Method of forming a small bore flexible vascular graft involving eluting solvent-elutable particles from a polymeric tubular article
Assignee: Ortech Corp
•
Filing: 1982-02-23
•
Granted: 1984-07-10
•
Expires: 2002-02-23
Abstract
Abstract Novel cardiovascular prosthetic devices or implants having many useful cardiovascular applications comprise a porous surface and a network of interconnected interstitial pores below the surface in fluid flow communication with the surface pores. Tissue forms a smooth thin adherent coating of self-determining thickness on the porous surface making it resistant to the formation of the blood clots normally associated with the presence of foreign bodies in the blood stream. The device has particular utility in heart valves, pacemaker electrodes, blood pumps, blood stream filters, an artificial pancreas, vascular access tubes, small and large bore vascular grafts, blood pump diaphragms and vascular and intracardiac patches.
Inventors
- 👤 David C. MacGregor
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-22 23:43
CPC Classifications
A; A61; A61N; A61N1/00; A61N1/02; A61N1/04; A61N1/05; A61N1/056; A61N1/0565; A61F; A61F2/00; A61F2/0077; A61F2/02; A61F2/04; A61F2/06; A61L; A61L27/00; A61L27/14; A61L27/18; A61L27/28; A61L27/34; A61L27/50; A61L27/56; A61L33/00; A61L33/02; A61L33/022; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12042
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
178 words
A method of forming a small bore flexible vascular graft constructed of flexible biocompatible polymeric material, which comprises: (a) uniformly dispersing solvent-elutable particles dimensioned to provide a pore size of less than about 50 microns in the graft in a continuous or discontinuous polymer phase in a quantity sufficient to establish a porosity of about 10 to about 70% by volume in the graft, (b) forming a coherent shaped tubular article having an inside diameter of from about 2 to about 6 mm from the dispersion wherein the solvent-elutable particles are substantially uniformly dispersed throughout a continuous solid phase tubular article in intraparticulate contacting relationship, and (c) eluting the solvent-elutable particles from the tubular article using a solvent for said particles to provide a porous tubular product suitable for use as a vascular graft and having a subsurface regions comprising a network of interconnected pores substantially uniformly distributed therein, porous inner and outer surfaces communicating with said subsurface, a pore size of less than about 50 microns and a porosity of about 10 to about 70% by volume.
Claim 2
Independent Claim
178 words
A method of forming a small bore flexible vascular graft constructed of flexible biocompatible polymeric material, which comprises: (a) uniformly dispersing solvent-elutable particles dimensioned to provide a pore size of less than about 50 microns in the graft in a continuous or discontinuous polymer phase in a quantity sufficient to establish a porosity of about 10 to about 70% by volume in the graft, (b) forming a coherent shaped tubular article having an inside diameter of from about 2 to about 6 mm from the dispersion wherein the solvent-elutable particles are substantially uniformly dispersed throughout a continuous solid phase tubular article in intraparticulate contacting relationship, and (c) eluting the solvent-elutable particles from the tubular article using a solvent for said particles to provide a porous tubular product suitable for use as a vascular graft and having a subsurface regions comprising a network of interconnected pores substantially uniformly distributed therein, porous inner and outer surfaces communicating with said subsurface, a pore size of less than about 50 microns and a porosity of about 10 to about 70% by volume.
Claim 3
Dependent Claim
57 words
The method of claim 1, wherein steps (a) and (b) are effected by forming a viscous casting solution of the polymer, uniformly dispersing the solvent-elutable particles in the polymer solution, casting the resulting dispersion onto a casting surface in tubular form, and removing the solvent phase from the casting solution to provide said coherent shaped tubular article.
Claim 4
Dependent Claim
37 words
The method of claim 2, wherein said procedure further includes positioning a fabric tube within said casting prior to removal of said solvent phase to provide a reinforcing fabric layer within the wall of the tubular graft.
Claim 5
Dependent Claim
19 words
The method of claim 2 including heat treating the cast tube during or following removal of said solvent-elutable particles.
Claim 6
Dependent Claim
12 words
The method of claim 1 wherein said solvent-elutable particles are sodium chloride.
Claim 7
Independent Claim
180 words
A method of forming a large bore flexible vascular graft constructed of flexible biocompatible polymeric material, which comprises: (a) uniformly dispersing solvent-elutable particles dimensioned to provide a pore size of less than about 200 microns in the graft in a continuous or discontinuous polymer phase in a quantity sufficient to establish a porosity of about 10 to about 70% by volume in the graft, (b) forming a coherent shaped tubular article having an inside diameter of from about 6 mm to about 10 cm from the dispersion wherein the solvent-elutable particles are substantially uniformly dispersed throughout a continuous solid phase tubular article in intraparticulate contacting relationship, and (c) eluting the solvent-elutable particles from the tubular article using a solvent for said particles to provide a porous tubular polymer product suitable for use as a vascular graft and having a subsurface region comprising a network of interconnected pores substantially uniformly distributed therein, porous inner and outer surfaces communicating with said subsurface, a pore size of less than about 200 microns and a porosity of about 10 to about 70% by volume.
Claim 8
Independent Claim
180 words
A method of forming a large bore flexible vascular graft constructed of flexible biocompatible polymeric material, which comprises: (a) uniformly dispersing solvent-elutable particles dimensioned to provide a pore size of less than about 200 microns in the graft in a continuous or discontinuous polymer phase in a quantity sufficient to establish a porosity of about 10 to about 70% by volume in the graft, (b) forming a coherent shaped tubular article having an inside diameter of from about 6 mm to about 10 cm from the dispersion wherein the solvent-elutable particles are substantially uniformly dispersed throughout a continuous solid phase tubular article in intraparticulate contacting relationship, and (c) eluting the solvent-elutable particles from the tubular article using a solvent for said particles to provide a porous tubular polymer product suitable for use as a vascular graft and having a subsurface region comprising a network of interconnected pores substantially uniformly distributed therein, porous inner and outer surfaces communicating with said subsurface, a pore size of less than about 200 microns and a porosity of about 10 to about 70% by volume.
Claim 9
Dependent Claim
57 words
The method of claim 6, wherein steps (a) and (b) are effected by forming a viscous casting solution of the polymer, uniformly dispersing the solvent-elutable particles in the polymer solution, casting the resulting dispersion onto a casting surface in tubular form, and removing the solvent phase from the casting solution to provide said coherent shaped tubular article.
Claim 10
Dependent Claim
37 words
The method of claim 7 wherein said procedure further includes positioning a fabric tube within said casting prior to removal of said solvent phase to provide a reinforcing fabric layer within the wall of the tubular graft.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-07-10 | 1988-01-09 | 1988-07-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-07-10 | 1992-01-09 | 1992-07-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-07-10 | 1996-01-09 | 1996-07-10 | $7700.00 | Window Closed / Lapsed |