Abstract
Abstract This invention is directed to a process for producing flame retardant flexible polyurethane foams having a porosity generally in the range between 0.5 and 10 cubic feet per minute. A polyol having an average molecular weight between about 250 and about 6,500, preferably about 3,500 to 6,500, is reacted with a polyisocyanate, such as toluene diisocyanate, which comprises a mixture of 2,4- and 2,6-toluene diisocyanate isomers. The formulation of the present invention includes a flame retardant mixture of a plasticizer and dibromoneopentyl glycol. The plasticizer is either a halogented phosphonate or halogenated phosphate ester. Chlorine is the preferred halogen atom. The weight ratio of those ingredients is between about 20/80 and about 90/10. The concentration of that mixture is in excess of about 20 to about 60 percent by weight of the polyol. Other ingredients that can be included in this formulation are water, a silicone surfactant, a tertiary amine catalyst, a tertiary amine co-catalyst, an auxiliary blowing agent and a tin catalyst. This process results in foam products that are flame retardant, suitable for automotive and furniture applications, and have low flame spread indices according to the Radiant Panel Test ASTM E 162-78.
Inventors
- 👤 Gunter H. Wegner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 05:06
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/0014; C08J9/0038; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/30; C08G18/38; C08G18/3802; C08G18/3804; C08G18/3806; C08G18/381; C08J2375/00; C08J2375/04
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
129 words
In a process for producing flexible polyether or polyester polyurethane foams having a porosity in the range from about 0.5 to about 10 cubic feet per minute, in which a polyfunctional isocyanate is reacted with a polyol in the presence of a small amount of a blowing agent and a catalytic amount of a polymerization catalyst, the improvement which comprises: incorporating as a separate reactant into the reaction mixture prior to polymerization in excess of about 20 to about 60 percent by weight of a mixture of dibromoneopentyl glycol or its esters and flame retardant plasticizer, based on the weight of polyol used in the polymerization reaction, which manner of incorporating said mixture results in substantially more flame retardant foams without adversely affecting the physical characteristics of said foams.
Claim 2
Dependent Claim
129 words
In a process for producing flexible polyether or polyester polyurethane foams having a porosity in the range from about 0.5 to about 10 cubic feet per minute, in which a polyfunctional isocyanate is reacted with a polyol in the presence of a small amount of a blowing agent and a catalytic amount of a polymerization catalyst, the improvement which comprises: incorporating as a separate reactant into the reaction mixture prior to polymerization in excess of about 20 to about 60 percent by weight of a mixture of dibromoneopentyl glycol or its esters and flame retardant plasticizer, based on the weight of polyol used in the polymerization reaction, which manner of incorporating said mixture results in substantially more flame retardant foams without adversely affecting the physical characteristics of said foams.
Claim 3
Dependent Claim
40 words
The process for producing high resiliency flame retardant flexible polyether polyurethane foams according to claim 1, in which the polyol is a poly(propylene oxide/ethylene oxide) triol having an average molecular weight in the range from about 3,500 to about 6,500.
Claim 4
Dependent Claim
30 words
The process for producing flame retardant flexible polyurethane foams according to claim 2, in which the polyol is reacted with a sufficient amount of a mixture of toluene diisocyanate isomers.
Claim 5
Dependent Claim
31 words
The process for producing flame retardant flexible polyurethane foams according to claim 2, in which the dibromoeopentyl glycol/plasticizer mixture is incorporated in the reaction medium in the form of a solution.
Claim 6
Dependent Claim
27 words
The process for producing flame retardant flexible polyurethane foams according to claim 2, in which the dibromoneopentyl glycol/plasticizer mixture is incorporated in the form of a dispersion.
Claim 7
Dependent Claim
57 words
The process for producing flame retardant flexible polyurethane foams according to claim 2, in which from about 0.5 to about 5.5 percent by weight of water and from about 25 to about 50 percent by weight of dibromoneopentyl glycol/plasticizer mixture, based on the weight of polyol used in the polymerization reaction, are used in the reaction mixture.
Claim 8
Dependent Claim
29 words
The process for producing flame retardant flexible polyurethane foams according to claim 2, in which the weight ratio of plasticizer to dibromoneopentyl glycol is from about 20/80 to 90/10.
Claim 9
Dependent Claim
29 words
The process for producing flame retardant flexible polyurethane foams according to claim 2, in which the weight ratio of plasticizer to dibromoneopentyl glycol is from about 50/50 to 75/25.
Claim 10
Dependent Claim
22 words
The process for producing flame retardant flexible polyurethane foams according to claim 2, in which the plasticizer is a chlorinated phosphonate ester.
Claim 11
Dependent Claim
22 words
The process for producing flame retardant flexible polyurethane foams according to claim 2, in which the plasticizer is a chlorinated phosphate ester.
Claim 12
Dependent Claim
22 words
The process for producing flame retardant flexible polyurethane foams according to claim 2, in which the plasticizer is a brominated phosphate ester.
Claim 13
Dependent Claim
33 words
The process for producing flame retardant flexible polyurethane foams according to claim 2, in which the foam obtained has a Flame Spread Index according to ASTM E 162-78 of less than about 25.
Claim 14
Dependent Claim
144 words
A process for producing flexible, high resiliency, flame retardant polyether polyurethane foam having a porosity in the range from about 0.5 to about 10 cubic feet per minute, in which an isomeric mixture of 2,4- and 2,6 toluene diisocyanate is reacted with a (propylene oxide/ethylene oxide) triol having a molecular weight from about 3,500 to about 6,500 in the presence of a small amount of water and a catalytic amount of polymerization catalyst, the improvement which comprises: incorporating as a separate reactant into the reaction mixture prior to polymerization in excess of about 20 to about 60 percent by weight of a mixture of dibromoneopentyl glycol and flame retardant plasticizer, based on the weight of the polyol used in the polymerization reaction, which manner of incorporating said mixture results in substantially more flame retardant foam without adversely affecting the physical characteristics of said foams.
Claim 15
Dependent Claim
144 words
A process for producing flexible, high resiliency, flame retardant polyether polyurethane foam having a porosity in the range from about 0.5 to about 10 cubic feet per minute, in which an isomeric mixture of 2,4- and 2,6 toluene diisocyanate is reacted with a (propylene oxide/ethylene oxide) triol having a molecular weight from about 3,500 to about 6,500 in the presence of a small amount of water and a catalytic amount of polymerization catalyst, the improvement which comprises: incorporating as a separate reactant into the reaction mixture prior to polymerization in excess of about 20 to about 60 percent by weight of a mixture of dibromoneopentyl glycol and flame retardant plasticizer, based on the weight of the polyol used in the polymerization reaction, which manner of incorporating said mixture results in substantially more flame retardant foam without adversely affecting the physical characteristics of said foams.
Claim 16
Dependent Claim
31 words
The process for producing flame retardant polyurethane foam according to claim 13 in which the dibromoneopentyl glycol plasticizer mixture is incorporated in the reaction mixture in the form of a solution.
Claim 17
Dependent Claim
20 words
A process for producing flame retardant polyurethane foam according to claim 13 in which the plasticizer is a chlorophosphonate ester.
Claim 18
Dependent Claim
26 words
A process for producing flame retardant polyurethane foam according to claim 13 in which the toluene diisocyanate is an 80/20 blend of the 2,4- and 2,6-isomers.
Claim 19
Dependent Claim
29 words
A process for producing flame retardant polyurethane foam according to claim 13 in which the weight ratio of plasticizer to dibromoneopentyl glycol is from about 50/50 to about 75/25.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-13 | 1986-06-14 | 1986-12-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-13 | 1990-06-14 | 1990-12-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-13 | 1994-06-14 | 1994-12-14 | $7700.00 | Window Closed / Lapsed |