Process for producing coarse-grain crystalline/mono-crystalline metal and alloy films
Assignee: Siemens AG
•
Filing: 1980-06-09
•
Granted: 1983-02-08
•
Expires: 2000-06-09
Abstract
Abstract Coarse-grained crystalline or monocrystalline metal or alloy regions are produced on substrates composed of a material selected from the group consisting of a ceramic, a glass and silicon, and which are provided with a layer of an amorphous or disordered metallic film, for example tantalum, by controllably irradiating select regions of the amorphous film with a focused beam of thermal-energy and/or light-energy, such as obtained from a focused laser beam, while substantially simultaneously maintaining the temperature of such substrate at about the temperature utilized in depositing the amorphous film on the substrate, whereby crystallization seeds are generated at the point of beam irradiation and function as a starting point for the crystalline or monocrystalline front on the metallic surface. Via controlled beam guidance, as by a computer, over the amorphous metal coated substrate surface, the crystallization front is extended uniformly in a desired path along the irradiated surface. The process is useful in producing metallizations for integrated semiconductor circuits, manufacture of contact electrodes for silicon solar cells, etc.
Inventors
- 👤 Guenther Menzel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 10:26
CPC Classifications
C; C30; C30B; C30B1/00; C30B1/02; C30B1/06; C30B1/08; C30B1/023; Y; Y10; Y10S; Y10S117/00; Y10S117/903; Y10S117/904; Y10S148/00; Y10S148/092; Y10S148/093
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
150 words
In a method of producing specifically shaped coarse-grained crystalline or monocrystalline surfaces or lines in metal or alloy films on substrates composed of a material selected from the group consisting of ceramic, glass and silicon through the conversion of an amorphous film deposited at a temperature ranging from about room temperature to about -160° C. on a surface of such substrate, the improvement comprising: controllably guiding a focused energy beam over select areas of said amorphous metallic layer; and substantially simultaneous maintaining said substrate and said deposited metallic layer at a relatively low temperature approximately equal to said deposition temperature of said metallic layer onto said substrate whereby crystallization seeds are locally and directly formed at the beam-irradiated areas and function as a starting point for a monocrystalline front which is guided into a desired direction to form specifically-shaped crystalline or monocrystalline surfaces or lines in the amorphous metallic films.
Claim 2
Dependent Claim
150 words
In a method of producing specifically shaped coarse-grained crystalline or monocrystalline surfaces or lines in metal or alloy films on substrates composed of a material selected from the group consisting of ceramic, glass and silicon through the conversion of an amorphous film deposited at a temperature ranging from about room temperature to about -160° C. on a surface of such substrate, the improvement comprising: controllably guiding a focused energy beam over select areas of said amorphous metallic layer; and substantially simultaneous maintaining said substrate and said deposited metallic layer at a relatively low temperature approximately equal to said deposition temperature of said metallic layer onto said substrate whereby crystallization seeds are locally and directly formed at the beam-irradiated areas and function as a starting point for a monocrystalline front which is guided into a desired direction to form specifically-shaped crystalline or monocrystalline surfaces or lines in the amorphous metallic films.
Claim 3
Dependent Claim
20 words
In a method as defined in claim 1 wherein said focused energy beam is generated by a monochromatic light source.
Claim 4
Dependent Claim
17 words
In a method as defined in claim 2 wherein said light source is a laser beam source.
Claim 5
Dependent Claim
44 words
In a method as defined in claim 2 wherein said laser beam source is selectively movable relative to said amorphous metallic film for select different spacing between said source and said film and for selective different beaming direction between said source and said film.
Claim 6
Dependent Claim
40 words
In a method as defined in claim 3 wherein said laser beam source is operationally connected to a computer means and said computer means guides the generated laser beam onto said amorphous metallic film in accordance with a preselected program.
Claim 7
Independent Claim
173 words
A method of producing metallizations for integrated semiconductor circuits, comprising: providing a substrate composed of a material selected from the group consisting of ceramic, glass and silicon and having a plurality of separate semiconductor circuit components on a surface thereof arranged to define an integrated semiconductor circuit; depositing at a temperature ranging from about room temperature to about -160° C. a selectively structured amorphous metallic layer onto said substrate surface at regions thereof requiring metallization; maintaining the so-coated substrate at a relatively low temperature about equal to said temperature utilized during deposition of said amorphous metallic layer; and substantially simultaneously guiding a focused energy beam over select areas of said amorphous metallic layer whereby crystallization seeds are locally and directly formed at the beam-irradiated areas and function as a starting point for a monocrystalline front which is guided into the desired direction to form a coarse-grained crystalline or monocrystalline metallic layer in the amorphous metallic layer so as to metallically connect said plurality of separate circuit components into an operational integrated semiconductor circuit.
Claim 8
Independent Claim
173 words
A method of producing metallizations for integrated semiconductor circuits, comprising: providing a substrate composed of a material selected from the group consisting of ceramic, glass and silicon and having a plurality of separate semiconductor circuit components on a surface thereof arranged to define an integrated semiconductor circuit; depositing at a temperature ranging from about room temperature to about -160° C. a selectively structured amorphous metallic layer onto said substrate surface at regions thereof requiring metallization; maintaining the so-coated substrate at a relatively low temperature about equal to said temperature utilized during deposition of said amorphous metallic layer; and substantially simultaneously guiding a focused energy beam over select areas of said amorphous metallic layer whereby crystallization seeds are locally and directly formed at the beam-irradiated areas and function as a starting point for a monocrystalline front which is guided into the desired direction to form a coarse-grained crystalline or monocrystalline metallic layer in the amorphous metallic layer so as to metallically connect said plurality of separate circuit components into an operational integrated semiconductor circuit.
Claim 9
Independent Claim
140 words
A method of manufacturing contact electrodes for solar cells comprising: providing operative solar cells having a surface for contact electrodes; depositing at a temperature ranging from about room temperature to about -160° C. a selectively structured amorphous metallic layer onto said surface of the solar cells at regions thereof requiring contact electrodes; maintaining the so-coated solar cells at a relatively low temperature about equal to said temperature utilized during deposition of said amorphous metallic layer; and substantially simultaneously controllably guiding a focused energy beam over select areas of said amorphous metallic layer whereby crystallization seeds are locally and directly formed at the beam-irradiated areas and function as a starting point for a monocrystalline front which is guided into a desired direction to form specifically-shaped crystalline or monocrystalline lines in the amorphous metallic layer defining contact electrodes for said solar cells.
Claim 10
Independent Claim
140 words
A method of manufacturing contact electrodes for solar cells comprising: providing operative solar cells having a surface for contact electrodes; depositing at a temperature ranging from about room temperature to about -160° C. a selectively structured amorphous metallic layer onto said surface of the solar cells at regions thereof requiring contact electrodes; maintaining the so-coated solar cells at a relatively low temperature about equal to said temperature utilized during deposition of said amorphous metallic layer; and substantially simultaneously controllably guiding a focused energy beam over select areas of said amorphous metallic layer whereby crystallization seeds are locally and directly formed at the beam-irradiated areas and function as a starting point for a monocrystalline front which is guided into a desired direction to form specifically-shaped crystalline or monocrystalline lines in the amorphous metallic layer defining contact electrodes for said solar cells.
Claim 11
Dependent Claim
16 words
A method as defined in claim 7 wherein said solar cells are composed of amorphous silicon.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-02-07 | 1986-08-09 | 1987-02-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-02-07 | 1990-08-09 | 1991-02-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-02-07 | 1994-08-09 | 1995-02-08 | $7700.00 | Window Closed / Lapsed |