Method of producing semiconductor displacement transducer
Assignee: Hitachi Ltd
•
Filing: 1980-07-07
•
Granted: 1982-03-16
•
Expires: 2000-07-07
Abstract
Abstract A strain gauge is formed on one main surface of a semiconductor single crystal substrate while an insulating oxide film is formed on the other main surface of the substrate. A metal junction layer including several layers inclusive of eutectic alloy layers is formed on the surface of the insulating oxide film and the thus prepared structure is mounted on a metal strain generator. By heating this assembly to temperatures approximating to the eutectic point of the eutectic alloy layer, the semiconductor substrate and the metal strain generator are joined together.
Inventors
- 👤 Masanori Tanabe
- 👤 Satoshi Shimada
- 👤 Akio Yasukawa
- 👤 Hideyuki Nemoto
- 👤 Motohisa Nishihara
- 👤 Masatoshi Tsuchiya
- 👤 Ko Soeno
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 19:37
CPC Classifications
H; H10; H10D; H10D48/00; H10D48/50; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49082; Y10T29/49103
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
108 words
A method of producing a semiconductor displacement transducer, comprising: forming a strain gauge on one surface of a semiconductor single crystal substrate; forming an insulating oxide film on the other surface of said substrate; forming a first metal layer on said insulating oxide film; forming a second metal layer on said first metal layer; forming a eutectic alloy layer on said second metal layer; and mounting said substrate thus treated onto a metal strain generator and joining them together by heating this assembly to a temperature approximating the eutectic point of said eutectic alloy to form a compound of said first metal layer and said eutectic alloy layer.
Claim 2
Independent Claim
108 words
A method of producing a semiconductor displacement transducer, comprising: forming a strain gauge on one surface of a semiconductor single crystal substrate; forming an insulating oxide film on the other surface of said substrate; forming a first metal layer on said insulating oxide film; forming a second metal layer on said first metal layer; forming a eutectic alloy layer on said second metal layer; and mounting said substrate thus treated onto a metal strain generator and joining them together by heating this assembly to a temperature approximating the eutectic point of said eutectic alloy to form a compound of said first metal layer and said eutectic alloy layer.
Claim 3
Dependent Claim
36 words
A method as claimed in claim 1, wherein said first metal layer is of Cr, said second metal layer is of Cu or Ni, and said eutectic alloy layer is of Au-Ge or Au-Si eutectic alloy.
Claim 4
Dependent Claim
24 words
A method as claimed in claim 1, wherein said first and second metal layers and said eutectic alloy layer are formed by vacuum deposition.
Claim 5
Dependent Claim
24 words
A method as claimed in claim 1, wherein said strain gauge is formed by diffusing an impurity into said one surface of said substrate.
Claim 6
Dependent Claim
29 words
A method as claimed in claim 1, wherein the thickness of said eutectic alloy layer is controlled to be substantially not greater than 1.5 μm after the heating treatment.
Claim 7
Independent Claim
132 words
A method of producing a semiconductor displacement transducer, comprising: forming a P-type strain gauge in one of the main surfaces of an N-type semiconductor single crystal substrate and pads for applying a high electric potential to said substrate therethrough on said one main surface of said substrate; forming an insulating oxide film on the other main surface of said substrate; forming a metal junction layer on said insulating oxide layer, said metal junction layer including a plurality of metal layers inclusive of eutectic alloy layers; and mounting said substrate thus treated onto a metal strain generator and joining them together by heating this assembly to a temperature approximating the eutectic point of said eutectic alloy to form a compound of one of said metal layers and one of said eutectic alloy layers.
Claim 8
Independent Claim
132 words
A method of producing a semiconductor displacement transducer, comprising: forming a P-type strain gauge in one of the main surfaces of an N-type semiconductor single crystal substrate and pads for applying a high electric potential to said substrate therethrough on said one main surface of said substrate; forming an insulating oxide film on the other main surface of said substrate; forming a metal junction layer on said insulating oxide layer, said metal junction layer including a plurality of metal layers inclusive of eutectic alloy layers; and mounting said substrate thus treated onto a metal strain generator and joining them together by heating this assembly to a temperature approximating the eutectic point of said eutectic alloy to form a compound of one of said metal layers and one of said eutectic alloy layers.
Claim 9
Dependent Claim
42 words
A method as claimed in claim 6, wherein the component layers of said metal junction layer are a Cr layer, a Cu or Ni layer and a Au-Ge or Au-Si eutectic alloy layer, deposited in this order on said insulating oxide film.
Claim 10
Dependent Claim
21 words
A method as claimed in claim 6, wherein said metal junction layer is formed on said oxide layer by vacuum deposition.
Claim 11
Dependent Claim
23 words
A method as claimed in claim 6, wherein said strain gauge is formed by diffusing an impurity into the surface of said substrate.
Claim 12
Dependent Claim
29 words
A method as claimed in claim 6, wherein the thickness of said eutectic alloy layer is controlled to be substantially not greater than 1.5 μm after the heating treatment.
Claim 13
Independent Claim
181 words
A method of producing a semiconductor displacement transducer, comprising: forming a strain gauge by diffusing an impurity into one main surface of a semiconductor single crystal substrate; forming an insulating oxide film on the other main surface of said substrate; forming a Cr layer on the surface of said insulating oxide film by vacuum deposition; forming a Cr-Cu or Cr-Ni layer on the surface of said Cr layer by vacuum deposition; forming a Cu or Ni layer on the surface of said Cu-Cr or Cr-Ni layer by vacuum deposition; forming a Au layer on the surface of said Cu or Ni layer by vacuum deposition; forming a Au-Ge or Au-Si eutectic alloy layer on the surface of said Au layer by vacuum deposition; plating the surface of a metal strain generator with gold by ion plating method; and mounting said substrate thus treated onto said gold-plated metal strain generator and joining them together by heating this assembly to a temperature approximating the eutectic point of said eutectic alloy to form a compound of said Cr layer and said eutectic alloy layer.
Claim 14
Independent Claim
181 words
A method of producing a semiconductor displacement transducer, comprising: forming a strain gauge by diffusing an impurity into one main surface of a semiconductor single crystal substrate; forming an insulating oxide film on the other main surface of said substrate; forming a Cr layer on the surface of said insulating oxide film by vacuum deposition; forming a Cr-Cu or Cr-Ni layer on the surface of said Cr layer by vacuum deposition; forming a Cu or Ni layer on the surface of said Cu-Cr or Cr-Ni layer by vacuum deposition; forming a Au layer on the surface of said Cu or Ni layer by vacuum deposition; forming a Au-Ge or Au-Si eutectic alloy layer on the surface of said Au layer by vacuum deposition; plating the surface of a metal strain generator with gold by ion plating method; and mounting said substrate thus treated onto said gold-plated metal strain generator and joining them together by heating this assembly to a temperature approximating the eutectic point of said eutectic alloy to form a compound of said Cr layer and said eutectic alloy layer.
Claim 15
Dependent Claim
22 words
A method as claimed in claim 2 or 7, wherein said metal strain generator comprises a substrate coated with a gold layer.
Claim 16
Dependent Claim
54 words
A method as claimed in claim 1, wherein a third metal layer is formed between the first and second metal layers to improve adhesion between said first and second layers and a fourth metal layer is formed between said second and eutectic alloy layers to improve adhesion between said second and eutectic alloy layers.
Claim 17
Dependent Claim
43 words
A method as claimed in claim 1 or 11, wherein said metal strain generator is made of a Ni containing metal, and wherein during said heating, nickel from said metal strain generator forms a compound of said eutectic alloy layer and said nickel.
Claim 18
Dependent Claim
17 words
A method as claimed in claim 14, wherein said Ni containing metal is Fe-Ni or Fe-Ni-Co alloy.
Claim 19
Dependent Claim
42 words
A method as claimed in claim 6, wherein said metal strain generator is made of a Ni-containing metal, and wherein, during said heating, nickel from said metal strain generator forms a compound of one of said eutectic alloy layers and said nickel.
Claim 20
Dependent Claim
16 words
A method as claimed in claim 16, wherein said Ni-containing metal is Fe-Ni or Fe-Ni-Co alloy.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-03-15 | 1985-09-14 | 1986-03-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-03-15 | 1989-09-14 | 1990-03-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-03-15 | 1993-09-14 | 1994-03-16 | $7700.00 | Window Closed / Lapsed |