Low viscosity bone cement
Assignee: Zimmer Inc
•
Filing: 1980-02-20
•
Granted: 1982-07-27
•
Expires: 2000-02-20
Abstract
Abstract An acrylic cement-like substance which permits seating and securing of a prosthesis into living bone which comprises a mixture of a liquid monomer component and a polymer powder component such that upon mixing the two components, a cement which maintains a low viscosity for a longer period of time is formed. The low viscosity bone cement is intended for syringe or injector gun use only as it is to be used before the cement becomes doughy. This low viscosity bone cement has a viscosity of approximately 20 degrees C. (68 degrees F.), of less than 1500 poise, and preferably less than 1000 poise up to the sixth or seventh minute after the two components are mixed. The cement used in the lower viscosity state is more capable of penetrating the trabeculae of bones when used to secure a prosthesis, than when the cement is applied in the doughy state.
Inventors
- 👤 David A. Anuta
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 03:25
CPC Classifications
A; A61; A61L; A61L24/00; A61L24/0047; A61L24/0073; A61L24/0089; A61L24/001; C; C09; C09J; C09J4/00; C09J4/06; A61L2430/00; A61L2430/02
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
245 words
An acrylic bone cement composition comprising: a liquid monomer component and a polymer powder component in the form of beads wherein the liquid component to powder component ratio is 1 to 2 (volume weight) there the liquid component is measured in milliliters and the powder component is measured in grams and wherein said liquid monomer component is comprised of methylmethacrylate monomer and said polymer powder component is comprised at least 80% by weight of polymethylmethacrylate polymer powder in which at least 85-95% by weight of the polymethylmethacrylate polymer powder beads are regular beads which fall through a #40 mesh (425 micron openings) screen and a #100 mesh screen (150 micron openings) and which have a maximum average size of about 25 microns and a minimum average size of about 13 microns, and about 5-15% by weight of polymethylmethacrylate polymer powder beads which fall through a #40 mesh (425 micron openings) screen, but not through a #100 mesh screen, (150 micron openings) and are subsequently milled to roughen and break up the surface of the bead, and whereby when the liquid monomer component is mixed with said polymer powder component, the resulting cement has a viscosity of less than 1500 poise at approximately 20 degrees C. (68 degrees F.) for at least six minutes after the components are initially mixed, and such that the resulting bone cement becomes completely hard in not more than ten to eleven minutes from the time the components were initially mixed.
Claim 2
Dependent Claim
245 words
An acrylic bone cement composition comprising: a liquid monomer component and a polymer powder component in the form of beads wherein the liquid component to powder component ratio is 1 to 2 (volume weight) there the liquid component is measured in milliliters and the powder component is measured in grams and wherein said liquid monomer component is comprised of methylmethacrylate monomer and said polymer powder component is comprised at least 80% by weight of polymethylmethacrylate polymer powder in which at least 85-95% by weight of the polymethylmethacrylate polymer powder beads are regular beads which fall through a #40 mesh (425 micron openings) screen and a #100 mesh screen (150 micron openings) and which have a maximum average size of about 25 microns and a minimum average size of about 13 microns, and about 5-15% by weight of polymethylmethacrylate polymer powder beads which fall through a #40 mesh (425 micron openings) screen, but not through a #100 mesh screen, (150 micron openings) and are subsequently milled to roughen and break up the surface of the bead, and whereby when the liquid monomer component is mixed with said polymer powder component, the resulting cement has a viscosity of less than 1500 poise at approximately 20 degrees C. (68 degrees F.) for at least six minutes after the components are initially mixed, and such that the resulting bone cement becomes completely hard in not more than ten to eleven minutes from the time the components were initially mixed.
Claim 3
Dependent Claim
32 words
An acrylic cement as described in claim 1, wherein the polymer powder is comprised of a mixture of 90% regular polymer beads and 10% of said polymer beads which have been milled.
Claim 4
Dependent Claim
34 words
An acrylic cement as described in claim 1, wherein the liquid monomer component is comprised of 96.2 % to 98.3% by volume of methyl methacrylate monomer, and 2.5% to 3.0% by volume of N,N-dimethyl-p-toluidine.
Claim 5
Dependent Claim
19 words
An acrylic cement as described in claim 3, wherein the liquid monomer component further includes 75±10 ppm of hydroquinone.
Claim 6
Dependent Claim
53 words
An acrylic cement as described in claim 1, wherein the powder component is comprised of 80 to 100% by weight of the poly methyl methacrylate bead mixture and 0.5 to 1.0% by weight of benzoyl peroxide, a catalyst, and wherein the powder component allows for a maximum of 1% by weight moisture content.
Claim 7
Dependent Claim
32 words
An acrylic cement as described in claims 1 or 5, wherein the polymer powder component further includes 9.0 to 11.0% by weight of barium sulfate, U.S.P. to provide radiopacity to the cement.
Claim 8
Dependent Claim
74 words
An acrylic cement as described in claim 1, wherein the polymer powder component further includes a dispersion of 1.8 to 2.2% by weight of high modulus graphite fibers, wherein the cross-section of said fibers is substantially dog-bone shaped and has a major and minor diameter, wherein the major diameter is approximately 15 microns and the minor diameter is approximately 6 microns, and wherein said fibers have a length of approximately 0.79 to 7.14 millimeters.
Claim 9
Dependent Claim
23 words
An acrylic cement as described in claim 7, wherein the liquid monomer component is comprised of the proportions as stated in claim 3.
Claim 10
Dependent Claim
59 words
An acrylic cement as described in claim 7, wherein the powder component is comprised of 80 to 100% by weight of the poly methyl methacrylate bead mixture, 1.8 to 2.2% by weight of high modulus carbon fibers, and 0.5 to 1.0% by weight of benzoyl peroxide, a catalyst, and allows for a maximum of 1% by weight moisture content.
Claim 11
Dependent Claim
32 words
An acrylic cement as described in claims 7 or 9 wherein the polymer powder component further includes 9 to 11% by weight of barium sulfate, U.S.P. to provide radiopacity to the cement.
Claim 12
Dependent Claim
223 words
An acyrlic bone cement composition comprising: a liquid monomer component and a polymer powder component in the form of beads wherein the liquid component to powder component ratio is 1 to 2 (volume/weight) where the liquid component is measured in milliliters and the powder component is measured in grams and wherein said liquid monomer component is comprised of methylmethacrylate monomer and said polymer powder component is comprised at least 80% by weight of poly methylmethacrylate polymer powder in which at least 85-95% by weight of the poly methylmethacrylate polymer powder beads are regular beads which fall through a #40 mesh (425 micron openings) screen and a #100 mesh screen (150 micron openings) and which have a maximum average size of about 25 microns and a minimum average size of about 13 microns, and about 5-15% by weight of poly methylmethacrylate polymer powder beads which are less than 13 to 17 microns in diameter, and whereby when the liquid monomer component is mixed with said polymer powder component, the resulting cement has a viscosity of less than 1500 poise at approximately 20 degrees C. (68 degrees F.) for at least six minutes after the components are initially mixed, and such that the resulting bone cement becomes completely hard in not more than ten to eleven minutes from the time the components were initially mixed.
Claim 13
Dependent Claim
223 words
An acyrlic bone cement composition comprising: a liquid monomer component and a polymer powder component in the form of beads wherein the liquid component to powder component ratio is 1 to 2 (volume/weight) where the liquid component is measured in milliliters and the powder component is measured in grams and wherein said liquid monomer component is comprised of methylmethacrylate monomer and said polymer powder component is comprised at least 80% by weight of poly methylmethacrylate polymer powder in which at least 85-95% by weight of the poly methylmethacrylate polymer powder beads are regular beads which fall through a #40 mesh (425 micron openings) screen and a #100 mesh screen (150 micron openings) and which have a maximum average size of about 25 microns and a minimum average size of about 13 microns, and about 5-15% by weight of poly methylmethacrylate polymer powder beads which are less than 13 to 17 microns in diameter, and whereby when the liquid monomer component is mixed with said polymer powder component, the resulting cement has a viscosity of less than 1500 poise at approximately 20 degrees C. (68 degrees F.) for at least six minutes after the components are initially mixed, and such that the resulting bone cement becomes completely hard in not more than ten to eleven minutes from the time the components were initially mixed.
Claim 14
Dependent Claim
38 words
An acrylic cement as described in claim 11, wherein the polymer powder is comprised of a mixture of 90% regular polymer beads and 10% of said polymer beads which are less than 13 to 17 microns in diameter.
Claim 15
Dependent Claim
34 words
An acrylic cement as described in claim 11, wherein the liquid monomer component is comprised of 96.2% to 98.3% by volume of methyl methacrylate monomer, and 2.5% to 3.0% by volume of N, N-dimethyl-p-toluidine.
Claim 16
Dependent Claim
19 words
An acrylic cement as described in claim 13, wherein the liquid monomer component further includes 75±10 ppm of hydroquinone.
Claim 17
Dependent Claim
52 words
An acrylic cement as described in claim 11, wherein the powder component is comprised of 80 to 100% by weight of the poly methylmethacrylate bead mixture and 0.5 to 1.0% by weight of benzoyl peroxide, a catalyst, and wherein the powder component allows for a maximum of 1% by weight moisture content.
Claim 18
Dependent Claim
32 words
An acrylic cement as described in claims 11 or 15, wherein the polymer powder component further includes 9.0 to 11.0% by weight of barium sulfate, U.S.P. to provide radiopacity to the cement.
Claim 19
Dependent Claim
74 words
An acrylic cement as described in claim 11, wherein the polymer powder component further includes a dispersion of 1.8 to 2.2% by weight of high modulus graphite fibers, wherein the cross-section of said fibers is substantially dog-bone shaped and has a major and minor diameter, wherein the major diameter is approximately 15 microns and the minor diameter is approximately 6 microns, and wherein said fibers have a length of approximately 0.79 to 7.14 millimeters.
Claim 20
Dependent Claim
23 words
An acrylic cement as described in claim 17, wherein the liquid monomer component is comprised of the proportions as stated in claim 3.
Claim 21
Dependent Claim
58 words
An acrylic cement as described in claim 17, wherein the powder component is comprised of 80 to 100% by weight of the poly methylmethacrylate bead mixture, 1.8 to 2.2% by weight of high modulus carbon fibers, and 0.5 to 1.0% by weight of benzoyl peroxide, a catalyst, and allows for a maximum of 1% by weight moisture content.
Claim 22
Dependent Claim
32 words
An acrylic cement as described in claims 17 or 19, wherein the polymer powder component further includes 9 to 11% by weight of barium sulfate, U.S.P. to provide radiopacity to the cement.
Claim 23
Dependent Claim
44 words
An acrylic cement as described in claims 1 or 11, wherein the viscosity of the resulting bone cement after mixing is less than 1000 poise at approximately 20 degrees C. (68 degrees F.) for at least six minutes after the components are initially mixed.
References Cited (Backward Citations)
US3223083A
Cited
US3649608A
Cited
GB1431211A
Cited
US4107845A
Cited
US4141864A
Cited
US4093576A
Cited
US4064566A
Cited
GB2009200B
Cited
US4282140A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-26 | 1986-01-25 | 1986-07-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-26 | 1990-01-25 | 1990-07-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-26 | 1994-01-25 | 1994-07-27 | $7700.00 | Window Closed / Lapsed |