Vascular prosthesis and method of making the same
Assignee: Iowa State University Research Foundation Inc
•
Filing: 1979-05-23
•
Granted: 1981-09-01
•
Expires: 1999-05-23
Abstract
Abstract A vascular prosthesis and its method of fabrication. The prosthesis takes the form of a flexible and conformable support tube having a luminal surface formed of a smooth, homogenous, and substantially non-thrombogenic hydrogel having relatively small pores or microvoids suitable for tissue ingrowth but resistant to thrombus formation, and having an outer surface formed of essentially the same hydrogel having a heterogenous microstructure which includes relatively large pores or macrovoids especially suitable for cellular ingrowth from perigraft sources and attachment sites. In one embodiment, the tubular substrate is foraminous and the inner and outer hydrogel layers merge through the interstices of the substrate to provide a unified ground substance characterized by strata having selectively different pore characteristics for promoting effective endothelialization and for reducing possibilities of thrombotic occlusion.
Inventors
- 👤 Raymond T. Greer
- 👤 Bradley H. Vale
- 👤 Randall L. Knoll
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-22 20:11
CPC Classifications
A; A61; A61L; A61L27/00; A61L27/14; A61F; A61F2/00; A61F2/02; A61F2/04; A61F2/06; A61L33/00; A61L33/06; A61L33/064; A61F2250/00; A61F2250/0014; A61F2250/0023
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
75 words
A vascular prosthesis comprising a flexible support tube having a porous homogenous hydrogel layer along the inside thereof and a porous heterogenous hydrogel layer along the outside thereof, said homogenous layer having pores of a maximum size less than 20 microns Feret diameter, and said heterogenous layer having pores of the same size as said homogenous layer and in addition having larger pores of a Feret diameter within the range of 20 to 200 microns.
Claim 2
Dependent Claim
75 words
A vascular prosthesis comprising a flexible support tube having a porous homogenous hydrogel layer along the inside thereof and a porous heterogenous hydrogel layer along the outside thereof, said homogenous layer having pores of a maximum size less than 20 microns Feret diameter, and said heterogenous layer having pores of the same size as said homogenous layer and in addition having larger pores of a Feret diameter within the range of 20 to 200 microns.
Claim 3
Dependent Claim
24 words
The prosthesis of claim 1 in which said pores of said homogenous layer have a maximum size less than 10 microns in Feret diameter.
Claim 4
Dependent Claim
21 words
The prosthesis of claim 1 in which said larger pores of said heterogenous layer all have Feret diameters above 30 microns.
Claim 5
Dependent Claim
25 words
The prosthesis of claim 1 in which the hydrogel of said homogenous layer has the same chemical composition as the hydrogel of said heterogenous layer.
Claim 6
Dependent Claim
17 words
The prosthesis of claim 4 in which said hydrogel is a sparingly cross-linked polymer of hyroxyalkyl methacrylate.
Claim 7
Dependent Claim
13 words
The prosthesis of claim 5 in which said hydroxyalkyl methacrylate is 2-hydroxyethyl methacrylate.
Claim 8
Dependent Claim
16 words
The prosthesis of claim 6 in which said polymer is sparingly cross-linked by ethylene glycol dimethacrylate.
Claim 9
Dependent Claim
23 words
The prosthesis of claim 1 in which the inside diameter of said tube falls within the general range of 1 to 30 millimeters.
Claim 10
Dependent Claim
16 words
The prosthesis of claim 8 in which said tube has an inside diameter under 10 millimeters.
Claim 11
Dependent Claim
21 words
The prosthesis of claim 8 in which said tube has a wall thickness within the range of 0.5 to 1.5 millimeters.
Claim 12
Dependent Claim
128 words
A vascular prosthesis comprising a flexible support tube having an inside diameter within the range of 1 to 30 millimeters and having a wall of open mesh construction with openings extending therethrough, a porous homogenous hydrogel layer secured to and extending along the inside of said tube and a porous heterogenous hydrogel layer secured to and extending along the outside of said tube, said homogeneous layer having pores extending therethrough of a maximum size less than 20 microns Feret diameter, and said heterogenous layer having pores of the same size as said homogenous layer and in addition having larger pores of a Feret diameter within the range of 20 to 200 microns, said inner and outer hydrogel layers extending into the openings of said wall of said tube.
Claim 13
Dependent Claim
128 words
A vascular prosthesis comprising a flexible support tube having an inside diameter within the range of 1 to 30 millimeters and having a wall of open mesh construction with openings extending therethrough, a porous homogenous hydrogel layer secured to and extending along the inside of said tube and a porous heterogenous hydrogel layer secured to and extending along the outside of said tube, said homogeneous layer having pores extending therethrough of a maximum size less than 20 microns Feret diameter, and said heterogenous layer having pores of the same size as said homogenous layer and in addition having larger pores of a Feret diameter within the range of 20 to 200 microns, said inner and outer hydrogel layers extending into the openings of said wall of said tube.
Claim 14
Dependent Claim
27 words
The prosthesis of claim 11 in which said heterogenous hydrogel layer extends into the openings in the wall of said tube and contacts said homogenous hydrogel layer.
Claim 15
Dependent Claim
25 words
The prosthesis of claim 12 in which said homogenous hydrogel layer extends into at least some of the larger pores of said heterogenous hydrogel layer.
Claim 16
Dependent Claim
20 words
The prosthesis of claim 12 in which said homogenous and heterogenous hydrogel layers are of substantially the same chemical composition.
Claim 17
Dependent Claim
23 words
The prosthesis of claim 14 in which said hydrogel of said homogenous and heterogenous layers is a sparingly cross-linked polymer of hydroxyalkyl methacrylate.
Claim 18
Dependent Claim
13 words
The prosthesis of claim 15 in which said hydroxyalkyl methacrylate is 2-hydroxyethyl methacrylate.
Claim 19
Dependent Claim
16 words
The prosthesis of claim 16 in which said polymer is sparingly cross-linked by ethylene glycol dimethacrylate.
Claim 20
Dependent Claim
36 words
The prosthesis of claim 11 in which said flexible support tube is formed from a material selected from the group consisting of polyethylene terephthalate, polytetrafluoroethylene, polyethylene, poly-E-caprolactone, poly(glycolic acid), poly (lactic acid), and poly(hydroxy butyric acid).
Claim 21
Dependent Claim
20 words
The prosthesis of claim 11 in which said pores of said homogenous layer are less than 10 microns Feret diameter.
Claim 22
Dependent Claim
20 words
The prosthesis of claim 11 in which said larger pores of said heterogenous layers have Feret diameters under 30 microns.
Claim 23
Dependent Claim
21 words
The prosthesis of claim 11 in which said tube has a wall thickness within the range of 0.5 to 1.5 millimeters.
Claim 24
Independent Claim
175 words
A method for making a vascular prosthesis, comprising the steps of impregnating a porous flexible support tube with a polymerizable mixture of a monolefinic monomer and a minor proportion of a cross-linking agent dissolved in a first cosolvent medium comprising a first constituent in which both the monomer and polymer are readily soluble and a second constituent in which said monomer is soluble but said polymer is substantially insoluble, said second constituent exceeding 45% by weight of said polymerizable mixture, polymerizing said monomer in said first cosolvent medium to provide a cross-linked heterogenous hydrogel having a microstructure characterized by both microvoids and macrovoids, coating the interior of said tube with a second polymerizable mixture of the same monomer and cross-linking agent in a second cosolvent medium containing the same constituents as said first cosolvent medium but wherein said second constituent is less than 45% by weight of the polymerizable mixture, and polymerizing said monomer of said second mixture to produce a smooth hydrogel lining for said tube having a homogenous microstructure substantially free of macrovoids.
Claim 25
Independent Claim
175 words
A method for making a vascular prosthesis, comprising the steps of impregnating a porous flexible support tube with a polymerizable mixture of a monolefinic monomer and a minor proportion of a cross-linking agent dissolved in a first cosolvent medium comprising a first constituent in which both the monomer and polymer are readily soluble and a second constituent in which said monomer is soluble but said polymer is substantially insoluble, said second constituent exceeding 45% by weight of said polymerizable mixture, polymerizing said monomer in said first cosolvent medium to provide a cross-linked heterogenous hydrogel having a microstructure characterized by both microvoids and macrovoids, coating the interior of said tube with a second polymerizable mixture of the same monomer and cross-linking agent in a second cosolvent medium containing the same constituents as said first cosolvent medium but wherein said second constituent is less than 45% by weight of the polymerizable mixture, and polymerizing said monomer of said second mixture to produce a smooth hydrogel lining for said tube having a homogenous microstructure substantially free of macrovoids.
Claim 26
Dependent Claim
12 words
The method of claim 22 in which said monomer is hydroxyethyl methacrylate.
Claim 27
Dependent Claim
40 words
The method of claim 22 in which said first constituent of said cosolvent medium is selected from the group consisting of methanol, ethanol, dioxane, dimethyl formamide, tetrahydrofuryl alcohol, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, dimethyl sulfoxide, and 2,2,3,3-tetrafluoropropanol.
Claim 28
Dependent Claim
24 words
The method of claim 22 in which said second constituent of said cosolvent medium is selected from the group consisting of water and 1-butanol.
Claim 29
Dependent Claim
26 words
The method of claim 22 in which said step of coating the interior of said tube includes contacting said heterogenous hydrogel with said second polymerizable mixture.
Claim 30
Dependent Claim
21 words
The method of claim 26 wherein said second polymerizable mixture invades at least some of the macrovoids of said heterogenous hydrogel.
Claim 31
Dependent Claim
36 words
The method of claim 22 in which said porous flexible support tube is formed of a material selected from the group consisting of polyethylene terephthalate, polytetrafluoroethylene, polyethylene, poly-E-caprolactone, poly(glycolic acid), poly(lactic acid), and poly(hydroxy butyric acid).
Claim 32
Independent Claim
149 words
A method for making a vascular prosthesis, comprising the steps of impregnating a porous flexible support tube with a polymerizable mixture of a water-soluble monolefinic monomer and a minor proportion of a cross-linking agent dissolved in a first solvent consisting essentially of water and a water-miscible organic solvent, said water exceeding 45% by weight of said mixture, polymerizing said monomer in said first solvent to produce a cross-linked heterogenous hydrogel having a microstructure characterized by both microvoids and macrovoids, coating the interior of said tube with a second polymerizable mixture of the same monomer and cross-linking agent in a second solvent containing the same components as said first solvent but wherein the water content is less than 45% by weight of said second mixture, and polymerizing said monomer of said second mixture to produce a smooth hydrogel lining for said tube having a homogenous microstructure substantially free of macrovoids.
Claim 33
Independent Claim
149 words
A method for making a vascular prosthesis, comprising the steps of impregnating a porous flexible support tube with a polymerizable mixture of a water-soluble monolefinic monomer and a minor proportion of a cross-linking agent dissolved in a first solvent consisting essentially of water and a water-miscible organic solvent, said water exceeding 45% by weight of said mixture, polymerizing said monomer in said first solvent to produce a cross-linked heterogenous hydrogel having a microstructure characterized by both microvoids and macrovoids, coating the interior of said tube with a second polymerizable mixture of the same monomer and cross-linking agent in a second solvent containing the same components as said first solvent but wherein the water content is less than 45% by weight of said second mixture, and polymerizing said monomer of said second mixture to produce a smooth hydrogel lining for said tube having a homogenous microstructure substantially free of macrovoids.
Claim 34
Dependent Claim
12 words
The method of claim 29 in which said monomer is hydroxyethyl methacrylate.
Claim 35
Dependent Claim
35 words
The method of claim 29 in which said organic solvent is selected from the group consisting of methanol, ethanol, dimethyl formamide, tetrahydrofuryl alcohol, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, dimethyl sulfoxide, and 2,2,3,3-tetrafluoropropanol.
Claim 36
Dependent Claim
26 words
The method of claim 29 in which said step of coating the interior of said tube includes contacting said heterogenous hydrogel with said second polymerizable mixture.
Claim 37
Dependent Claim
21 words
The method of claim 32 wherein said second polymerizable mixture invades at least some of the macrovoids of said heterogenous hydrogel.
Claim 38
Dependent Claim
35 words
The method of claim 29 in which said porous flexible support tube is formed of a material selected from the group consisting of polyethylene terephthalate, polytetrafluoroethylene, polyethylene, poly-E-caprolactone, poly(glycolic acid), poly(lactic acid), and poly(hydroxybutyric acid).
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-31 | 1985-03-02 | 1985-09-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-31 | 1989-03-02 | 1989-09-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-31 | 1993-03-02 | 1993-09-01 | $7700.00 | Window Closed / Lapsed |