Graded start rods for the production of optical waveguides
Assignee: Times Fiber Communications Inc
•
Filing: 1979-07-13
•
Granted: 1981-11-03
•
Expires: 1999-07-13
Abstract
Abstract A process for preparing a glass rod having a graded refractive index for use as the start rod in the production of optical waveguides is disclosed. The process comprises depositing and sintering borosilicate particles on a glass rod to form a rod having a larger diameter than the original fused silica rod and drawing this rod to obtain a start rod having the same diameter as the original glass rod but exhibiting a partially radially graded refractive index. Optical waveguides prepared from such graded start rods have a more uniformly graded radial index of refraction profile.
Inventors
- 👤 Franklin W. Dabby
- 👤 Ronald B. Chesler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 11:52
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/01486; C03B37/01493; C03B37/01205; C03B37/01466; C03B2201/00; C03B2201/06; C03B2201/08; C03B2201/10; C03B2203/00; C03B2203/10; C03B2203/22; C03B2203/24
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
106 words
A process for the production of optical waveguides which comprises preparing a preform by depositing and sintering borosilicate particles on a cylindrical glass rod, heating said preform to the drawing temperature and drawing said preform into optical waveguides, wherein said cylindrical glass rod comprises a central area of constant refractive index and an outer region of varying refractive index and wherein said cylindrical glass rod is prepared by the process comprising depositing and sintering borosilicate particles on a pure fused silica glass rod and drawing the resulting composite to obtain a graded start rod of about the same diameter as the original pure fused silica rod.
Claim 2
Dependent Claim
106 words
A process for the production of optical waveguides which comprises preparing a preform by depositing and sintering borosilicate particles on a cylindrical glass rod, heating said preform to the drawing temperature and drawing said preform into optical waveguides, wherein said cylindrical glass rod comprises a central area of constant refractive index and an outer region of varying refractive index and wherein said cylindrical glass rod is prepared by the process comprising depositing and sintering borosilicate particles on a pure fused silica glass rod and drawing the resulting composite to obtain a graded start rod of about the same diameter as the original pure fused silica rod.
Claim 3
Dependent Claim
34 words
The process as defined by claim 1, wherein said cylindrical glass rod comprises a pure fused silica central area and a borosilicate outer region having radially increasing proportions of boron oxide relative to silica.
Claim 4
Dependent Claim
30 words
The process as defined by claim 2, wherein said borosilicate outer region exhibits an increasing ratio of boron oxide to silica with radial distance from the pure fused silica core.
Claim 5
Dependent Claim
22 words
The process as defined by claim 1, wherein the diameter of said pure fused silica rod is about 3 to 6 mm.
Claim 6
Dependent Claim
22 words
The process as defined by claim 1, wherein the diameter of said composite prior to drawing is about 6 to 12 mm.
Claim 7
Dependent Claim
58 words
The process as defined by claim 1, wherein said borosilicate particles are produced by high temperature pyrolysis of a first gaseous reactant selected from the group consisting of SiH 4 , SiCl 4 and SiBr 4 and a second gaseous reactant selected from the group consisting of B 2 H 6 , BCl 3 and BBr 3 .
Claim 8
Dependent Claim
17 words
The process as defined by claim 6, wherein said reactants are SiCl 4 and BCl 3 .
Claim 9
Dependent Claim
27 words
The process as defined by claim 6, wherein said high temperature pyrolysis is conducted as a flame pyrolysis by burning natural gas in the presence of oxygen.
References Cited (Backward Citations)
US3843229A
Cited
US3823995A
Cited
US3826560A
Cited
US4161505A
Cited
US4165152A
Cited
US3932160A
Cited
US3989350A
Cited
US4141710A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-02 | 1985-05-04 | 1985-11-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-02 | 1989-05-04 | 1989-11-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-02 | 1993-05-04 | 1993-11-03 | $7700.00 | Window Closed / Lapsed |