Supported catalysts and process for their preparation
Assignee: Bayer AG
•
Filing: 1981-07-20
•
Granted: 1983-10-04
•
Expires: 2001-07-20
Abstract
Abstract A process for the preparation of a supported catalyst containing a catalytically active metal such as a noble metal is disclosed wherein the supported catalyst is prepared by initially contacting the inert support with a base and disposing an amount of base in the support corresponding to 0.01 to 50 gram equivalents of base per gram equivalent of catalytically active metal to be deposited thereon, drying the so-treated support to a residual moisture content of less than 10 percent of the maximum absorbency of the support and thereafter impregnating the same with a salt solution of a catalytically active metal, e.g., a salt of a catalytically active noble metal. The inert support is one having a BET surface area of less than 20 square meters per gram. The catalyst is useful in hydrogenation, dehydrogenation, hydrogenolysis, oxidation, polymerization, isomerization or cyclization reactions.
Inventors
- 👤 Udo Birkenstock
- 👤 Herbert Schmidt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 10:26
CPC Classifications
C; C07; C07C; C07C209/00; C07C209/30; C07C209/32; C07C209/36; B; B01; B01J; B01J23/00; B01J23/38; B01J23/40; B01J37/00; B01J37/02; B01J37/0201; B01J37/03; C07C29/00; C07C29/17; C07C29/19; C07C29/20; C07C45/00; C07C45/006; B01J23/44; B01J23/70; B01J23/89; B01J35/00; B01J35/60; B01J35/61; B01J35/613; C07C2601/00; C07C2601/12; C07C2601/14
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
180 words
A supported catalyst comprising an inert support material having a BET surface area of less than 20 square meters per gram and a catalytically active material disposed in an annular zone located inside and just below the surface of said inert support prepared by a process consisting essentially of: A. contacting said inert support, prior to any impregnation with the catalytically active metal in accordance with its absorbency to saturation, with a solution of a base so as to dispose within said inert support 0.01 to 50 grams equivalents of base per gram equivalent of catalytically active metal to be impregnated within said inert support; B. drying the so-base-treated inert support at a temperature of 50° to 200° C. so that said inert support has a constant weight and has a residual moisture content of less than 10 percent of the maximum obsorbency of the support; and C. impregnating the so-dried inert material in accordance with its absorbency to saturation with a solution of a catalytically active metal; and D. washing, drying and reducing or calcining the so-impregnated inert material.
Claim 2
Dependent Claim
180 words
A supported catalyst comprising an inert support material having a BET surface area of less than 20 square meters per gram and a catalytically active material disposed in an annular zone located inside and just below the surface of said inert support prepared by a process consisting essentially of: A. contacting said inert support, prior to any impregnation with the catalytically active metal in accordance with its absorbency to saturation, with a solution of a base so as to dispose within said inert support 0.01 to 50 grams equivalents of base per gram equivalent of catalytically active metal to be impregnated within said inert support; B. drying the so-base-treated inert support at a temperature of 50° to 200° C. so that said inert support has a constant weight and has a residual moisture content of less than 10 percent of the maximum obsorbency of the support; and C. impregnating the so-dried inert material in accordance with its absorbency to saturation with a solution of a catalytically active metal; and D. washing, drying and reducing or calcining the so-impregnated inert material.
Claim 3
Dependent Claim
34 words
A catalyst according to claim 1 wherein said supported catalyst comprises a noble metal in compound or elemental form and said solution of a metal salt is a solution of a noble metal salt.
Claim 4
Dependent Claim
156 words
A process for preparing a supported catalyst according to claim 1, which consists essentially of the steps of: A. contacting an inert support material having a BET surface area of less than 20 square meters per gram with a base such as to dispose within said inert support material 0.01 to 50 gram equivalents of base per gram equivalent of metal to be inserted pursuant to step C; B. drying the so-base-treated inert support at a temperature of 50°-200° C. so that said inert support has a constant weight and a residual moisture content of less than 10 percent of the maximum absorbency of the support; C. impregnating the so-dried inert support material with a salt solution of a catalytically active metal; and D. washing, drying, and reducing or calcining the so-impregnated inert material whereby the catalytically active metal is disposed in an annular zone located inside and just below the surface of said inert support.
Claim 5
Dependent Claim
24 words
A supported catalyst according to claim 1 wherein said catalytically active metal is present on or in said support in elemental or compound form.
Claim 6
Dependent Claim
30 words
A process according to claim 3 wherein following impregnation of said support material with said solution of said catalytically active metal the metal on or in said support is reduced.
Claim 7
Dependent Claim
23 words
A process according to claim 3 wherein said inert support is a metal oxide, silicate, spinel, carbide, or carbonate or a mixture thereof.
Claim 8
Dependent Claim
45 words
A process according to claim 3 wherein the amount of base added to said inert support is 0.5 to 20 gram equivalents per gram equivalent of metal applied in accordance with step C and said base is added in the form of an aqueous solution.
Claim 9
Dependent Claim
29 words
A process according to claim 3 wherein step B is carried out until the residual moisture content of the support is less than 2 percent of its maximum absorbency.
Claim 10
Dependent Claim
24 words
A process according to claim 3 wherein the base is an oxide, carbonate, bicarbonate, hydrogen phosphate, hydroxide, alkoxide, or formate or a mixture thereof.
Claim 11
Dependent Claim
40 words
A process according to claim 3 wherein the impregnation of step C is carried out to saturation with a salt solution of a metal of Groups IIIb, IVa, IVb, Va, Vb, VIa, VIIIa, Ib or IIb of the Periodic Table.
Claim 12
Dependent Claim
14 words
A supported catalyst according to claim 1 wherein said catalytically active metal is palladium.
Claim 13
Dependent Claim
13 words
A supported catalyst according to claim 11 wherein said inert support is α-alumina.
Claim 14
Dependent Claim
11 words
A support according to claim 1 wherein said metal is iron.
Claim 15
Dependent Claim
11 words
A support according to claim 1 wherein said metal is nickel.
Claim 16
Dependent Claim
11 words
A support according to claim 1 wherein said metal is cobalt.
Claim 17
Dependent Claim
11 words
A support according to claim 1 wherein said metal is manganese.
Claim 18
Dependent Claim
16 words
A support according to claim 1 wherein said inert support is impregnated with palladium and iron.
Claim 19
Dependent Claim
17 words
A supported catalyst according to claim 1 wherein said metal is a mixture of palladium and nickel.
Claim 20
Dependent Claim
17 words
A supported catalyst according to claim 1 wherein said metal is a mixture of palladium and cobalt.
Claim 21
Dependent Claim
17 words
A supported catalyst according to claim 1 wherein said metal is a mixture of palladium and manganese.
Claim 22
Dependent Claim
18 words
A supported catalyst according to claim 1 wherein said metal comprises a mixture of palladium, copper, and chromium.
Claim 23
Dependent Claim
17 words
A supported catalyst according to claim 1 wherein said metal comprises a mixture of palladium and bismuth.
Claim 24
Dependent Claim
17 words
A supported catalyst according to claim 1 wherein said metal comprises a mixture of palladium and gold.
Claim 25
Dependent Claim
12 words
A supported catalyst according to claim 1 wherein said metal comprises thorium.
Claim 26
Dependent Claim
12 words
A supported catalyst according to claim 1 wherein said metal is samarium.
Claim 27
Dependent Claim
12 words
A supported catalyst according to claim 1 wherein said metal is titanium.
Claim 28
Dependent Claim
12 words
A supported catalyst according to claim 1 wherein said metal is silver.
References Cited (Backward Citations)
US3036137A
Cited
US3116342A
Cited
DE1944933U
Cited
US3839225A
Cited
US4094821A
Cited
US4171329A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-03 | 1987-04-04 | 1987-10-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-03 | 1991-04-04 | 1991-10-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-03 | 1995-04-04 | 1995-10-04 | $7700.00 | Window Closed / Lapsed |