Magnetic head slider material
Assignee: Nippon Tungsten Co Ltd
•
Filing: 1982-05-28
•
Granted: 1984-02-07
•
Expires: 2002-05-28
Abstract
Abstract A material for magnetic head sliders comprises a mixed powder consisting of 40 to 80% by weight of Al 2 O 3 and 20 to 60% by weight of TiO 2 , and further contains, per 100 parts by weight of the Al 2 O 3 and TiO 2 mixture, 0.5 to 5 parts by weight of at least one of CaO, MgO and Y 2 O 3 , and 0.5 to 10 parts by weight of ZrO 2 .
Inventors
- 👤 Toshiaki Wada
- 👤 Mitsuhiko Furukawa
- 👤 Michito Miyahara
- 👤 Masaharu Shiroyama
- 👤 Kiyohito Misumi
- 👤 Takashi Kitahira
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:30
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/46; C04B35/462; C04B35/478; G; G11; G11B; G11B5/00; G11B5/10; G11B5/102; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/11; Y10T428/1164
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
145 words
A wear-resistant product which is useful in fabricating magnetic head sliders, said product consisting essentially of 40 to 80% by weight of Al 2 O 3 , 20 to 60% by weight of TiO 2 , 0.5 to 5 parts by weight, based on 100 parts by weight of combined Al 2 O 3 and TiO 2 , of at least one oxide selected from the group consisting of CaO, MgO and Y 2 O 3 , and 0.5 to 10 parts by weight, based on 100 parts by weight of combined Al 2 O 3 and TiO 2 , of ZrO 2 which has a purity of at least 99.0% and maximum particle diameters of 2 microns; said product having a hardness of between about 89.0 and 89.3 (HrA) and a wear resistance of between about 0.1 and about 0.3 mm 3 (pin-disk method).
Claim 2
Dependent Claim
145 words
A wear-resistant product which is useful in fabricating magnetic head sliders, said product consisting essentially of 40 to 80% by weight of Al 2 O 3 , 20 to 60% by weight of TiO 2 , 0.5 to 5 parts by weight, based on 100 parts by weight of combined Al 2 O 3 and TiO 2 , of at least one oxide selected from the group consisting of CaO, MgO and Y 2 O 3 , and 0.5 to 10 parts by weight, based on 100 parts by weight of combined Al 2 O 3 and TiO 2 , of ZrO 2 which has a purity of at least 99.0% and maximum particle diameters of 2 microns; said product having a hardness of between about 89.0 and 89.3 (HrA) and a wear resistance of between about 0.1 and about 0.3 mm 3 (pin-disk method).
Claim 3
Dependent Claim
16 words
A wear-resistant product as defined in claim 1 which has been formed by hot isostatic pressing.
Claim 4
Dependent Claim
14 words
A wear-resistant product as defined in claim 1 which has been formed by sintering.
Claim 5
Dependent Claim
52 words
A wear-resistant product as defined in claim 1 which displays a specific gravity of 3.99 to 4.0, a hardness of 89.1 to 89.3 (HrA), a breaking strength of 46 to 48 Kg/mm 2 , a thermal conductivity of about 0.0273 cal/mm sec.°C., and an electrical resistance of at least 10 6 Ωcm.
Claim 6
Dependent Claim
12 words
A magnetic head slider which includes the wear-resistant product of claim 1.
References Cited (Backward Citations)
US3301646A
Cited
US3665436A
Cited
US4130847A
Cited
US4194917A
Cited
DE2741295A1
Cited
US4331627A
Cited
US4251841A
Cited
US4314827A
Cited
US4248440A
Cited
US4316964A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-02-06 | 1987-08-08 | 1988-02-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-02-06 | 1991-08-08 | 1992-02-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-02-06 | 1995-08-08 | 1996-02-07 | $7700.00 | Window Closed / Lapsed |