Method for molding contact lenses using microwave energy
Assignee: Ciba Vision Corp
•
Filing: 1981-02-27
•
Granted: 1983-06-28
•
Expires: 2001-02-27
Abstract
Abstract The invention relates to a fabrication method for molding a contact lens with the required optical qualities. This method consists in designing a mold (1, 2) of high thermal inertia, which is transparent to, or little absorbing the electromagnetic microwave frequencies between 10 6 Hz and 10 11 Hz, in developing a base composition from polymerizing double-bond monomers which are absorbing with respect to the above microwaves, and in ensuring the polymerization of the composition within the closed mold by irradiation with the above cited electromagnetic waves at a power density suited to keep the temperature at the mold level approximately below 40° C.
Inventors
- 👤 Bernard Feurer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:29
CPC Classifications
G; G02; G02B; G02B1/00; G02B1/04; G02B1/041; G02B1/043; B; B29; B29D; B29D11/00; B29D11/00009; B29D11/00038; B29D11/00125; Y; Y10; Y10S; Y10S425/00; Y10S425/808
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
232 words
A method for producing a finished contact lens comprising: providing a mold of male and female parts substantially transparent to microwave energy within the range of about 10 6 Hz to 10 11 Hz, said mold having a heat capacity significantly greater than the amount of the composition being molded whereby heat generated during molding may be dissipated without raising the temperature of said mold above about 40° C., each said male and female part having a unitary mold surface rigid at temperatures below about 40° C., said parts being adapted to interfit with the peripheries of said mold surfaces in contact so as to form an airtight closed mold cavity, said unitary male mold surface and said unitary female mold surface alone forming in its entirety the final undeformed shape of the lens to be molded, introducing a polymerizable lens forming monomer into said mold cavity and interfitting said mold parts so as to close said mold cavity, irradiating said monomer containing mold substantially uniformly with microwave energy at a frequency within the range of about 10 6 Hz to 10 11 Hz and at a power density such as to keep the temperature of said mold below about 40° C. so as to polymerize said monomer without detachment of the lens material from said mold surfaces and without deformation of said mold surfaces, and removing the lens from said mold.
Claim 2
Independent Claim
232 words
A method for producing a finished contact lens comprising: providing a mold of male and female parts substantially transparent to microwave energy within the range of about 10 6 Hz to 10 11 Hz, said mold having a heat capacity significantly greater than the amount of the composition being molded whereby heat generated during molding may be dissipated without raising the temperature of said mold above about 40° C., each said male and female part having a unitary mold surface rigid at temperatures below about 40° C., said parts being adapted to interfit with the peripheries of said mold surfaces in contact so as to form an airtight closed mold cavity, said unitary male mold surface and said unitary female mold surface alone forming in its entirety the final undeformed shape of the lens to be molded, introducing a polymerizable lens forming monomer into said mold cavity and interfitting said mold parts so as to close said mold cavity, irradiating said monomer containing mold substantially uniformly with microwave energy at a frequency within the range of about 10 6 Hz to 10 11 Hz and at a power density such as to keep the temperature of said mold below about 40° C. so as to polymerize said monomer without detachment of the lens material from said mold surfaces and without deformation of said mold surfaces, and removing the lens from said mold.
Claim 3
Dependent Claim
51 words
A method as in claim 1 and wherein said polymerizable lens forming monomer is selected from the group consisting of allyl monomers, vinyl monomers, or a mixture of ally and vinyl monomers, and conducting said irradiation with microwave energy at a frequency of between 2×10 8 Hz and 4×10 9 Hz.
Claim 4
Dependent Claim
46 words
A method as in claim 1 and wherein said mold is formed from a non-charged polymer selected from the group consisting of polypropylene and polyethylene, and carrying out said irradiation with microwave energy at a frequency of between about 2×10 8 Hz and 4×10 9 Hz.
Claim 5
Dependent Claim
16 words
A method as in claim 1 and including adding a polymerization initiator to said polymerizable monomer.
Claim 6
Dependent Claim
44 words
A method as in claim 1 and wherein one of said mold surfaces is concave so as to form the convex side of the lens, and the other of said mold surfaces is convex so as to form the other side of said lens.
Claim 7
Dependent Claim
42 words
A method as in claim 1, 2, 3 or 4 and wherein said polymerizable lens forming monomer is selected from the group consisting of hydroxyethyl methacrylate, hydroxypropyl methacrylate, hydroxyethyl acrylate, ethyleneglycol dimethacrylate, vinyl pyrrolidone, glycidyl methacrylate, methacrylamide, bisphenol A bis(2 hydroxypropyl methacrylate).
Claim 8
Dependent Claim
31 words
A method as in claim 6 and wherein said polymerizable lens forming monomer includes at least one linear polymer selected from the group consisting of polyglycidyl methacrylate, polymethyl methacrylate, polyvinyl pyrrolidone.
Claim 9
Dependent Claim
17 words
A method as in claim 6 and including carrying out said irradiation step at substantially atmospheric pressure.
Claim 10
Dependent Claim
21 words
A method as in claim 6 and including carrying out said irradiation at a pressure of about 2 to 10 bars.
Claim 11
Dependent Claim
22 words
A method as in claim 6 and wherein said power density is between about 0.5×10 -3 and 1,000×10 -3 watt/cm 3 .
Claim 12
Dependent Claim
15 words
A process as in claim 10 and including cooling said mold during said irradiation step.
Claim 13
Dependent Claim
33 words
A method as in claim 1, 2, 3 or 4 and wherein said mold has a mass at least 20 times the mass of said polymerizable lens forming monomer in said mold cavity.
References Cited (Backward Citations)
US3171869A
Cited
US4073577A
Cited
US4121896A
Cited
US4138086A
Cited
US4159292A
Cited
US4166088A
Cited
US4179484A
Cited
US4209289A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-06-27 | 1986-12-27 | 1987-06-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-06-27 | 1990-12-27 | 1991-06-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-06-27 | 1994-12-27 | 1995-06-28 | $7700.00 | Window Closed / Lapsed |