Treatment of formaldehyde laden wood panels to reduce excess formaldehyde
Assignee: RELIANCE UNIVERSAL Inc A CORP OF KY
•
Filing: 1980-10-27
•
Granted: 1983-03-15
•
Expires: 2000-10-27
Abstract
Abstract A substantial reduction of free excess formaldehyde in formaldehyde laden wood panels is achieved by coating at least one side of the panel with a salt solution containing an ammonium cation such as a 10-15% aqueous solution of ammonium bicarbonate. After coating, a barrier is placed over the coated surface such as by stacking a plurality of similarly coated panels with the barrier being maintained sufficiently long to allow ammonia gas generated from normal degradation of the ammonium salt to migrate to the free formaldehyde zone where the ammonia gas reacts with the formaldehyde to produce a stable, low volatility reaction product. The treatment may be applied to raw or finished panels and the generated ammonia gas reacts in the stacked panels with formaldehyde in both the glue lines and the formaldehyde based finish topcoating.
Inventors
- 👤 Dickson Y. Cannon
- 👤 Norman G. Wolfe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:56
CPC Classifications
B; B32; B32B; B32B21/00; B32B21/14; B27; B27K; B27K3/00; B27K3/02; B27K3/0278; B27K3/0292; B27K3/16; B27K3/20; B32B21/13; B32B7/00; B32B7/04; B32B7/12; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31942; Y10T428/31949; Y10T428/31957; Y10T428/3196
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
171 words
A method of after treating formaldehyde laden wood panel products to reduce the emissions of free formaldehyde from the product, the method comprising the steps of treating at least one side surface of the panel subsequent to composition of the panel with an ammonium salt solution, the ammonium salt being one which hydrolizes at ambient temperatures below 120° F. in the presence of water to form ammonium hydroxide and a weak acid, wherein the ammonium hydroxide decomposes to generate ammonia in sufficient degree to be available to react with the free formaldehyde in the wood product; establishing a barrier between the treated panel side and the ambient environment to minimize loss of vaporous ammonia to the ambient environment; and maintaining the treated panel with the barrier in place for a predetermined time sufficient to allow the vaporous ammonia to migrate into the formaldehyde laden zones of the panel; whereby a stable reaction product of gaseous ammonia and formaldehyde is formed, substantially reducing the emission of formaldehyde from the wood panel product.
Claim 2
Independent Claim
171 words
A method of after treating formaldehyde laden wood panel products to reduce the emissions of free formaldehyde from the product, the method comprising the steps of treating at least one side surface of the panel subsequent to composition of the panel with an ammonium salt solution, the ammonium salt being one which hydrolizes at ambient temperatures below 120° F. in the presence of water to form ammonium hydroxide and a weak acid, wherein the ammonium hydroxide decomposes to generate ammonia in sufficient degree to be available to react with the free formaldehyde in the wood product; establishing a barrier between the treated panel side and the ambient environment to minimize loss of vaporous ammonia to the ambient environment; and maintaining the treated panel with the barrier in place for a predetermined time sufficient to allow the vaporous ammonia to migrate into the formaldehyde laden zones of the panel; whereby a stable reaction product of gaseous ammonia and formaldehyde is formed, substantially reducing the emission of formaldehyde from the wood panel product.
Claim 3
Dependent Claim
26 words
The method of claim 1 in which the salt solution is selected from the group consisting of ammonium carbonate, ammonium bicarbonate, ammonium phosphate and ammonium acetate.
Claim 4
Dependent Claim
23 words
The method of claim 1 in which the salt solution is an aqueous solution of ammonium bicarbonate of at least about 10% concentration.
Claim 5
Dependent Claim
19 words
The method of claim 3 in which the concentration of ammonium bicarbonate is in the range of about 10%-15%.
Claim 6
Dependent Claim
33 words
The method of claim 1 in which a finish coating is applied to one side of the panel and the other side of the panel is subsequently treated with the ammonium salt solution.
Claim 7
Dependent Claim
41 words
The method of claim 1 in which the panel is treated with the ammonium salt solution on both sides and barriers are maintained in place on both sides for said predetermined time before any finish coating is applied to the panel.
Claim 8
Dependent Claim
71 words
The method of claim 1 in which a formaldehyde-based finish coating is applied to one side of each of a plurality of said panels, the other side of each of said panels is treated with the salt solution and said panels are stacked such that the finish coated side of each panel in the stack serves as said barrier for the treated other side of each adjacent panel in the stack.
Claim 9
Dependent Claim
37 words
The method of claim 1 in which a plurality of said panels are treated, stacked and stored for a time period of about 16-24 hours at ambient room temperature before finish coating is applied to said panels.
Claim 10
Dependent Claim
24 words
A formaldehyde-laden wood panel product treated in accordance with the method of claim 1 to reduce the emission of free formaldehyde from the product.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-14 | 1986-09-13 | 1987-03-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-14 | 1990-09-13 | 1991-03-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-14 | 1994-09-13 | 1995-03-15 | $7700.00 | Window Closed / Lapsed |