B29C53/587; A; A61; A61F; A61F2/00; A61F2/02; A61F2/04; A61F2/06; A61L; A61L27/00; A61L27/14; A61L27/18; B29C37/00; B29C37/0003; B29C37/0017; B29K; B29K2105/00; B29K2105/04; B29L; B29L2031/00; B29L2031/753; B29L2031/7532; B29L2031/7534
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
217 words
A method of forming a porous flexible biocompatible and biocompliable tubular vascular graft, which comprises: extruding an extrudable biocompatible and biocompliable thermoplastic polymeric material through an opening having a diameter larger than the intended diameter of fibers to be drawn therefrom, said polymeric material being capable of forming flexible fibres therefrom, drawing a continuous fibre of diameter of less than about 100 microns from said extruded material by attenuating the extruded material using a drawing force applied longitudinally of the fibre, winding said continuous fibre on a mandrel having a diameter of about 1 to about 50 mm while simultaneously providing fibre-to-fibre bonding between overlying fibres as the continuous fibre subtends an angle of about 10° to about 80° to the axis of the mandrel until a thickness of about 0.1 to about 2 mm has been formed on said mandrel to form a porous tubular product having a porosity of about 50 to about 80 volume percent on said mandrel, rotating said mandrel on its axis at sufficient speed during said winding to apply said longitudinal drawing force to said fibre to effect the drawing and attenuation of said continuous fibre from said extruded polymeric material, and removing said porous tubular product from said mandrel to provide said porous flexible biocompatible and biocompliable tubular vascular graft.
Claim 2
Independent Claim
217 words
A method of forming a porous flexible biocompatible and biocompliable tubular vascular graft, which comprises: extruding an extrudable biocompatible and biocompliable thermoplastic polymeric material through an opening having a diameter larger than the intended diameter of fibers to be drawn therefrom, said polymeric material being capable of forming flexible fibres therefrom, drawing a continuous fibre of diameter of less than about 100 microns from said extruded material by attenuating the extruded material using a drawing force applied longitudinally of the fibre, winding said continuous fibre on a mandrel having a diameter of about 1 to about 50 mm while simultaneously providing fibre-to-fibre bonding between overlying fibres as the continuous fibre subtends an angle of about 10° to about 80° to the axis of the mandrel until a thickness of about 0.1 to about 2 mm has been formed on said mandrel to form a porous tubular product having a porosity of about 50 to about 80 volume percent on said mandrel, rotating said mandrel on its axis at sufficient speed during said winding to apply said longitudinal drawing force to said fibre to effect the drawing and attenuation of said continuous fibre from said extruded polymeric material, and removing said porous tubular product from said mandrel to provide said porous flexible biocompatible and biocompliable tubular vascular graft.
Claim 3
Dependent Claim
44 words
The method of claim 1 wherein said extrudable polymeric material takes the form of a viscous solution of a polymeric material from which a fibre may be drawn, and wherein said fibre-to-fibre bonding is achieved by removal of said solvent from said overlying fibres.
Claim 4
Dependent Claim
25 words
The method of claim 2 wherein said mandrel is heated to assist in evaporation of solvent from said overlying fibres to achieve said fibre-to-fibre bonding.
Claim 5
Dependent Claim
37 words
The method of claim 1 wherein said extrudable polymeric material takes the form of a molten polymeric thermoplastic material and wherein said fibre-to-fibre bonding is achieved by fusion of overlying fibres and solidification of the fused fibres.
Claim 6
Dependent Claim
29 words
The method of claim 1 including the further step of cutting said porous tubular product after said removal from said mandrel to form a planar sheet of porous material.
Claim 7
Independent Claim
275 words
A method of forming a porous flexible biocompatible and biocompliable tubular vascular graft, which comprises: extruding an extrudable biocompatible and biocompliable thermoplastic polymeric material through a plurality of openings in a spinnaret containing said polymeric material, each of said openings having substantially the same diameter and larger than the intended diameter of fibres to be drawn therefrom, said polymeric material being capable of forming flexible fibres therefrom, drawing a plurality of individual continuous fibres of diameter of about 10 to about 30 microns from the extruded polymeric material by attenuating the extruded material using a drawing force applied longitudinally of the fibre, winding said plurality of fibres onto a mandrel having a diameter of about 1 to about 50 mm by rotating said mandrel on its axis while simultaneously providing fibre-to-fibre bonding between overlying fibres, reciprocating said spinnaret relative to said mandrel as said mandrel rotates on its axis and the continuous fibres subtend an angle of about 10° to about 80° to the axis of the mandrel until a thickness of about 0.1 to about 2 mm has been formed on said mandrel to form a porous tubular product having a porosity of about 50 to about 80 volume percent and pore openings of about 10 to about 100 microns on said mandrel, rotating said mandrel on its axis at sufficient speed during said winding to apply said longitudinal drawing force to each of said continuous fibres to effect said drawing of said fibres from said extruded polymeric material and attenuation of said fibres, and removing said porous tubular product from said mandrel to provide said porous flexible biocompatible and biocompliable tubular vascular graft.
Claim 8
Independent Claim
275 words
A method of forming a porous flexible biocompatible and biocompliable tubular vascular graft, which comprises: extruding an extrudable biocompatible and biocompliable thermoplastic polymeric material through a plurality of openings in a spinnaret containing said polymeric material, each of said openings having substantially the same diameter and larger than the intended diameter of fibres to be drawn therefrom, said polymeric material being capable of forming flexible fibres therefrom, drawing a plurality of individual continuous fibres of diameter of about 10 to about 30 microns from the extruded polymeric material by attenuating the extruded material using a drawing force applied longitudinally of the fibre, winding said plurality of fibres onto a mandrel having a diameter of about 1 to about 50 mm by rotating said mandrel on its axis while simultaneously providing fibre-to-fibre bonding between overlying fibres, reciprocating said spinnaret relative to said mandrel as said mandrel rotates on its axis and the continuous fibres subtend an angle of about 10° to about 80° to the axis of the mandrel until a thickness of about 0.1 to about 2 mm has been formed on said mandrel to form a porous tubular product having a porosity of about 50 to about 80 volume percent and pore openings of about 10 to about 100 microns on said mandrel, rotating said mandrel on its axis at sufficient speed during said winding to apply said longitudinal drawing force to each of said continuous fibres to effect said drawing of said fibres from said extruded polymeric material and attenuation of said fibres, and removing said porous tubular product from said mandrel to provide said porous flexible biocompatible and biocompliable tubular vascular graft.
Claim 9
Dependent Claim
25 words
The method of claim 6 wherein said rotating mandrel is located with its axis substantially horizontal and said spinnaret reciprocates parallel to said mandrel axis.
Claim 10
Dependent Claim
30 words
The method of claim 6 wherein said fibres are extruded through openings in said spinnaret which are about 4 to 5 times larger than the diameter of the drawn fibres.
Claim 11
Dependent Claim
13 words
The method of claim 6 wherein said angle is about 60° to 70°.
Claim 12
Dependent Claim
26 words
The method of claim 6 wherein said mandrel diameter is about 3 to about 25 mm and said thickness is about 0.5 to about 1 mm.
References Cited (Backward Citations)
US2988469A
Cited
US3554851A
Cited
US3490975A
Cited
US3787265A
Cited
US3801400A
Cited
US4021281A
Cited
US4044404A
Cited
US4116738A
Cited
US4323525A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-09 | 1988-04-09 | 1988-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-09 | 1992-04-09 | 1992-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-09 | 1996-04-09 | 1996-10-09 | $7700.00 | Window Closed / Lapsed |