Method for producing a collapse resistant polyester container for hot fill applications

Claim 1

A method for producing a collapse resistant, molecularly oriented, heat set polyester container for use in hot fill applications, said method comprising the steps of: (a) forming in a mold cavity a molecularly oriented polyester container having at least one preselected region which projects inwardly into said container in a first configuration; (b) heating said oriented container while in contact with the cavity walls at a temperature sufficient to induce rapid crystallization of the polyester to form a heat set container, at least said region being heated to a temperature and for a time sufficient to produce from about 28% to about 32% crystallinity in said region; (c) reshaping said region outwardly to a second configuration at a temperature from just above the hot fill product temperature up to the heating temperature of step (b); and (d) cooling the resulting container while maintaining said region in said second configuration to provide a thermoelastically deformable region which tends to return to said first configuration after hot filling and sealing said resulting container to at least partially relieve pressure forces which tend to collapse said container after hot filling and sealing.

Claim 2

A method for producing a collapse resistant, molecularly oriented, heat set polyester container for use in hot fill applications, said method comprising the steps of: (a) forming in a mold cavity a molecularly oriented polyester container having at least one preselected region which projects inwardly into said container in a first configuration; (b) heating said oriented container while in contact with the cavity walls at a temperature sufficient to induce rapid crystallization of the polyester to form a heat set container, at least said region being heated to a temperature and for a time sufficient to produce from about 28% to about 32% crystallinity in said region; (c) reshaping said region outwardly to a second configuration at a temperature from just above the hot fill product temperature up to the heating temperature of step (b); and (d) cooling the resulting container while maintaining said region in said second configuration to provide a thermoelastically deformable region which tends to return to said first configuration after hot filling and sealing said resulting container to at least partially relieve pressure forces which tend to collapse said container after hot filling and sealing.

Claim 3

A method for producing a collapse resistant, molecularly oriented, heat set polyester container for use in hot fill applications, said method comprising the steps of (a) distending a substantially amorphous polyester preform at a temperature within the molecular orientation temperature range of said polyester in a mold to form an oriented container having sidewalls and a base, said base being formed in a first configuration which projects inwardly into said container; (b) heating said oriented container in and while in contact with walls of said mold, at a temperature sufficient to induce rapid crystallization of said polyester to form a heat set container, at least the inwardly projecting base being heated to a temperature and for a time sufficient to produce from about 28% to about 32% crystallinity in said base; (c) reshaping said base outwardly to a second configuration at a temperature from just above the hot fill product temperature up to the heating temperature of step (b); and (d) cooling the resulting container while maintaining said base in said second configuration to provide a thermoelastically deformable base which tends to return to said first configuration after hot filling and sealing said resulting container to at least partially relieve pressure forces which tend to collapse said container after hot filling and sealing.

Claim 4

A method for producing a collapse resistant, molecularly oriented, heat set polyester container for use in hot fill applications, said method comprising the steps of (a) distending a substantially amorphous polyester preform at a temperature within the molecular orientation temperature range of said polyester in a mold to form an oriented container having sidewalls and a base, said base being formed in a first configuration which projects inwardly into said container; (b) heating said oriented container in and while in contact with walls of said mold, at a temperature sufficient to induce rapid crystallization of said polyester to form a heat set container, at least the inwardly projecting base being heated to a temperature and for a time sufficient to produce from about 28% to about 32% crystallinity in said base; (c) reshaping said base outwardly to a second configuration at a temperature from just above the hot fill product temperature up to the heating temperature of step (b); and (d) cooling the resulting container while maintaining said base in said second configuration to provide a thermoelastically deformable base which tends to return to said first configuration after hot filling and sealing said resulting container to at least partially relieve pressure forces which tend to collapse said container after hot filling and sealing.

Claim 5

A method for producing a collapse resistant, oriented heat set polyester container for use in hot fill applications, said method comprising the steps of: (a) distending a substantially amorphous polyester preform at a temperature in the molecular orientation temperature range of said polyester in a mold to form an oriented container having sidewalls and a base, said base being formed in a first configuration which projects inwardly into said container; (b) differentially heating said oriented container in and while in contact with walls of said mold, said differential heating comprising heating said sidewalls at a temperature and for a time sufficient to produce at least about 35% crystallinity in said sidewalls, and heating said base at a temperature and for a time sufficient to produce from about 28% to about 32% crystallinity in said base; (c) reshaping said base outwardly to a second configuration at a temperature from just above the hot fill product temperature up to the base heating temperature of step (b); and (d) cooling the resulting container while maintaining said base in said second configuration to provide a thermoelastically deformable base which tends to return to said first configuration after hot filling and sealing said resulting container to at least partially relieve pressure forces which tend to collapse said container after hot filling and sealing.

Claim 6

A method for producing a collapse resistant, oriented heat set polyester container for use in hot fill applications, said method comprising the steps of: (a) distending a substantially amorphous polyester preform at a temperature in the molecular orientation temperature range of said polyester in a mold to form an oriented container having sidewalls and a base, said base being formed in a first configuration which projects inwardly into said container; (b) differentially heating said oriented container in and while in contact with walls of said mold, said differential heating comprising heating said sidewalls at a temperature and for a time sufficient to produce at least about 35% crystallinity in said sidewalls, and heating said base at a temperature and for a time sufficient to produce from about 28% to about 32% crystallinity in said base; (c) reshaping said base outwardly to a second configuration at a temperature from just above the hot fill product temperature up to the base heating temperature of step (b); and (d) cooling the resulting container while maintaining said base in said second configuration to provide a thermoelastically deformable base which tends to return to said first configuration after hot filling and sealing said resulting container to at least partially relieve pressure forces which tend to collapse said container after hot filling and sealing.

Claim 8

The method of claims 1, 2 or 3 wherein said polyester is polyethylene terephthalate.

Claim 9

The method of claims 2 or 3 wherein said preform is made by injection molding.

Claim 10

The method of claims 2 or 3 wherein said preform is distended at a temperature of from about 20° F. to about 65° F. above the glass transition temperature of said polyester.

Claim 13

The method of claims 1, 2 or 3 wherein the oriented container has a combined stretch of from about 150% to about 475%.

Claim 14

The method of claims 2, 3 or 4 wherein said base is heated to a temperature of from about 240° F. to about 270° F.

Claim 16

The method of claims 1, 2 or 3 wherein said heating of said oriented container is carried out for a time of up to about 10 seconds.

Claim 17

The method of claims 1, 2 or 3 wherein said reshaping and said cooling are effected in a mold with an inner surface corresponding to said second configuration.

Claim 18

The method of claims 1, 2 or 3 wherein said reshaping is effected at a temperature of from about 180° F. up to about 285° F.

Claim 19

The method of claims 1, 2 or 3 wherein said container is cooled to a temperature in the range of from about 20° F. to about 150° F.

Claim 20

The method of claims 2 or 3 additionally comprising the step of molding stiffening members into said container sidewalls.

Claim 21

The method of claims 2 or 3 additionally comprising molding a plurality of stress points into said base in said second configuration to facilitate the uniform thermoelastic deformation of said base to said first configuration.

Claim 22

The method of claims 2 or 3 additionally comprising the step of molding at least one preselected, substantially planar pressure deformable region into said container sidewalls.

Claim 23

The method of claims 1, 2 or 3 wherein said container has a capacity of from about 120 to about 3780 cubic centimeters.