Process for treating spent fluids to recover copper and copper oxide
Assignee: AT&T Inc
•
Filing: 1982-12-30
•
Granted: 1984-01-31
•
Expires: 2002-12-30
Abstract
Abstract A process for recovering copper and copper oxide for spent ammoniacal etchant, electroless and copper persulfate bath fluids used in the manufacture of copper printed wiring boards such that the treated baths contain no ammonia. The spent solutions are placed in a cooking vessel having its inner surface made of titanium and the formaldehyde is added. The ingredients are then stirred while air is bubbled through the ingredients until thoroughly mixed after which the pH of the mixture is adjusted to between 12.0 and 14.0. The adjusted mixture is now heated to a temperature within the range of 200°-210° F. and air is bubbled through the heated mixture until copper and copper oxide precipitates form in the mixture. After the precipitates form the mixture is allowed to cool to permit the precipitates to settle to the bottom of the vessel and the mixture is decanted from the vessel. The copper and copper oxide precipitates are washed and then collected.
Inventors
- 👤 Kenneth J. Krotz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:00
CPC Classifications
C; C01; C01G; C01G3/00; C01G3/02; C22; C22B; C22B15/00; C22B15/0063; C22B15/0084; C22B15/0089; C22B15/0093; C22B7/00; C22B7/006; C22B7/008; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
136 words
A process for recovering copper and copper oxide from a combination of spent ammoniacal etchant, electroless and copper ammonium persulfate bath solutions used in the manufacture of printed wiring boards and for producing an ammonia free decant solution comprising the steps of: placing the combination and formaldehyde in the ratio of approximately one gallon of formaldehyde per fourteen gallons of the combination in a cooking vessel having its inner surface coated with titanium; stirring and bubbling air through the contents of the vessel; adjusting the pH of the mixture to be within the range of 12.0 to 14.0; and heating the adjusted mixture to a temperature of 200°-210° F. (93.3°-98.9° C.) while bubbling air through the mixture until copper and copper oxide precipitates are formed in the heated mixture such that the mixture is ammonia free.
Claim 2
Dependent Claim
136 words
A process for recovering copper and copper oxide from a combination of spent ammoniacal etchant, electroless and copper ammonium persulfate bath solutions used in the manufacture of printed wiring boards and for producing an ammonia free decant solution comprising the steps of: placing the combination and formaldehyde in the ratio of approximately one gallon of formaldehyde per fourteen gallons of the combination in a cooking vessel having its inner surface coated with titanium; stirring and bubbling air through the contents of the vessel; adjusting the pH of the mixture to be within the range of 12.0 to 14.0; and heating the adjusted mixture to a temperature of 200°-210° F. (93.3°-98.9° C.) while bubbling air through the mixture until copper and copper oxide precipitates are formed in the heated mixture such that the mixture is ammonia free.
Claim 3
Dependent Claim
51 words
A process as recited in claim 1 comprising the additional steps of: cooling the heated mixture to permit the copper and copper oxide precipitates to settle to the bottom of the vessel; decanting the ammonia free mixture from the vessel; and washing the copper and copper oxide precipitate to remove impurities.
Claim 4
Dependent Claim
18 words
A process as recited in claim 1 wherein the stirring step is performed for at least an hour.
Claim 5
Dependent Claim
31 words
A process as recited in claim 1 wherein the adjusting step is performed by adding sodium hydroxide to the mixture until the pH of the mixture is between 12.8 and 13.0.
Claim 6
Dependent Claim
25 words
A process as recited in claim 1 wherein the heating step is performed by discharging live steam into the mixture for at least four hours.
Claim 7
Dependent Claim
29 words
A process as recited in claim 1 wherein air is bubbled through the mixture during the stirring and heating steps at the rate of 120 cubic feet per minute.
Claim 8
Dependent Claim
148 words
A process for treating spent ammoniacal etchant, electroless and copper ammonium persulfate bath solutions to recover copper and copper oxide from the solutions and to form an ammonia free decant mixture comprising the steps of: placing the spent solutions in a vessel having its inner surface made of titanium; adding formaldehyde to the solutions in the proportion of 1 gallon of formaldehyde to approximately 18.3 gallons of spent solutions; stirring the solutions at ambient temperature; bubbling air through the solutions at the rate of 120 cfm while the solutions are being stirred; adding sufficient sodium hydroxide to the mixture until the pH of the mixture is adjusted to be within the range of 12.8 to 13.0; and heating the adjusted mixture until copper and copper oxide precipitates are formed in the mixture while bubbling air through the heated mixture to form an ammonia free mixture suitable for decanting.
Claim 9
Dependent Claim
148 words
A process for treating spent ammoniacal etchant, electroless and copper ammonium persulfate bath solutions to recover copper and copper oxide from the solutions and to form an ammonia free decant mixture comprising the steps of: placing the spent solutions in a vessel having its inner surface made of titanium; adding formaldehyde to the solutions in the proportion of 1 gallon of formaldehyde to approximately 18.3 gallons of spent solutions; stirring the solutions at ambient temperature; bubbling air through the solutions at the rate of 120 cfm while the solutions are being stirred; adding sufficient sodium hydroxide to the mixture until the pH of the mixture is adjusted to be within the range of 12.8 to 13.0; and heating the adjusted mixture until copper and copper oxide precipitates are formed in the mixture while bubbling air through the heated mixture to form an ammonia free mixture suitable for decanting.
Claim 10
Dependent Claim
34 words
A process as recited in claim 7 wherein: the heating step is achieved by applying live steam to heat the mixture in the vessel for approximately four hours to a temperature of 200°-210° F.
Claim 11
Dependent Claim
61 words
A process as recited in claim 7 further comprising the steps of: cooling the mixture to allow the precipitates to settle to the bottom of the vessel; decanting the cooled ammonia free mixture from the vessel; washing the precipitates to remove impurities; and removing the cleaned precipitates from the bottom of the vessel by vacuum belt filtration to remove excess water.
Claim 12
Dependent Claim
136 words
A process for treating spent electroless plating and copper ammonium persulfate bath solutions to prevent ammonia from forming in the treated solutions and to recover copper and copper oxide from the spent solutions comprising the steps of: placing the spent solutions in a vessel having its inner surface made of titanium; adding formaldehyde to the vessel in the ratio of approximately three gallons of formaldehyde to five gallons of the spent solutions; stirring the contents of the vessel while also bubbling air through the stirred contents; adjusting the pH of the mixture until the pH is within the range of 12.0 to 14.0; and heating the adjusted mixture in the vessel while bubbling air through the mixture until copper and copper oxide precipitates are formed in the mixture such that the mixture is free of ammonia.
Claim 13
Dependent Claim
136 words
A process for treating spent electroless plating and copper ammonium persulfate bath solutions to prevent ammonia from forming in the treated solutions and to recover copper and copper oxide from the spent solutions comprising the steps of: placing the spent solutions in a vessel having its inner surface made of titanium; adding formaldehyde to the vessel in the ratio of approximately three gallons of formaldehyde to five gallons of the spent solutions; stirring the contents of the vessel while also bubbling air through the stirred contents; adjusting the pH of the mixture until the pH is within the range of 12.0 to 14.0; and heating the adjusted mixture in the vessel while bubbling air through the mixture until copper and copper oxide precipitates are formed in the mixture such that the mixture is free of ammonia.
Claim 14
Dependent Claim
20 words
A process as recited in claim 10 wherein the final heating step is continued until the mixture becomes substantially colorless.
Claim 15
Dependent Claim
31 words
A process as recited in claim 10 wherein during the heating step the mixture is heated to a temperature in the range of 200°-210° F. by discharging steam into the mixture.
Claim 16
Dependent Claim
56 words
A process as recited in claim 10 comprising the additional steps of: cooling the ammonia free mixture to permit the copper and copper oxide precipitates to settle to the bottom of the vessel; decanting the mixture from the vessel; and washing the copper and copper oxide precipitates with deionized water to remove impurities from the precipitates.
Claim 17
Dependent Claim
143 words
A process for treating a spent ammoniacal etchant bath solution used in the manufacture of copper printed wiring boards to prevent the formation of ammonia in the treated solution and to recover copper and copper oxide from the solution comprising the steps of: placing the spent solution in a vessel having its inner surface made of titanium; adding formaldehyde to the solution in the quantity of approximately 1 gallon formaldehyde to 20 gallons of spent etchant solution; stirring the contents of the vessel while bubbling air through the contents; adjusting the pH of the mixture to within the range of 12.0 to 14.0; and heating the adjusted mixture while air is being bubbled through the adjusted mixture until copper and copper oxide precipitates are formed in the heated mixture or until the mixture becomes substantially colorless such that the mixture is ammonia free.
Claim 18
Dependent Claim
143 words
A process for treating a spent ammoniacal etchant bath solution used in the manufacture of copper printed wiring boards to prevent the formation of ammonia in the treated solution and to recover copper and copper oxide from the solution comprising the steps of: placing the spent solution in a vessel having its inner surface made of titanium; adding formaldehyde to the solution in the quantity of approximately 1 gallon formaldehyde to 20 gallons of spent etchant solution; stirring the contents of the vessel while bubbling air through the contents; adjusting the pH of the mixture to within the range of 12.0 to 14.0; and heating the adjusted mixture while air is being bubbled through the adjusted mixture until copper and copper oxide precipitates are formed in the heated mixture or until the mixture becomes substantially colorless such that the mixture is ammonia free.
Claim 19
Dependent Claim
53 words
A process as recited in claim 14 comprising the additional steps of: cooling the heated ammonia free mixture to allow the copper and copper oxide precipitates to settle at the bottom of the vessel; decanting the ammonia free mixture from the vessel; and washing the copper and copper oxide precipitates to remove impurities.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-01-30 | 1987-08-01 | 1988-01-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-01-30 | 1991-08-01 | 1992-01-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-01-30 | 1995-08-01 | 1996-01-31 | $7700.00 | Window Closed / Lapsed |