Abstract
Abstract A solvent-free preform of a 3-hydroxybutyric acid polymer is subjected to a compression step to reduce its thickness by at least 5% and the compressed preform is then drawn uni- or bi- axially to induce orientation.
Inventors
- 👤 Peter J. Barham
- 👤 Paul A. Holmes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 13:48
CPC Classifications
C; C07; C07D; C07D295/00; C07D295/04; C07D295/08; C07D295/096; C07C; C07C17/00; C07C17/093; C07C17/16; C07C29/00; C07C29/132; C07C29/136; C07C29/147; C07C405/00; C07C405/0008; C07C405/0033; C07C405/0041; C07C45/00; C07C45/27; C07C45/30; C07D267/00; C07D267/02; C07D267/08; C07D267/10; C07D295/10; C07D295/112; C07D295/14; C07D295/155; C07D307/00; C07D307/77; C07D307/93; C07D307/935; C07D309/00; C07D309/02; C07D309/08; C07D309/10; C07D309/12; C07D311/00; C07D333/00; C07D333/02; C07D333/04; C07D333/06; C07D333/12; C07D333/14; C07D333/16; C07D333/22; C07D333/24; D; D01; D01F; D01F6/00; D01F6/58; D01F6/62; D01F6/625; Y; Y10; Y10S; Y10S428/00; Y10S428/91
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
74 words
A process for the production of a shaped article from a polymeric material in which 3-hydroxybutyric acid residues form at least 40 mole % of the polymer chain comprising subjecting a solvent-free preform of the polymer to compressive force at a temperature between the glass transition temperature and the crystalline melting point of the polymer so that its thickness is reduced by at least 5%, and thereafter drawing the compressed preform uni- or bi-axially.
Claim 2
Dependent Claim
74 words
A process for the production of a shaped article from a polymeric material in which 3-hydroxybutyric acid residues form at least 40 mole % of the polymer chain comprising subjecting a solvent-free preform of the polymer to compressive force at a temperature between the glass transition temperature and the crystalline melting point of the polymer so that its thickness is reduced by at least 5%, and thereafter drawing the compressed preform uni- or bi-axially.
Claim 3
Dependent Claim
31 words
A process according to claim 1 wherein the preform is subjected to said compressive force at a temperature between 50° and 150° C. below the crystalline melting point of the polymer.
Claim 4
Dependent Claim
31 words
A process according to claim 1 or claim 2 wherein the compressed preform is drawn at a temperature between 40° to 90° C. below the crystalline melting point of the polymer.
Claim 5
Dependent Claim
21 words
A process according to claim 1 wherein the preform is compressed by pressing the preform between the plattens of a press.
Claim 6
Dependent Claim
24 words
A process according to claim 1 wherein the preform is compressed by passing the preform through the nip of a pair of nip rollers.
Claim 7
Dependent Claim
21 words
A process according to claim 1 wherein the preform is compressed by solid state extrusion of the preform through a die.
Claim 8
Dependent Claim
38 words
A process according to claim 5 wherein the preform is passed between the nip of a pair of nip rollers prefiled corresponding to the desired cross-section of the compressed preform and then the rolled preform is drawn uniaxially.
Claim 9
Dependent Claim
19 words
A process according to claim 1 wherein the draw ratio, in at least one direction, is at least 1.5:1.
Claim 10
Dependent Claim
35 words
A process according to claim 1 wherein the amount of compression and the draw ratio in the drawing step are such that the overall draw ratio in at least one direction is at least 3:1.
Claim 11
Dependent Claim
50 words
A process according to claim 9 wherein the compressed preform is drawn uniaxially and the amount of compression and the draw ratio in the drawing step are such that the length of the drawn preform is at least four times the length of the preform prior to the compression step.
Claim 12
Dependent Claim
21 words
A process according to claim 1 wherein the preform is produced by melt processing the polymeric material into the desired shape.
Claim 13
Dependent Claim
99 words
A process for the production of an oriented film from a polymeric material in which 3-hydroxybutyric acid residues form at least 40 mole % of the polymer chain compressing applying a solution of said polymeric material in a solvent therefore to a surface, evaporating solvent from said solution to form a solution cast film, subjecting said film to a compressive force at a temperature between the glass transition temperature and the crystalline melting point of the polymer so that the thickness of the film is reduced by at least 5%, and thereafter drawing the compressed film uni- or bi-axially.
Claim 14
Dependent Claim
99 words
A process for the production of an oriented film from a polymeric material in which 3-hydroxybutyric acid residues form at least 40 mole % of the polymer chain compressing applying a solution of said polymeric material in a solvent therefore to a surface, evaporating solvent from said solution to form a solution cast film, subjecting said film to a compressive force at a temperature between the glass transition temperature and the crystalline melting point of the polymer so that the thickness of the film is reduced by at least 5%, and thereafter drawing the compressed film uni- or bi-axially.
References Cited (Backward Citations)
US4360488A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-01-23 | 1987-07-25 | 1988-01-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-01-23 | 1991-07-25 | 1992-01-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-01-23 | 1995-07-25 | 1996-01-24 | $7700.00 | Window Closed / Lapsed |