Method for producing sapphire tubes
Assignee: Individual
•
Filing: 1982-01-07
•
Granted: 1983-11-22
•
Expires: 2002-01-07
Abstract
Abstract During the process of pulling sapphire tubes from a melt with the aid of a seed, the longitudinal temperature gradient in the zone between the solidified front and the region of pulling where the temperature is between 1850 and 1900 deg. C. is maintained not in excess of 30 deg. C./cm. The tube so grown is annealed at a temperature between 1950 and 2000 deg. C. by increasing the temperature at a rate of 30 to 40 deg. C./min and keeping the tube at said temperature during a period between 3 and 4 hours. After that the tube is cooled down to room temperature at a rate of 30-40 deg. C./min. Disclosed is also an apparatus which enables said temperature gradient to be maintained while pulling the tube.
Inventors
- 👤 Boris B. Pelts
- 👤 Beniamin A. Tumasian
- 👤 Leonid P. Egorov
- 👤 Lev M. Zatulovsky
- 👤 Peter M. Chaikin
- 👤 Efim A. Freiman
- 👤 Eduard A. Chalian
- 👤 Grant I. Abramian
- 👤 Stepan E. Azoian
- 👤 Kliment A. Kostandian
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 14:55
CPC Classifications
C; C30; C30B; C30B15/00; C30B15/34; C30B15/005; C30B29/00; C30B29/10; C30B29/16; C30B29/20; C30B29/60; C30B29/66
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
107 words
A method for producing a crystalline sapphire tube comprising melting a material for producing said tube, pulling a tube from said melt using a seed through a die under an inert-gas blanket, maintaining a longitudinal temperature gradient of not more than 30° C./cm in the wall of said tube within a zone between a solidified front of said tube and a pulling region wherein the temperature is 1850 to 1900° C., annealing said tube at a temperature between 1950 and 2000° C. by heating said tube at a rate of 30 to 40° C./min, and cooling said annealed tube at a rate of 30° to 40° C./min.
Claim 2
Independent Claim
107 words
A method for producing a crystalline sapphire tube comprising melting a material for producing said tube, pulling a tube from said melt using a seed through a die under an inert-gas blanket, maintaining a longitudinal temperature gradient of not more than 30° C./cm in the wall of said tube within a zone between a solidified front of said tube and a pulling region wherein the temperature is 1850 to 1900° C., annealing said tube at a temperature between 1950 and 2000° C. by heating said tube at a rate of 30 to 40° C./min, and cooling said annealed tube at a rate of 30° to 40° C./min.
Claim 3
Dependent Claim
16 words
A method as claimed in claim 1 wherein the annealing lasts between 3 and 4 hours.
Claim 4
Dependent Claim
17 words
The method of claim 1 in which said tube is anneled for between 3 and 4 hours.
Claim 5
Dependent Claim
14 words
The method of claim 1 in which said tube is cooled to room temperature.
Claim 6
Dependent Claim
15 words
The method of claim 1 in which said temperature gradient is 10° to 20° C./cm.
Claim 7
Dependent Claim
56 words
The method of claim 1, wherein a longitudinal temperature gradient of not more than 30° C./cm in the wall of said tube within fthe zone between a solidified front of said tube and a pulling region wherein the temperature is 1850° to 1900° C. is provided by heat-insulating shields and pins mad of heat conducting material.
Claim 8
Independent Claim
148 words
A method for producing a crystalline sapphire tube comprising melting aluminum oxide by means of induction heating in an air-tight chamber, pulling a tube from said melt using a seed through a die under an inert-gas blanket and an excess pressure between 0.1 to 0.3 atm. gauge, maintaining a longitudinal temperature gradient of 10° to 20° C./cm in the wall of said tube within a zone between a solidified front and a pulling region wherein the temperature is 1850° to 1900° C., said temperature gradient being maintained at least partially by regulating convective gas flow upstream of said die in said pulling region, annealing said tube at a temperature between 1950° and 2000° C. by heating said tube at a rate of 30° to 40° C./min for between 3 and 4 hours, and cooling said annealed tube to room temperature at a rate of 30° to 40° C./cm.
Claim 9
Independent Claim
148 words
A method for producing a crystalline sapphire tube comprising melting aluminum oxide by means of induction heating in an air-tight chamber, pulling a tube from said melt using a seed through a die under an inert-gas blanket and an excess pressure between 0.1 to 0.3 atm. gauge, maintaining a longitudinal temperature gradient of 10° to 20° C./cm in the wall of said tube within a zone between a solidified front and a pulling region wherein the temperature is 1850° to 1900° C., said temperature gradient being maintained at least partially by regulating convective gas flow upstream of said die in said pulling region, annealing said tube at a temperature between 1950° and 2000° C. by heating said tube at a rate of 30° to 40° C./min for between 3 and 4 hours, and cooling said annealed tube to room temperature at a rate of 30° to 40° C./cm.
Claim 10
Dependent Claim
55 words
A method according to claim 7 wherein the longitudinal temperature gradient of 10° to 20° C. per centimeter in the wall of said tube within a zone between a solidified front and a pulling region wherein the temperature is 1850° to 1900° C. is provided by heat-insulating shields and pins made of heat conducting material.
Claim 11
Dependent Claim
31 words
A method according to claim 8 wherein the regulation of the convective gas flow upstream of said die and said pulling region is provide by perforations in the heat insulating shields.
References Cited (Backward Citations)
US3953174A
Cited
US4184907A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-21 | 1987-05-23 | 1987-11-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-21 | 1991-05-23 | 1991-11-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-21 | 1995-05-23 | 1995-11-22 | $7700.00 | Window Closed / Lapsed |