Abstract
Abstract A method of producing long life precision abrasive articles for use in metal removal operations. In this method abrasive particles are impinged against the inner surfaces of a rotating cylindrical mold by centrifugal force. During rotation of the mold a metallic matrix is deposited electrolytically on the inner surfaces of the mold until a matrix supporting the abrasive particles is formed. The matrix is then removed to receive core material and the core is then machined to the finished dimensions. The method is carried out at low temperatures, thereby avoiding heat distortion of the end product.
Inventors
- 👤 Alfred E. Grazen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 17:53
CPC Classifications
B; B24; B24D; B24D18/00; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/4998
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
207 words
A method of making a precision abrasive tool, which comprises (a) depositing loose diamond particles in a metallic mold having an inner annular surface in an amount which is in excess of the number of particles needed to cover the inner annular surface of said mold. (b) rotating said mold about its horizontal axis to spread said diamond particles evenly over the inner annular surface of said mold by centrifugal force rotating means, (c) distributing by an electrolytic distributing means an electrolytic solution containing a metal into the rotating mold, (1) wherein the mold annular surface has a negative charge forming a cathode. (2) wherein the electrolytic solution distributing means has a positive charge forming an anode. (d) forming a solidified matrix of metal by electrolytic deposition around the diamond particles on the inner annular surface of said mold, (e) removing the diamond particles which are not contained within said matrix, (f) continuing the buildup of the matrix to the desired thickness by electrolytic deposition, (g) removing the mold from the rotating means, and introducing core material into the mold as backup for said matrix, (h) machining the core material to desired dimensions, (i) separating the mold from said matrix with the diamond particles and core material.
Claim 2
Independent Claim
207 words
A method of making a precision abrasive tool, which comprises (a) depositing loose diamond particles in a metallic mold having an inner annular surface in an amount which is in excess of the number of particles needed to cover the inner annular surface of said mold. (b) rotating said mold about its horizontal axis to spread said diamond particles evenly over the inner annular surface of said mold by centrifugal force rotating means, (c) distributing by an electrolytic distributing means an electrolytic solution containing a metal into the rotating mold, (1) wherein the mold annular surface has a negative charge forming a cathode. (2) wherein the electrolytic solution distributing means has a positive charge forming an anode. (d) forming a solidified matrix of metal by electrolytic deposition around the diamond particles on the inner annular surface of said mold, (e) removing the diamond particles which are not contained within said matrix, (f) continuing the buildup of the matrix to the desired thickness by electrolytic deposition, (g) removing the mold from the rotating means, and introducing core material into the mold as backup for said matrix, (h) machining the core material to desired dimensions, (i) separating the mold from said matrix with the diamond particles and core material.
Claim 3
Dependent Claim
28 words
A method as set forth in claim 1 wherein the metal in the electrolytic solution is selected from the group consisting of nickel, copper, iron, tin or silver.
Claim 4
Dependent Claim
20 words
A method as set forth in claim 1 wherein the matrix thickness falls in the range of 0.0001" to 0.5".
Claim 5
Dependent Claim
22 words
A method as set forth in claim 1 wherein the temperature of electrolytic deposition may range from room temperature to 200° F.
Claim 6
Dependent Claim
22 words
A method as set forth in claim 1 wherein the core material is a plastic or ceramic which hardens at room temperature.
Claim 7
Dependent Claim
18 words
A method as set forth in claim 1 wherein the mold is made from materials other than metals.
Claim 8
Dependent Claim
27 words
A method as set forth in claim 1 wherein the mold is separated from the matrix by means of chemical dissolution in an acid or alkali solution.
Claim 9
Dependent Claim
35 words
A method as set forth in claim 1 wherein the surface of the matrix after said matrix has been separated from the mold is etched to further expose the cutting edges of the diamond particles.
Claim 10
Dependent Claim
18 words
A method as set forth in claim 8 wherein the etching is performed chemically with acids or alkalis.
Claim 11
Independent Claim
145 words
A method of making a precision abrasive tool, which comprises (a) depositing abrasive particles in a hollow mold having an inner annular surface, (b) distributing said abrasive particles on said inner annular surface by rotating said mold by centrifugal force rotating means, (c) introducing an electrolytic solution containing a metal into the rotating mold, (d) forming a solidified matrix of metal by electrolytic deposition around the abrasive particles on the inner annular surface of said mold, (e) removing the abrasive particles which are not contained within said matrix, and (f) continuing the buildup of the matrix to the desired thickness by electrolytic deposition, (g) removing the mold from the rotating means, and introducing core material into the mold as backup for said matrix, (h) machining the core material to desired dimensions, (i) separating the mold from said matrix with the diamond particles and core material.
Claim 12
Independent Claim
145 words
A method of making a precision abrasive tool, which comprises (a) depositing abrasive particles in a hollow mold having an inner annular surface, (b) distributing said abrasive particles on said inner annular surface by rotating said mold by centrifugal force rotating means, (c) introducing an electrolytic solution containing a metal into the rotating mold, (d) forming a solidified matrix of metal by electrolytic deposition around the abrasive particles on the inner annular surface of said mold, (e) removing the abrasive particles which are not contained within said matrix, and (f) continuing the buildup of the matrix to the desired thickness by electrolytic deposition, (g) removing the mold from the rotating means, and introducing core material into the mold as backup for said matrix, (h) machining the core material to desired dimensions, (i) separating the mold from said matrix with the diamond particles and core material.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-02-14 | 1986-08-16 | 1987-02-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-02-14 | 1990-08-16 | 1991-02-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-02-14 | 1994-08-16 | 1995-02-15 | $7700.00 | Window Closed / Lapsed |