Packaging material for food to be subjected to high-temperature short-time sterilization and process for the preparation thereof

Claim 2

A packaging material for food to be subjected to high-temperature short-time sterilization, which comprises a flexible laminate sheet including (a) a heat-sealable inner face layer of a crystalline polypropylene and (b) a heat-resistant resin outer face layer of a thermoplastic resin having a melting point or decomposition point higher than the melting point of said polypropylene, said thermoplastic resin being selected from the group consisting of (a) polyesters and copolyesters comprising recurring units expressed by the following formula ##STR4## wherein R 1 is an alkylene or cycloalkylene group having 2 to 8 carbon atoms, and R 2 is an arylene group, (b) polyamides and copolyamides comprising recurring units expressed by the following formula ##STR5## wherein n is a number of 3 to 13 and m is a number of 4 to 11, (c) polycarbonates comprising recurring units represented by the following formula ##STR6## wherein R 3 is a hydrocarbon group having 8 to 15 carbon atoms, (d) biaxially stretched isotactic polypropylene films, and (e) acetyl cellulose, said heat-sealable inner face layer of said crystalline polypropylene film being characterized in that (i) said film is one prepared by melting in an extruder a crystalline polypropylene having a melt flow index of 0.5 to 3, extruding the melt in the form of a film at a temperature of 230° to 260° C., through a T die, and contacting the extruded film with a chill roll having a surface temperature of 20° to 70° C., to thereby cool rapidly and solidify the film, (ii) when the film is extracted in salad oil at 130° C. for 30 minutes, the amount extracted of the polypropylene is smaller than 1500 ppm, (iii) the polypropylene film has a pseudohexagonal crystal form or a crystal form of a combination of the pseudohexogonal system and α-monoclinic system and a degree of orientation not higher than 3.0 and (iv) the surface of the polypropylene film confronting the layer (b) has a tension in the wet state (T 1 ) of at least 38 dyne/cm when it is allowed to stand still in an atmosphere of a temperature of 20° C. and a relative humidity of 40% for 1 week.

Claim 3

A packaging material according to claim 1 wherein said laminate sheet comprises (c) an oxygen-barrier layer interposed between said layers (a) and (b).

Claim 4

A packaging material according to claim 2 wherein the oxygen-barrier layer (c) is an aluminum foil.

Claim 5

A packaging material according to claim 2 wherein the polypropylene layer (a) has a thickness of 30 to 100μ, the intermediate oxygen-barrier layer (c) has a thickness of 10 to 50μ and the heat-resistant resin layer (b) has a thickness of 2 to 30μ.

Claim 6

A packaging material according to claim 1 wherein the heat-resistant resin layer (b) is composed of a polyethylene terephthalate.

Claim 7

A packaging material according to claim 1 wherein the polypropylene layer (a) has a thickness of 30 to 100μ and the heat-resistant resin layer (b) has a thickness of 10 to 50μ.

Claim 8

A packaging material according to claim 6 wherein the thermoplastic resin constituting layer (d) has a free surface energy of at least 35 dyne/cm.

Claim 9

A packaging material according to claim 1 wherein adjacent layers of the laminate sheet are bonded together with an adhesive selected from an isocyanate type adhesive, an epoxy type adhesive or an isocyanate-epoxy type adhesive.

Claim 10

A packaging material as set forth in claim 1 wherein the polypropylene film has (i) a salad oil extraction ratio not higher than 500 ppm, (ii) a tension in the wet state of at least 40 dyne/cm and (iii) a degree of orientation of 0.4 to 2.3.

Claim 11

A packaging material as set forth in claim 1 wherein the decrease (ΔW) of the wetting tension, defined by the following formula, of the polypropylene film is not larger than 6 dyne/cm, especially not higher than 4 dyne/cm: ΔW=W.sub.O -W.sub.1 wherein W O denotes the wetting tension (dyne/cm) of the polypropylene film just after preparation and W 1 denotes the wetting tension (dyne/cm) of the film when it is allowed to stand still in an atmosphere of a temperature of 20° C. and a relative humidity of 40% for 1 week.

Claim 12

A packaging material for food to be subjected to high-temperature short-time sterilization, which comprises a flexible laminate sheet including (a) a heat-sealable inner face layer of a crystalline polypropylene, (b) a heat-resistant outer face layer of a thermoplastic resin having a melting point or decomposition point higher than the melting point of said polypropylene, (c) an oxygen-barrier layer interposed between said layers (a) and (b), and (d) a layer or layers of themoplastic resin interposed between layers (a) and (c) and/or layers (b) and (c), said heat-resistant thermoplastic resin layer (b) being selected from the group consisting of polyesters and copolyesters comprising recurring units expressed by the following formula: ##STR7## wherein R 1 is an alkylene or cycloalkylene group having 2 to 8 carbon atoms, and R 2 is an arylene group, said thermoplastic resin layer (d) having an impact absorbing coefficient, K I , of at least 0.5×10 -4 cm, said value K I being defined by the formula K I =S/E in which S is the load (in kg/cm) of the resin film having a width of 1 cm under 30% elongation and E is the tensile strength (in kg/cm 2 ) of the resin film S and E both being measured after the high-temperature short-time sterilization, said polypropylene layer being composed of a film of a polypropylene having a melt flow index of 0.5 to 3, said film being characterized in that (i) said film is one prepared by melting in an extruder a crystalline polypropylene having a melt flow index of 0.5 to 3, extruding the melt in the form of a film at a temperature of 230° to 260° C., through a T die, and contacting the extruded film with a chill roll having a surface temperature of 20° to 70° C., to thereby cool rapidly and solidify the film, (ii) when the film is extracted in salad oil at 130° C. for 30 minutes, the amount extracted of the polypropylene is smaller than 1500 ppm, (iii) the polypropylene film has a pseudohexagonal crystal form or a crystal form of a combination of the pseudohexagonal system and α-monoclinic system and a degree of orientation not higher than 3.0 and (iv) the surface of the polypropylene film confronting the oxygen-barrier layer (c) has a tension in the wet state (T 1 ) of at least 38 dyne/cm when it is allowed to stand still in an atmosphere of a temperature of 20° C. and a relative humidity of 40% for 1 week.

Claim 13

A packaging material for food to be subjected to high-temperature short-time sterilization, which comprises a flexible laminate sheet including (a) a heat-sealable inner face layer of a crystalline polypropylene, (b) a heat-resistant outer face layer of a thermoplastic resin having a melting point or decomposition point higher than the melting point of said polypropylene, (c) an oxygen-barrier layer interposed between said layers (a) and (b), and (d) a layer or layers of themoplastic resin interposed between layers (a) and (c) and/or layers (b) and (c), said heat-resistant thermoplastic resin layer (b) being selected from the group consisting of polyesters and copolyesters comprising recurring units expressed by the following formula: ##STR7## wherein R 1 is an alkylene or cycloalkylene group having 2 to 8 carbon atoms, and R 2 is an arylene group, said thermoplastic resin layer (d) having an impact absorbing coefficient, K I , of at least 0.5×10 -4 cm, said value K I being defined by the formula K I =S/E in which S is the load (in kg/cm) of the resin film having a width of 1 cm under 30% elongation and E is the tensile strength (in kg/cm 2 ) of the resin film S and E both being measured after the high-temperature short-time sterilization, said polypropylene layer being composed of a film of a polypropylene having a melt flow index of 0.5 to 3, said film being characterized in that (i) said film is one prepared by melting in an extruder a crystalline polypropylene having a melt flow index of 0.5 to 3, extruding the melt in the form of a film at a temperature of 230° to 260° C., through a T die, and contacting the extruded film with a chill roll having a surface temperature of 20° to 70° C., to thereby cool rapidly and solidify the film, (ii) when the film is extracted in salad oil at 130° C. for 30 minutes, the amount extracted of the polypropylene is smaller than 1500 ppm, (iii) the polypropylene film has a pseudohexagonal crystal form or a crystal form of a combination of the pseudohexagonal system and α-monoclinic system and a degree of orientation not higher than 3.0 and (iv) the surface of the polypropylene film confronting the oxygen-barrier layer (c) has a tension in the wet state (T 1 ) of at least 38 dyne/cm when it is allowed to stand still in an atmosphere of a temperature of 20° C. and a relative humidity of 40% for 1 week.

Claim 14

A packaging material according to claim 11 wherein the oxygen-barrier layer (c) is an aluminum foil.

Claim 15

A packaging material according to claim 11 wherein the thermoplasic resin constituting layer (d) is a resin selected from a polyamide resin, a polycarbonate resin, a polyester-polyether resin or a polyester-polylactone resin.

Claim 16

A packaging material according to claim 13 wherein layer (d) is composed of a nylon selected from nylon-6, nylon-6,6 or nylon-12.

Claim 17

A packaging material according to claim 13 wherein layer (d) is composed of a polyester-polyether having recurring units represented by the following formula: {(OOC--R.sub.2 --COO--CH.sub.2).sub.n).sub.p OOC--R.sub.2 --CO--O--CH.sub.2).sub.m ].sub.l).sub.q }.sub.r wherein R 2 is a phenylene group, n has a value from 2 to 4, m has a value from 2 to 5, l has a value of at least 2, and p,q and r each has a value of at least 1.

Claim 18

A packaging material according to claim 11 wherein layer (d) has a thickness of 5 to 40μ.

Claim 19

A packaging material acccording to claim 16 wherein the polypropylene layer (a) has a thickness of 30 to 100μ, the thermoplastic resin layer (d) has a thickness of 5 to 40μ, the oxygen-barrier layer (c) has a thickness of 5 to 20μ and the heat-resistant resin layer (b) has a thickness of 5 to 20μ.

Claim 20

A packaging material for food to be subjected to high-temperature short-time sterilization, which comprises a flexible laminate sheet including (a) a heat-sealable inner face layer of a crystalline polypropylene and (b) a heat-resistant outer face layer of a thermoplastic resin having a melting point or decomposition point higher than the melting point of said polypropylene, said thermoplastic resin being selected from the group consisting of (a) polyesters and copolyesters comprising recurring units expressed by the following formula: ##STR8## wherein R 1 is an alkylene or cycloalkylene group having 2 to 8 carbon atoms, and R 2 is an arylene group, (b) polyamides and copolyamides comprising recurring units expressed by the following formula: ##STR9## wherein n is a number of 3 to 13 and m is a number of 4 to 11, (c) polycarbonates comprising recurring units represented by the following formula: ##STR10## wherein R 3 is a hydrocarbon group having 8 to 15 carbon atoms, (d) biaxially stretched isotactic polypropylene films, and (e) acetyl cellulose, said heat-sealable inner face layer of said crystalline polypropylene film being characterized in that (i) said film is one prepared by melting in an extruder a crystalline propylene-ethylene block copolymer having 2 to 10% by weight based on the total copolymer of ethylene, and extruding the melt in the form of a film at a temperature of 230° to 260° C., through a T die, and contacting the extruded film with a chill roll having a surface temperature of 20° to 70° C., to thereby cool rapidly and solidify the film, (ii) when the film is extracted in salad oil at 130° C. for 30 minutes, the amount extracted of the copolymer is smaller than 1500 ppm, (iii) the film has a pseudohexagonal crystal form or a crystal form of a combination of the pseudohexagonal system and α-monoclinic system and a degree of orientation not higher than 3.0 and (iv) the surface of the film confronting the layer (b) has a tension in the wet state (T 1 ) of at least 38 dyne/cm when it is allowed to stand still in an atmosphere of a temperature of 20° C. and a relative humidity of 40% for 1 week.

Claim 21

A packaging material for food to be subjected to high-temperature short-time sterilization, which comprises a flexible laminate sheet including (a) a heat-sealable inner face layer of a crystalline polypropylene and (b) a heat-resistant outer face layer of a thermoplastic resin having a melting point or decomposition point higher than the melting point of said polypropylene, said thermoplastic resin being selected from the group consisting of (a) polyesters and copolyesters comprising recurring units expressed by the following formula: ##STR8## wherein R 1 is an alkylene or cycloalkylene group having 2 to 8 carbon atoms, and R 2 is an arylene group, (b) polyamides and copolyamides comprising recurring units expressed by the following formula: ##STR9## wherein n is a number of 3 to 13 and m is a number of 4 to 11, (c) polycarbonates comprising recurring units represented by the following formula: ##STR10## wherein R 3 is a hydrocarbon group having 8 to 15 carbon atoms, (d) biaxially stretched isotactic polypropylene films, and (e) acetyl cellulose, said heat-sealable inner face layer of said crystalline polypropylene film being characterized in that (i) said film is one prepared by melting in an extruder a crystalline propylene-ethylene block copolymer having 2 to 10% by weight based on the total copolymer of ethylene, and extruding the melt in the form of a film at a temperature of 230° to 260° C., through a T die, and contacting the extruded film with a chill roll having a surface temperature of 20° to 70° C., to thereby cool rapidly and solidify the film, (ii) when the film is extracted in salad oil at 130° C. for 30 minutes, the amount extracted of the copolymer is smaller than 1500 ppm, (iii) the film has a pseudohexagonal crystal form or a crystal form of a combination of the pseudohexagonal system and α-monoclinic system and a degree of orientation not higher than 3.0 and (iv) the surface of the film confronting the layer (b) has a tension in the wet state (T 1 ) of at least 38 dyne/cm when it is allowed to stand still in an atmosphere of a temperature of 20° C. and a relative humidity of 40% for 1 week.