Coating composition of aminoplast, hydroxy polymers and vinylic monomers
Assignee: Ford Motor Co
•
Filing: 1979-10-17
•
Granted: 1981-10-27
•
Expires: 1999-10-17
Abstract
Abstract A thermosetting coating composition which may have nonvolatile solids content as high as 60% or greater and which may be employed as an automotive topcoat. The composition, exclusive of pigments, solvent, reactive and non-reactive diluents and other non-reactive components, consists essentially of: (A) A binder composition consisting essentially of: (1) Between about 30 and about 75 weight percent of one or more low viscosity resins selected from hydroxy functional acrylic polymers, hydroxy functional polyethers and hydroxy functional polyesters, each of which (i) is substantially soluble in the solvent of the composition and (ii) has a number average molecular weight of between about 1000 and about 2500; and (2) Between about 70 and about 25 weight percent of one or more crosslinked dispersion polymers each of which is substantially insoluble in the solvent of the composition; and (B) An aminoplast crosslinking agent in an amount of between about 5 and about 40 parts per 100 parts of said binder composition. The crosslinked dispersion polymer is prepared by free radical polymerization of 0.5 to 3.5 weight percent of di-,tri- or tetravinyl monomers and 99.5 to 96.5 weight percent of at least one other copolymerizable monoethylenically unsaturated monomer, in the presence of (i) hydrocarbon dispersing liquid which is a solvent for the polymerizable monomer, but a non-solvent for the resulting crosslinked polymer, and (ii) polymeric dispersion stabilizer which is solvated by said dispersing liquid and associated with said crosslinked polymer so as to maintain a separation between particles thereof, thereby inhibiting coagulation of said particles, wherein polymerization is carried out at elevated temperature such that the dispersion polymer first forms and then is crosslinked.
Inventors
- 👤 Yun-Feng Chang
- 👤 Henk V. Oene
- 👤 Elaine C. Beckwith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 19:35
CPC Classifications
C; C09; C09D; C09D133/00; C09D133/04; C09D133/06; C09D133/062; C09D133/066; C08; C08K; C08K5/00; C08K5/16; C08K5/34; C08K5/3467; C08K5/3477; C08K5/3492; C09D161/00; C09D161/20; C08L; C08L2205/00; C08L2205/14; C08L2205/18; C08L57/00; C08L61/00; C08L61/20; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31678
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
249 words
A thermosetting coating composition comprising organic solvent, binder composition, and aminoplast crosslinking agent, wherein said binder composition comprises: (A) between about 30 and about 75 weight percent of one or more low viscosity resins, each of which (1) is substantially soluble in the solvent of the composition, (2) has a number average molecular weight of between about 500 and about 3500 and (3) is selected from the group consisting of hydroxy functional acrylic polymers, hydroxy functional polyethers and hydroxy functional polyesters and bears no additional functionality which would interfere with the crosslinking reaction between the hydroxy functionality of the resin and the crosslinking agent of the composition; and (B) between about 70 and about 25 weight percent of one or more crosslinked dispersion polymers, each of which is substantially insoluble in the solvent of the composition, said dispersion polymers being formed by free radical polymerization of 0.5 to 3.5 weight percent of di-, tri-, or tetravinyl monomers and 99.5 to 96.5 weight percent of at least one other copolymerizable monoethylenically unsaturated monomer, in the presence of a (i) hydrocarbon dispersing liquid which is a solvent for the polymerizable monomers, but a non-solvent for the resulting crosslinked polymer, and (ii) polymeric dispersion stabilizer which is solvated by said dispersing liquid and associated with said crosslinked polymer so as to maintain a separation between particles thereof, thereby inhibiting coagulation of said particles, wherein polymerization is carried out at elevated temperature such that the dispersion polymer first forms and then is crosslinked.
Claim 2
Dependent Claim
249 words
A thermosetting coating composition comprising organic solvent, binder composition, and aminoplast crosslinking agent, wherein said binder composition comprises: (A) between about 30 and about 75 weight percent of one or more low viscosity resins, each of which (1) is substantially soluble in the solvent of the composition, (2) has a number average molecular weight of between about 500 and about 3500 and (3) is selected from the group consisting of hydroxy functional acrylic polymers, hydroxy functional polyethers and hydroxy functional polyesters and bears no additional functionality which would interfere with the crosslinking reaction between the hydroxy functionality of the resin and the crosslinking agent of the composition; and (B) between about 70 and about 25 weight percent of one or more crosslinked dispersion polymers, each of which is substantially insoluble in the solvent of the composition, said dispersion polymers being formed by free radical polymerization of 0.5 to 3.5 weight percent of di-, tri-, or tetravinyl monomers and 99.5 to 96.5 weight percent of at least one other copolymerizable monoethylenically unsaturated monomer, in the presence of a (i) hydrocarbon dispersing liquid which is a solvent for the polymerizable monomers, but a non-solvent for the resulting crosslinked polymer, and (ii) polymeric dispersion stabilizer which is solvated by said dispersing liquid and associated with said crosslinked polymer so as to maintain a separation between particles thereof, thereby inhibiting coagulation of said particles, wherein polymerization is carried out at elevated temperature such that the dispersion polymer first forms and then is crosslinked.
Claim 3
Dependent Claim
47 words
A composition in accordance with claim 1 wherein said polymeric dispersion stabilizer contains at least two segments, one of which is solvated by said dispersing liquid and a second of which is of different polarity than said first segment and is relatively insoluble in said dispersing liquid.
Claim 4
Dependent Claim
16 words
A composition in accordance with claim 1 wherein said polymeric dispersion stabilizer is a butylated melamine.
Claim 5
Dependent Claim
35 words
A composition in accordance with claim 1, wherein said aminoplast crosslinking agent is present in said composition in an amount ranging from about 5 to about 40 parts per 100 parts of said binder composition.
Claim 6
Dependent Claim
71 words
A composition in accordance with claim 1, wherein said low viscosity resin comprises an acrylic copolymer which has a glass transition temperature of between about -20° C. and about 45° C. and is formed from (i) 10-40 weight of hydroxy functional monoethylenically unsaturated monomers, (ii) 0-10 weight percent of carboxyl functional monoethylenically unsaturated monomers, and (iii) a remainder of monomers selected from esters of acrylic and methacrylic acid, and vinyl hydrocarbons.
Claim 7
Dependent Claim
56 words
A composition in accordance with claim 1, wherein said low viscosity resin comprises a hydroxy terminated polyether having the general structure HO--R--O].sub.n H wherein n is between 5 and 50, and R is selected from the group consisting of alkyl groups containing 2 to 12 carbons, cycloalkyl groups containing up to 12 carbons, and aromatic groups.
Claim 8
Dependent Claim
34 words
A composition in accordance with claim 1 wherein said low viscosity resin comprises a hydroxy functional polyester having an acid number of not greater than 3 and a hydroxyl value of at least 125.
Claim 9
Dependent Claim
39 words
A composition in accordance with claim 1, wherein said di-, tri-, or tetravinyl monomers used to form said crosslinked dispersion polymer are employed in an amount ranging from about 1 to about 2.5 weight percent of the reactant monomers.
Claim 10
Dependent Claim
44 words
A composition in accordance with claim 1, wherein said di-, tri-, or tetravinyl monomers used to form said crosslinked dispersion polymer are di-, tri-, or tetraacrylates, and wherein said monomethylenically unsaturated monomers used to form said crosslinked dispersion polymer are alpha-beta olefinically unsaturated monomers.
Claim 11
Dependent Claim
24 words
A composition in accordance with claim 9 wherein all of said alpha-beta monoethylenically unsaturated monomers employed in forming said crosslinked dispersion polymer are monofunctional.
Claim 12
Dependent Claim
50 words
A composition in accordance with claim 9 wherein said alpha-beta monoethylenically unsaturated monomers include between about 5 and about 35 weight percent, based on the total weight of reactants used in forming the crosslinked dispersion polymer, of monomers bearing functionality capable of crosslinking with the crosslinking agent of the composition.
Claim 13
Dependent Claim
25 words
A composition in accordance with claim 11 wherein said functionality capable of crosslinking with said crosslinking agent of said composition is hydroxyl or glycidyl functionality.
Claim 14
Dependent Claim
286 words
A thermosetting coating composition which, exclusive of pigments, organic solvent, reactive and nonreactive diluents and other non-reactive components, consists essentially of: (A) A binder composition consisting essentially of (1) Between about 40 and about 60 weight percent of one or more low viscosity resins selected from the group consisting of hydroxy functional acrylic polymers, hydroxy functional polyethers and hydroxy functional polyesters, each of which (i) is substantially soluble in the organic solvent of the composition, (ii) has a number average molecular weight between about 1000 and about 2500 and (iii) bears no additional functionality which would interfere with the crosslinking reaction between the hydroxyl functionality of the resin and crosslinking agent (B); and (2) Between about 60 and about 40 weight percent of one or more crosslinked dispersion polymers, each of which is substantially insoluble in the organic solvent of the composition, said crosslinked dispersion polymer being formed by free radical polymerization of from about 1 to about 2.5 weight percent of di-, tri-, or tetracrylate monomers and 99 to 97.5 weight percent of at least one other copolymerizable, alpha-beta olefinically unsaturated monomer in the presence of (i) a hydrocarbon dispersing liquid which is a solvent for the polymerizable monomers, but a non-solvent for the resultant crosslinked polymer, and (ii) polymeric dispersion stabiliser which is solvated by said dispersing liquid and associated with said crosslinked polymer so as to maintain a separation between particles thereof, thereby inhibiting coagulation of said particles, wherein the polymerization is carried out at elevated temperature such that the dispersion polymer is first formed and then is crosslinked; and (B) an aminoplast crosslinking agent in an amount of between about 5 and about 40 parts per 100 parts of said binder composition.
Claim 15
Dependent Claim
286 words
A thermosetting coating composition which, exclusive of pigments, organic solvent, reactive and nonreactive diluents and other non-reactive components, consists essentially of: (A) A binder composition consisting essentially of (1) Between about 40 and about 60 weight percent of one or more low viscosity resins selected from the group consisting of hydroxy functional acrylic polymers, hydroxy functional polyethers and hydroxy functional polyesters, each of which (i) is substantially soluble in the organic solvent of the composition, (ii) has a number average molecular weight between about 1000 and about 2500 and (iii) bears no additional functionality which would interfere with the crosslinking reaction between the hydroxyl functionality of the resin and crosslinking agent (B); and (2) Between about 60 and about 40 weight percent of one or more crosslinked dispersion polymers, each of which is substantially insoluble in the organic solvent of the composition, said crosslinked dispersion polymer being formed by free radical polymerization of from about 1 to about 2.5 weight percent of di-, tri-, or tetracrylate monomers and 99 to 97.5 weight percent of at least one other copolymerizable, alpha-beta olefinically unsaturated monomer in the presence of (i) a hydrocarbon dispersing liquid which is a solvent for the polymerizable monomers, but a non-solvent for the resultant crosslinked polymer, and (ii) polymeric dispersion stabiliser which is solvated by said dispersing liquid and associated with said crosslinked polymer so as to maintain a separation between particles thereof, thereby inhibiting coagulation of said particles, wherein the polymerization is carried out at elevated temperature such that the dispersion polymer is first formed and then is crosslinked; and (B) an aminoplast crosslinking agent in an amount of between about 5 and about 40 parts per 100 parts of said binder composition.
Claim 16
Dependent Claim
47 words
A composition in accordance with claim 13 wherein said polymeric dispersion stabilizer contains at least two segments, one of which is solvated by said dispersing liquid and a second of which is of different polarity than said first segment and is relatively insoluble in said dispersing liquid.
Claim 17
Dependent Claim
16 words
A composition in accordance with claim 13 wherein said polymeric dispersion stabilizer is a butylated melamine.
References Cited (Backward Citations)
US3544489A
Cited
GB1223343A
Cited
US3862071A
Cited
US3856883A
Cited
US3953644A
Cited
US4169825A
Cited
ZA806906B
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-10-26 | 1985-04-27 | 1985-10-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-10-26 | 1989-04-27 | 1989-10-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-10-26 | 1993-04-27 | 1993-10-27 | $7700.00 | Window Closed / Lapsed |