Electrically conductive fiber and method for producing the same
Assignee: Teijin Ltd
•
Filing: 1980-02-06
•
Granted: 1981-05-12
•
Expires: 2000-02-06
Abstract
Abstract An electrically conductive fiber having an electric resistivity of 1×10 12 ohm/cm or less under a D.C. voltage of 1 K.V., contains copper (I) iodide which has been deposited in the inside of at least the peripheral surface layer of an electrically non-conductive fiber matrix by contacting iodine with copper (I) ions therein.
Inventors
- 👤 Hiroaki Tanaka
- 👤 Kiyokazu Tsunawaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 12:26
CPC Classifications
D; D06; D06M; D06M11/00; D06M11/07; D06M11/11; D06M11/13; Y; Y10; Y10S; Y10S57/00; Y10S57/901; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/294; Y10T428/2958; Y10T428/2964; Y10T428/2967; Y10T428/2969; Y10T442/00; Y10T442/30; Y10T442/3049; Y10T442/3976; Y10T442/40; Y10T442/419; Y10T442/60; Y10T442/603
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
76 words
An electrically conductive fiber comprising an organic polymeric fiber matrix and copper (I) iodide which is located in the inside of at least the peripheral surface layer of said organic polymeric fiber matrix and which is in an amount sufficient to cause the electric resistivity of the conductive fiber under a D.C. voltage of 1 K.V. at a temperature of 20° C. and at a relative humidity of 65% to be 1×10 12 ohm/cm or less.
Claim 2
Dependent Claim
76 words
An electrically conductive fiber comprising an organic polymeric fiber matrix and copper (I) iodide which is located in the inside of at least the peripheral surface layer of said organic polymeric fiber matrix and which is in an amount sufficient to cause the electric resistivity of the conductive fiber under a D.C. voltage of 1 K.V. at a temperature of 20° C. and at a relative humidity of 65% to be 1×10 12 ohm/cm or less.
Claim 3
Dependent Claim
30 words
An electrically conductive fiber as claimed in claim 1, wherein the amount of copper (I) iodide is at least 2% based on the weight of said organic polymeric fiber matrix.
Claim 4
Dependent Claim
35 words
An electrically conductive fiber as claimed in claim 2, wherein the amount of copper (I) iodide is in a range of from 2 to 250% based on the weight of said organic polymeric fiber matrix.
Claim 5
Dependent Claim
43 words
An electrically conductive fiber as claimed in claim 1, wherein said organic polymeric fiber matrix is selected from the group consisting of polyester, aliphatic polyamide, whole aromatic polyamide, polyacrylic, vinyl compound polymer, cellulose diacetate and cellulose triacetate fibers, animal hair fibers and silk.
Claim 6
Independent Claim
118 words
A method for producing an electrically conductive fiber which comprises an organic polymeric fiber matrix and copper (I) iodide contained within at least the peripheral surface layer of said organic polymeric fiber matrix, and which exhibits an electric resistivity of 1×10 12 ohm/cm or less under a D.C. voltage of 1 K.V. at a temperature of 20° C. and at a relative humidity of 65%, said method comprising bringing iodine into contact with copper (I) ions in the inside of at least the peripheral surface layer of said organic polymeric fiber matrix and depositing the resultant copper (I) iodide therein in an amount sufficient to result in the above-mentioned level of electric resistivity of the resultant conductive fiber.
Claim 7
Independent Claim
118 words
A method for producing an electrically conductive fiber which comprises an organic polymeric fiber matrix and copper (I) iodide contained within at least the peripheral surface layer of said organic polymeric fiber matrix, and which exhibits an electric resistivity of 1×10 12 ohm/cm or less under a D.C. voltage of 1 K.V. at a temperature of 20° C. and at a relative humidity of 65%, said method comprising bringing iodine into contact with copper (I) ions in the inside of at least the peripheral surface layer of said organic polymeric fiber matrix and depositing the resultant copper (I) iodide therein in an amount sufficient to result in the above-mentioned level of electric resistivity of the resultant conductive fiber.
Claim 8
Dependent Claim
55 words
A method as claimed in claim 5, wherein said contact of iodine with said copper (I) ions is effected by the absorption of iodine by at least the peripheral surface layer of said organic polymeric fiber matrix and, then, by contact of said iodine-absorbed fiber matrix with an aqueous solution containing a copper (I) compound.
Claim 9
Dependent Claim
33 words
A method as claimed in claim 6, wherein said absorption operation is carried out by bringing said organic polymeric fiber matrix into contact with an aqueous solution containing iodine and an iodine-dissolving promoter.
Claim 10
Dependent Claim
29 words
A method as claimed in claim 6, wherein said copper (I) compound is selected from the group consisting of copper (I) chloride, copper (I) bromide and copper (I) sulfite.
Claim 11
Dependent Claim
31 words
A method as claimed in claim 6, wherein said aqueous solution of said copper (I) compound is prepared by reducing a copper (II) compound dissolved in water with a reducing agent.
Claim 12
Dependent Claim
31 words
A method as claimed in claim 6, wherein said contact of said iodine-absorbed fiber matrix with said copper (I) compound aqueous solution is carried out in the presence of metallic copper.
Claim 13
Dependent Claim
18 words
A method as claimed in claim 10, wherein said contact is carried out in a nitrogen gas atmosphere.
Claim 14
Dependent Claim
57 words
A method as claimed in claim 5, wherein said contact of iodine with said copper (I) ions is effected by the absorption of said copper (I) ions by at least the peripheral surface layer of said organic polymeric fiber matrix and, then, by contact of said copper (I) ion-absorbed fiber matrix, with an aqueous solution containing iodine.
References Cited (Backward Citations)
US3817784A
Cited
US3983286A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-11 | 1984-11-10 | 1985-05-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-11 | 1988-11-10 | 1989-05-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-11 | 1992-11-10 | 1993-05-12 | $7700.00 | Window Closed / Lapsed |