Low-solvent, thermosetting reactive polyurethane coating composition, a process for its production and its use in direct and reverse coating processes

Claim 2

A low-solvent thermosetting reactive polyurethane coating composition which hardens to form light-fast polyurethane ureas with improved resistance to light, oxidation, heat and hydrolysis, characterized in that the coating composition comprises the following components in the following molar ratios: (A) a ketoxime-blocked NCO-prepolymer of (1) 1 mole of 2- to 4-functional relatively high molecular weight polyhydroxyl compounds having a molecular weight in the range from about 1000 to 4000, wherein said 1 mole comprises (a) from about 0.5 to 1.0 mole of a polyester carbonate having a molecular weight of from about 1000 to 4000 produced from diphenyl carbonate and ester glycols of ε-caprolactone and 1,6-hexane diol and (b) up to about 0.5 mole of 2-functional to 4-functional relatively high molecular weight polyester polyols having a molecular weight of from about 1000 to 4000; (2) from about 0.1 to 1.2 moles of low molecular weight polyols having molecular weights in the range from about 62 to 300, wherein said low molecular weight polyols comprise (c) from about 0.1 to 0.8 mole of bis-carbazinic ester polyols corresponding to the following general formula ##STR9## in which R is a straight-chain and/or branched-chain C 1 -C 5 -alkylene or hydroxyl-substituted alkylene radical and (d) up to about 1.1 mole of low molecular weight polyols; (3) aliphatic and/or cycloaliphatic diisocyanates in an NCO:OH ratio between the components ##EQU2## of from about 1.5:1 to 6:1, and (4) quantities of ketoximes substantially equivalent to the NCO-content; (B) a crosslinking agent which comprises aliphatic and/or cycloaliphatic polyamines containing at least two primary amino groups at an NCO/NH 2 ratio of (A) to (B) between about 1.2:1 and 0.8:1; and (C) up to about 40% by weight based on the total weight of the coating composition, of at least one organic solvent said organic solvent being sufficient to obtain a viscosity for the mixture of (A), (B) and (C) of from about 20,000 to 50,000 mPa.s at 20° C.

Claim 3

The coating composition as claimed in claim 1, characterized in that component (A) is a ketoxime-blocked NCO-prepolymer of 1 mole of 2- to 3-functional polyhydroxyl compounds having an average molecular weight of from about 1500 to 2500, wherein said 1 mole comprises (a) from about 0.5 to 1.0 mole of a linear polyester polycarbonate having a molecular weight of from about 1500 to 2500 produced from diphenol carbonate and ester glycols of ε-caprolactone and 1,6-hexane diol and (b) up to about 0.5 mole of 2- to 3-functional polyester polyols having a molecular weight of from 1500 to 2500 synthesized from components comprising diols containing 4 or more carbon atoms.

Claim 4

The coating composition as claimed in claim 1 or 2, characterized in that from about 0.1 to 0.8 mole of bis-carbazinic ester diols corresponding to the following formula ##STR10## in which R is a straight-chain and/or branched C 1 -C 5 -alkylene radical, are used as component (A)(2)(c).

Claim 5

The coating composition as claimed in claim 1 or 2, characterized in that in the bis-carbazinic ester diols the radical R is an ethylene and/or 1,2-propylene radical.

Claim 6

The coating composition as claimed in claim 1 or 2, characterized in that aliphatic diols and triols containing tertiary amino groups are used as component (A)(2)(d).

Claim 7

The coating composition as claimed in claim 1 or 2, characterized in that the NCO-prepolymers (A) are prepared using cycloaliphatic diisocyanates in NCO/OH-molar ratios between the components ##EQU3## of from about 1.7 to 2.5:1.

Claim 8

The coating composition as claimed in claim 1 or 2, characterized in that aliphatic and/or cycloaliphatic primary diamines are used as the polyamines (B) in an NCO/NH 2 ratio of from about 1.05:1 to 0.95:1.

Claim 9

The coating composition as claimed in claim 1 or 2, characterized in that the predominant diamine is a cycloaliphatic diamine corresponding to the following formula ##STR11## in which R 1 , R 2 , R 3 and R 4 independently of one another represent hydrogen or a C 1 -C 3 -alkyl group, with the proviso that at least about 75% of the diamine comprises the cis, cis-isomer when R 1 to R 4 all represent hydrogen.

Claim 10

A process for the preparation of a low-solvent thermosetting reactive polyurethane coating composition which hardens to form light-fast polyurethane ureas with improved resistance to light, oxidation, heat and hydrolysis, which comprises: (A) forming a ketoxime-blocked NCO-prepolymer by reacting (1) 1 mole of 2- to 4-functional relatively high molecular weight polyhydroxyl compounds having a molecular weight in the range from about 1000 to 4000, wherein said 1 mole comprises (a) from about 0.5 to 1.0 mole of a polyester carbonate having a molecular weight of from about 1000 to 4000 produced from diphenyl carbonate and ester glycols of ε-caprolactone and 1,6-hexane diol and (b) up to about 0.5 mole of 2-functional to 4-functional relatively high molecular weight polyester polyols having a molecular weight of from about 1000 to 4000; and (2) from about 0.1 to 1.2 moles of low molecular weight polyols having molecular weights in the range from about 62 to 300, wherein said low molecular polyols comprise (c) from about 0.1 to 0.8 mole of bis-carbazinic ester polyols corresponding to the following general formula ##STR12## in which R is a straight-chain and/or branched-chain C 1 -C 5 -alkylene or hydroxyl-substituted alkylene radical and (d) up to about 1.1 mole of low molecular weight polyols; with (3) aliphatic and/or cycloaliphatic diisocyanates in an NCO:OH ratio between the components ##EQU4## of from about 1.5:1 to 6.1; and (4) subsequently blocking the terminal isocyanate groups with a substantially equivalent amount of ketoximes; (B) adding a crosslinking agent which comprises aliphatic and/or cycloaliphatic polyamines containing at least two primary amino groups at an NCO/NH 2 ratio of (A) to (B) between about 1.2:1 and 0.8:1; and (C) adding up to about 40% by weight based on the total weight of the coating composition, of at least one organic solvent before, during or after the production of (A) or the addition of (B) said organic solvent being sufficient to obtain a viscosity for the mixture of (A), (B) and (C) of from about 20,000 to 50,000 mPa.s at 20° C.

Claim 11

A process for the preparation of a low-solvent thermosetting reactive polyurethane coating composition which hardens to form light-fast polyurethane ureas with improved resistance to light, oxidation, heat and hydrolysis, which comprises: (A) forming a ketoxime-blocked NCO-prepolymer by reacting (1) 1 mole of 2- to 4-functional relatively high molecular weight polyhydroxyl compounds having a molecular weight in the range from about 1000 to 4000, wherein said 1 mole comprises (a) from about 0.5 to 1.0 mole of a polyester carbonate having a molecular weight of from about 1000 to 4000 produced from diphenyl carbonate and ester glycols of ε-caprolactone and 1,6-hexane diol and (b) up to about 0.5 mole of 2-functional to 4-functional relatively high molecular weight polyester polyols having a molecular weight of from about 1000 to 4000; and (2) from about 0.1 to 1.2 moles of low molecular weight polyols having molecular weights in the range from about 62 to 300, wherein said low molecular polyols comprise (c) from about 0.1 to 0.8 mole of bis-carbazinic ester polyols corresponding to the following general formula ##STR12## in which R is a straight-chain and/or branched-chain C 1 -C 5 -alkylene or hydroxyl-substituted alkylene radical and (d) up to about 1.1 mole of low molecular weight polyols; with (3) aliphatic and/or cycloaliphatic diisocyanates in an NCO:OH ratio between the components ##EQU4## of from about 1.5:1 to 6.1; and (4) subsequently blocking the terminal isocyanate groups with a substantially equivalent amount of ketoximes; (B) adding a crosslinking agent which comprises aliphatic and/or cycloaliphatic polyamines containing at least two primary amino groups at an NCO/NH 2 ratio of (A) to (B) between about 1.2:1 and 0.8:1; and (C) adding up to about 40% by weight based on the total weight of the coating composition, of at least one organic solvent before, during or after the production of (A) or the addition of (B) said organic solvent being sufficient to obtain a viscosity for the mixture of (A), (B) and (C) of from about 20,000 to 50,000 mPa.s at 20° C.

Claim 12

A process for the production of coatings which comprises applying the coating composition of claim 1 or 2 by the direct, reversal or matrix coating process and curing the said composition by heat to form polyurethane ureas.