Bearing material
Assignee: Daido Metal Co Ltd
•
Filing: 1979-08-14
•
Granted: 1982-01-26
•
Expires: 1999-08-14
Abstract
Abstract A porous metal or alloy layer is formed by sintering or the like on a metal backing formed of steel, for example. Copper or a copper-base alloy is generally used for forming the porous metal or alloy layer. The porous metal or alloy layer having the metal backing is impregnated with a mixture comprising 1-25% by volume of lead fluoride, 1-30% by volume of one or both of lead and a lead-tin alloy consisting of 3-30% by weight of tin and the remainder being lead, and the remainder essentially polytetrafluoroethylene, wherein the lead fluoride and one or both of the lead-tin alloy and lead being 2-25% by volume in total, thereby a bearing material of this invention is provided. Depending on the use to which the bearing material is put, at least one additive selected from the group consisting of molybdenum, tungsten disulfide, cadmium oxide, aluminum oxide, calcium fluoride, lithium fluoride, graphite, lead iodide, glass fibers, carbon fibers and a phosphate may be contained in 0.1-5% by volume in the mixture, to improve the performance of the bearing. The bearing material of this kind is suitable for use in shock absorbers of vehicles or the like which move in reciprocatory sliding movement under varying loads.
Inventors
- 👤 Sanae Mori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:39
CPC Classifications
F; F16; F16C; F16C33/00; F16C33/02; F16C33/04; F16C33/20; F16C33/201; C; C10; C10M; C10M7/00; C10M2201/00; C10M2201/04; C10M2201/041; C10M2201/042; C10M2201/06; C10M2201/061; C10M2201/062; C10M2201/065; C10M2201/066; C10M2201/08; C10M2201/081; C10M2201/082; C10M2201/084; C10M2201/12; C10M2201/16; C10M2201/18; C10M2211/00; C10M2211/06; C10M2213/00; C10M2213/02; C10M2213/06; C10M2213/062; C10N; C10N2040/00; C10N2040/02; C10N2050/00; C10N2050/08; C10N2050/10; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12007
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
73 words
A bearing material comprising: a porous material layer lined with a metal backing, said porous layer being impregnated with a mixture comprising 1-25% by volume of lead fluoride; 1-30% by volume of lead, a lead-tin alloy consisting essentially of 3-30% by weight of tin the balance being lead, or mixtures thereof; and the remainder being polytetrafluoroethylene, said lead fluoride and said lead, lead-tin alloy or mixture thereof being 2-35% by volume in total.
Claim 2
Dependent Claim
73 words
A bearing material comprising: a porous material layer lined with a metal backing, said porous layer being impregnated with a mixture comprising 1-25% by volume of lead fluoride; 1-30% by volume of lead, a lead-tin alloy consisting essentially of 3-30% by weight of tin the balance being lead, or mixtures thereof; and the remainder being polytetrafluoroethylene, said lead fluoride and said lead, lead-tin alloy or mixture thereof being 2-35% by volume in total.
Claim 3
Dependent Claim
29 words
A bearing material as set forth in claim 1, wherein said lead, lead-tin alloy or mixture thereof is lead, said lead being 1-30% by volume in said total mixture.
Claim 4
Dependent Claim
28 words
A bearing material as set forth in claim 1, wherein said lead, lead-tin alloy or mixture thereof is lead-tin alloy being 1-30% by volume in said total mixture.
Claim 5
Dependent Claim
41 words
A bearing material as set forth in claim 1, wherein said lead, lead-tin alloy or mixture thereof comprises a mixture of lead-tin alloy and lead, said lead-tin alloy and said lead being 1-30% by volume in total in said total mixture.
Claim 6
Dependent Claim
146 words
A bearing material comprising: a porous material layer lined with a metal backing said porous layer being impregnated with a mixture consisting essentially of: 1-25% by volume of lead fluoride; 1-30% by volume of lead, a lead-tin alloy which contains 3-30% by weight of tin, or mixtures thereof; at least one additive selected from the group consisting of a metal sulfide, a metal oxide, a metal fluoride other than lead fluoride, graphite, lead iodide, glass fibers, carbon fibers, and a phosphate, said additive comprising 0.1-5% by volume in total; and the balance essentially polytetrafluoroethylene; the total of said lead fluoride, said lead, lead-tin alloy or mixture thereof and said at least one additive selected from the group consisting of said metal sulfide, said metal oxide, said metal fluoride, said graphite, said lead iodide, said glass fibers, said carbon fibers and said phosphate being 2.1-35% by volume.
Claim 7
Dependent Claim
146 words
A bearing material comprising: a porous material layer lined with a metal backing said porous layer being impregnated with a mixture consisting essentially of: 1-25% by volume of lead fluoride; 1-30% by volume of lead, a lead-tin alloy which contains 3-30% by weight of tin, or mixtures thereof; at least one additive selected from the group consisting of a metal sulfide, a metal oxide, a metal fluoride other than lead fluoride, graphite, lead iodide, glass fibers, carbon fibers, and a phosphate, said additive comprising 0.1-5% by volume in total; and the balance essentially polytetrafluoroethylene; the total of said lead fluoride, said lead, lead-tin alloy or mixture thereof and said at least one additive selected from the group consisting of said metal sulfide, said metal oxide, said metal fluoride, said graphite, said lead iodide, said glass fibers, said carbon fibers and said phosphate being 2.1-35% by volume.
Claim 8
Dependent Claim
27 words
A bearing material as set forth in claim 5, wherein said lead, lead-tin alloy or mixture thereof is lead being 1-30% by volume in said total mixture.
Claim 9
Dependent Claim
28 words
A bearing material as set forth in claim 5, wherein said lead, lead-tin alloy or mixture thereof is lead-tin alloy being 1-30% by volume in said total mixture.
Claim 10
Dependent Claim
38 words
A bearing material as set forth in claim 5, wherein said lead, lead-tin alloy or mixture thereof constitutes said mixture of lead and lead-tin alloy in an amount of 1-30% by volume in total in said total mixture.
References Cited (Backward Citations)
DE213230C
Cited
CA772604A
Cited
US2995462A
Cited
US3218255A
Cited
DE1494078A1
Cited
SU148476A1
Cited
US3464845A
Cited
US3516933A
Cited
US3705450A
Cited
US3808130A
Cited
US4000982A
Cited
DE2631907A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-01-25 | 1985-07-27 | 1986-01-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-01-25 | 1989-07-27 | 1990-01-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-01-25 | 1993-07-27 | 1994-01-26 | $7700.00 | Window Closed / Lapsed |