Novel system for the production of polyurethanes

Claim 2

A polyurethane product formed by reacting (a) an isocyanate selected from the group consisting of 4,4'-diisocyanatodiphenylmethane, isocyanates based on 4,4'-diisocyanatodiphenylmethane, and mixtures thereof, (b) at least one polyether polyol having at least two and no more than three hydroxyl groups, (c) at least one polymer polyol prepared by polymerizing an ethylenically unsaturated monomer or monomers in a relatively high molecular weight organic compound containing at least two hydroxyl groups, the amount of polymer polyol being such that the combination of component (b) and component (c) has an average hydroxyl functionality of from about 2.10 to about 2.30, and a solids content of from about 2 to about 15 percent by weight, (d) from about 5 to about 15 percent by weight based on the total weight of components (b), (c) and (d) of a compound selected from the group consisting of ethylene glycol, 1,4-butanediol and mixtures thereof, in the presence of (e) a blowing agent and, optionally, catalyst and surfactant, wherein the amount of component (a) is such that the isocyanate index is from about 94 to about 105.

Claim 3

The product of claim 1 wherein the combination of component (b) and component (c) has a solids content of from about 4 to about 10 percent by weight.

Claim 4

The product of claim 1 wherein component (d) comprises from about 5 to about 10 percent by weight based on the total weight of components (b), (c), and (d).

Claim 5

A process for the production of a polyurethane product comprising reacting (a) an isocyanate selected from the group consisting of 4,4'-diisocyanatodiphenylmethane, isocyanates based on 4,4'-diisocyanatodiphenylmethane, and mixtures thereof, (b) at least one polyether polyol having at least two and no more than three hydroxyl groups, (c) at least one polymer polyol prepared by polymerizing an ethylenically unsaturated monomer or monomers in a relatively high molecular weight organic compound containing at least two hydroxyl groups, the amount of polymer polyol being such that the combination of component (b) and component (c) has an average hydroxyl functionality of from about 2.10 to about 2.30, and a solids content of from about 2 to about 15 percent by weight, (d) from about 5 to about 15 percent by weight based on the total weight of components (b), (c) and (d) of a compound selected from the group consisting of ethylene glycol, 1,4-butanediol and mixtures thereof, in the presence of (e) a blowing agent and, optionally, catalyst and surfactant, wherein the amount of component (a) is such that the isocyanate index is from about 94 to about 105.

Claim 6

A process for the production of a polyurethane product comprising reacting (a) an isocyanate selected from the group consisting of 4,4'-diisocyanatodiphenylmethane, isocyanates based on 4,4'-diisocyanatodiphenylmethane, and mixtures thereof, (b) at least one polyether polyol having at least two and no more than three hydroxyl groups, (c) at least one polymer polyol prepared by polymerizing an ethylenically unsaturated monomer or monomers in a relatively high molecular weight organic compound containing at least two hydroxyl groups, the amount of polymer polyol being such that the combination of component (b) and component (c) has an average hydroxyl functionality of from about 2.10 to about 2.30, and a solids content of from about 2 to about 15 percent by weight, (d) from about 5 to about 15 percent by weight based on the total weight of components (b), (c) and (d) of a compound selected from the group consisting of ethylene glycol, 1,4-butanediol and mixtures thereof, in the presence of (e) a blowing agent and, optionally, catalyst and surfactant, wherein the amount of component (a) is such that the isocyanate index is from about 94 to about 105.

Claim 7

The process of claim 4 wherein the combination of component (b) and component (c) has a solids content of from about 4 to about 10 percent by weight.

Claim 8

The process of claim 4 wherein component (d) comprises from about 5 to about 10 percent by weight based on the total weight of components (b), (c), and (d).

Claim 9

A polyol blend comprising (b) at least one polyether polyol having at least two and no more than three hydroxyl groups, (c) at least one polymer polyol prepared by polymerizing an ethylenically unsaturated monomer or monomers in a relatively high molecular weight organic compound containing at least two hydroxyl groups, the amount of polymer polyol being such that the combination of component (b) and component (c) has an average hydroxyl functionality of from about 2.10 to about 2.30, and a solids content of from about 2 to about 15 percent by weight.

Claim 10

A polyol blend comprising (b) at least one polyether polyol having at least two and no more than three hydroxyl groups, (c) at least one polymer polyol prepared by polymerizing an ethylenically unsaturated monomer or monomers in a relatively high molecular weight organic compound containing at least two hydroxyl groups, the amount of polymer polyol being such that the combination of component (b) and component (c) has an average hydroxyl functionality of from about 2.10 to about 2.30, and a solids content of from about 2 to about 15 percent by weight.

Claim 11

The blend of claim 7 wherein the combination of component (b) and component (c) has a solids content of from about 4 to about 10 percent by weight.

Claim 12

The blend of claim 7 wherein an additional component (d) selected from the group consisting of ethylene glycol, 1,4-butanediol and mixtures thereof comprises from about 5 to about 10 percent by weight based on the total weight of components (b), (c), and (d).

Claim 13

A blend comprising (b) at least one polyether polyol having at least two and no more than three hydroxyl groups, (c) at least one polymer polyol prepared by polymerizing an ethylenically unsaturated monomer or monomers in a relatively high molecular weight organic compound containing at least two hydroxyl groups, the amount of polymer polyol being such that the combination of component (b) and component (c) has an average hydroxyl functionality of from about 2.10 to about 2.30, and a solids content of from about 2 to about 15 percent by weight, (d) from about 5 to about 15 percent by weight based on the total weight of components (b), (c) and (d) of a compound selected from the group consisting of ethylene glycol, 1,4-butanediol and mixtures thereof, (e) a blowing agent, and optionally, catalyst and surfactant.

Claim 14

A blend comprising (b) at least one polyether polyol having at least two and no more than three hydroxyl groups, (c) at least one polymer polyol prepared by polymerizing an ethylenically unsaturated monomer or monomers in a relatively high molecular weight organic compound containing at least two hydroxyl groups, the amount of polymer polyol being such that the combination of component (b) and component (c) has an average hydroxyl functionality of from about 2.10 to about 2.30, and a solids content of from about 2 to about 15 percent by weight, (d) from about 5 to about 15 percent by weight based on the total weight of components (b), (c) and (d) of a compound selected from the group consisting of ethylene glycol, 1,4-butanediol and mixtures thereof, (e) a blowing agent, and optionally, catalyst and surfactant.

Claim 15

The blend of claim 10 wherein the combination of component (b) and component (c) has a solids content of from about 4 to about 10 percent by weight.

Claim 16

The blend of claim 10 wherein component (d) comprises from about 5 to about 10 percent by weight based on the total weight of components (b), (c), and (d).