Low density, microcellular foams, preparation, and articles
Assignee: United States Department of Energy
•
Filing: 1982-03-03
•
Granted: 1984-02-07
•
Expires: 2002-03-03
Abstract
Abstract A microcellular low density foam of poly(4-methyl-1-pentene) which is particularly useful for forming targets for inertial confinement fusion has been developed. Articles made from the foam have been machined to tolerances of 0.0001 inch, although the densities of the fragile foam are low (about 10 to about 100 mg/cc) and the cell sizes are small (about 10 to about 30 mu m). Methods for forming the foam and articles are given; and the yield strength of the foam of the invention is higher than was obtained in other structures of this same material.
Inventors
- 👤 Ainslie T. Young
- 👤 Robert G. Marsters
- 👤 Dawn K. Moreno
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 09:18
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/26; C08J3/00; C08J3/02; C08J3/09; C08J3/11; C08L; C08L23/00; C08L23/02; C08L23/18; C08L23/20; C08J2201/00; C08J2201/04; C08J2201/042; C08J2323/00; C08J2323/02; C08J2323/18; C08J2323/20
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
228 words
A method of forming a machinable composition of matter which after being leached forms a microcellular, low density foam of poly(4-methyl-1-pentene), said method comprising: (a) forming a mixture of poly(4-methyl-1-pentene) and solvent comprising bibenzyl such that the relative percent by weight of poly(4-methyl-1-pentene) in said mixture is within the range from about 1.0 to about 10.0 and the relative percent by weight of solvent in said mixture is within the range from about 99.0 to about 90.0; (b) heating said mixture to a first temperature sufficient so that complete solution of poly(4-methyl-1-pentene) and solvent occurs; (c) cooling said mixture down to a second temperature of about 180° C. and maintaining said second temperature for a period of time sufficient to enable said mixture to come to temperature equilibrium; (d) then cooling said mixture from about 180° C. at a rate within the range from about 0.9 to about 1.1° C. per minute down to a third temperature of about 160° C., thereby allowing reverse phase separation of said mixture to occur at a particular rate between said second temperature and said third temperature; (e) holding said mixture at said third temperature for a period of time sufficient to enable said mixture to come to temperature equilibrium; and (f) then allowing said mixture to cool down to room temperature, thus solidifying both said poly(4-methyl-1-pentene) and said solvent comprising bibenzyl.
Claim 2
Independent Claim
228 words
A method of forming a machinable composition of matter which after being leached forms a microcellular, low density foam of poly(4-methyl-1-pentene), said method comprising: (a) forming a mixture of poly(4-methyl-1-pentene) and solvent comprising bibenzyl such that the relative percent by weight of poly(4-methyl-1-pentene) in said mixture is within the range from about 1.0 to about 10.0 and the relative percent by weight of solvent in said mixture is within the range from about 99.0 to about 90.0; (b) heating said mixture to a first temperature sufficient so that complete solution of poly(4-methyl-1-pentene) and solvent occurs; (c) cooling said mixture down to a second temperature of about 180° C. and maintaining said second temperature for a period of time sufficient to enable said mixture to come to temperature equilibrium; (d) then cooling said mixture from about 180° C. at a rate within the range from about 0.9 to about 1.1° C. per minute down to a third temperature of about 160° C., thereby allowing reverse phase separation of said mixture to occur at a particular rate between said second temperature and said third temperature; (e) holding said mixture at said third temperature for a period of time sufficient to enable said mixture to come to temperature equilibrium; and (f) then allowing said mixture to cool down to room temperature, thus solidifying both said poly(4-methyl-1-pentene) and said solvent comprising bibenzyl.
Claim 3
Dependent Claim
31 words
A method according to claim 1, wherein said first temperature is a temperature within the range from about 220° to about 240° C. and wherein said solvent comprises also paraffin wax.
Claim 4
Dependent Claim
23 words
A method according to claim 2, wherein said second temperature is a temperature within the range from about 178° to about 182° C.
Claim 5
Dependent Claim
21 words
A method according to claim 3, wherein said third temperature is a temperature within the range from 158° to 162° C.
Claim 6
Dependent Claim
43 words
A method according to claim 4, wherein steps c through f are done without any agitation of said mixture and wherein said solvent consists of bibenzyl and paraffin wax in a relative weight ratio of bibenzyl: paraffin wax which is greater than 85:15.
Claim 7
Dependent Claim
22 words
A method according to claim 5 and including also the step of machining said machinable composition of matter which has been formed.
Claim 8
Dependent Claim
29 words
A method according to claim 6 and including also the step of leaching said bibenzyl from said machinable composition of matter so as to form a foam of poly(4-methyl-1-pentene).
Claim 9
Dependent Claim
22 words
A method according to claim 7, wherein said leaching is done by using a low molecular weight alcohol at about room temperature.
Claim 10
Dependent Claim
22 words
A method according to claim 5, wherein said solvent contains said paraffin wax in a relative amount of about 10 weight percent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-02-06 | 1987-08-08 | 1988-02-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-02-06 | 1991-08-08 | 1992-02-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-02-06 | 1995-08-08 | 1996-02-07 | $7700.00 | Window Closed / Lapsed |