Reaction injection molded polyurethanes having particular flexural modulus factors and at least two thermal transition temperatures in a particular range

Claim 2

A polyurethane having a flexural modulus factor (-20° F./158° F.) of not greater than about 3.4 and at least three thermal transition temperatures measured between -100° C. and the decomposition temperature of the polyurethane as determined by thermomechanical analysis.

Claim 3

The polyurethane of claim 1 wherein the flexural modulus factor (-20° F./158° F.) is less than about 3.

Claim 4

The polyurethane of claim 1 wherein the flexural modulus factor (-20° F./158° F.) is less than about 2.75.

Claim 5

The polyurethane of claim 1 wherein the flexural modulus factor (-20° F./158° F.) is less than about 2.0.

Claim 6

A polyurethane composition having a flexural modulus factor (-20° F./158° F.) of not greater than 3.4 and at least two thermal transition temperatures between -100° C. and the decomposition temperature of the polyurethane as determined by thermomechanical analysis, said composition resulting from admixing and reacting the components of a composition comprising at least three different polyols having different relative reactivities at the temperature of reaction and an organic compound having a plurality of NCO and/or NCS groups wherein each of said polyols have a solubility parameter different from each other by a value greater than 0.49 when said polyols are present in quantities such that the number of active hydrogen equivalents contributed by the second most reactive polyol is greater than that contributed by the most reactive polyol, said solubility parameters being determined by the method of Small and wherein the NCO and/or NCS:active hydrogen equivalent ratio is from about 0.75:1 to about 1.5:1.

Claim 7

A polyurethane composition having a flexural modulus factor (-20° F./158° F.) of not greater than 3.4 and at least two thermal transition temperatures between -100° C. and the decomposition temperature of the polyurethane as determined by thermomechanical analysis, said composition resulting from admixing and reacting the components of a composition comprising at least three different polyols having different relative reactivities at the temperature of reaction and an organic compound having a plurality of NCO and/or NCS groups wherein each of said polyols have a solubility parameter different from each other by a value greater than 0.49 when said polyols are present in quantities such that the number of active hydrogen equivalents contributed by the second most reactive polyol is greater than that contributed by the most reactive polyol, said solubility parameters being determined by the method of Small and wherein the NCO and/or NCS:active hydrogen equivalent ratio is from about 0.75:1 to about 1.5:1.

Claim 8

A polyurethane composition having a flexural modulus factor (-20° F./158° F.) of not greater than 3.4 and at least two thermal transition temperatures between -100° C. and the decomposition temperature of the polyurethane as determined by thermomechanical analysis, said composition resulting from admixing and reacting the components of a composition comprising: (A) a first polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an average active hydrogen equivalent weight of from about 50 to about 4000 and an average active hydrogen functionality of from about 2 to about 8; (B) a second polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an average active hydrogen equivalent weight of from about 50 to about 4000 and an active hydrogen functionality of from about 2 to about 8; (C) a third polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an active hydrogen equivalent weight of from about 20 to about 4000 and an average active hydrogen functionality of from about 2 to about 6; and (D) an organic compound having a plurality of NCO and/or NCS groups or mixture of such compounds; wherein (1) at least two of the polyol components (A), (B) and (C) have different relative reactivities, at the temperature of reaction, with component (D) and the relative reactivity of polyol component (B) being equal to or greater than that of polyol components (A) and (C); (2) the solubility parameter of each of the polyols in polyol components (A), (B) and (C) is different from each other by a value greater than 0.49 when the number of active hydrogen equivalents contributed by polyol component (C) is greater than the number of active hydrogen equivalents contributed by polyol component (B) said solubility parameters being determined by the method of Small; (3) the NCO and/or NCS:active hydrogen equivalent ratio is from about 0.75:1 to about 1.5:1.

Claim 9

A polyurethane composition having a flexural modulus factor (-20° F./158° F.) of not greater than 3.4 and at least two thermal transition temperatures between -100° C. and the decomposition temperature of the polyurethane as determined by thermomechanical analysis, said composition resulting from admixing and reacting the components of a composition comprising: (A) a first polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an average active hydrogen equivalent weight of from about 50 to about 4000 and an average active hydrogen functionality of from about 2 to about 8; (B) a second polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an average active hydrogen equivalent weight of from about 50 to about 4000 and an active hydrogen functionality of from about 2 to about 8; (C) a third polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an active hydrogen equivalent weight of from about 20 to about 4000 and an average active hydrogen functionality of from about 2 to about 6; and (D) an organic compound having a plurality of NCO and/or NCS groups or mixture of such compounds; wherein (1) at least two of the polyol components (A), (B) and (C) have different relative reactivities, at the temperature of reaction, with component (D) and the relative reactivity of polyol component (B) being equal to or greater than that of polyol components (A) and (C); (2) the solubility parameter of each of the polyols in polyol components (A), (B) and (C) is different from each other by a value greater than 0.49 when the number of active hydrogen equivalents contributed by polyol component (C) is greater than the number of active hydrogen equivalents contributed by polyol component (B) said solubility parameters being determined by the method of Small; (3) the NCO and/or NCS:active hydrogen equivalent ratio is from about 0.75:1 to about 1.5:1.

Claim 10

The polyurethane composition of claim 6 wherein: (1) said first polyol component has an active hydrogen equivalent weight of from about 70 to about 3000 and a functionality of from about 2 to about 4; (2) said second polyol component has an active hydrogen equivalent weight of from about 65 to about 1000 and a functionality of from about 3 to about 4; (3) said third polyol component has an active hydrogen equivalent weight of from about 30 to about 120 and a functionality of from about 2 to about 4; (4) the NCO and/or NCS:active hydrogen ratio is from about 0.75:1 to about 1.25:1 and (5) the relative reactivities for all three of said first, second or third polyol or mixture of polyols are different; and (6) component (D) is an aromatic compound.

Claim 11

The polyurethane composition of claim 7 wherein: (1) said first polyol component has an active hydrogen equivalent weight of from about 85 to about 2500; (2) said second polyol component has an active hydrogen equivalent weight of from about 65 to about 500; (3) said third polyol component has an active hydrogen equivalent weight of from about 50 to about 100 and a functionality of from about 2 to about 3; (4) the NCO and/or NCS:active hydrogen equivalent ratio is from about 0.95:1 to about 1.25:1; and (5) the relative reactivities for all three of said first, second or third polyol components are in the order of second >third>first.

Claim 12

The polyurethane of claim 8 wherein the solubility parameter of said first, second and third polyol components differ from each other by a value of at least 1, and the NCO and/or NCS:active hydrogen equivalent ratio is from about 1.01:1 to about 1.10:1.

Claim 13

The polyurethane of claim 9 wherein (1) each of said first, second and third polyol components contain only active hydrogens derived from --OH, --NH, or NH 2 groups; and (2) component (D) is a compound or mixture of compounds having only a plurality of NCO groups.

Claim 14

The polyurethane of claim 10 wherein each of said first, second and third polyol components contain only active hydrogens derived from OH groups.

Claim 15

The polyurethane of claims 6, 7, 8, 9, 10 or 11 wherein the flexural modulus factor (-20° F./158° F.) is less than about 3.

Claim 16

The polyurethane of claims 6, 7, 8, 9, 10 or 11 wherein the flexural modulus factor (-20° F./158° F.) is less than about 2.75.

Claim 17

The polyurethane of claims 6, 7, 8, 9, 10 or 11 wherein the flexural modulus factor (-20° F./158° F.) is less than about 2.0.

Claim 18

The polyurethane of claim 12 containing at least three thermal transition temperatures.

Claim 19

The polyurethane of claim 13 containing at least three thermal transition temperatures.

Claim 20

The polyurethane of claim 14 containing at least three thermal transition temperatures.

Claim 21

A polyol mixture suitable for reacting with an organic compound containing a plurality of NCO and/or NCS groups or mixture of such compounds so as to form a polyurethane having at least two thermal transition temperatures, as determined by thermomechanical analysis, between -100° C. and the decomposition temperature of the polyurethane and a flexural modulus factor (-20° F./158° F.) of not greater than 3.4; said polyol mixture comprising: (A) a first polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an average active hydrogen equivalent weight of from about 50 to about 4000 and an average active hydrogen functionality of from about 2 to about 8; (B) a second polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an average active hydrogen equivalent weight of from about 50 to about 4000 and an active hydrogen functionality of from about 2 to about 8; (C) a third polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an active hydrogen equivalent weight of from about 20 to about 4000 and an average active hydrogen functionality of from about 2 to about 6; (1) at least two of the polyol components (A), (B) and (C) have different relative reactivities, at the temperature of reaction, with component (D) and the relative reactivity of polyol component (B) being equal to or greater than that of polyol components (A) and (C); (2) the solubility parameter of each of the polyols in polyol components (A), (B) and (C) is different from each other by a value greater than 0.49 when the number of active hydrogen equivalents contributed by polyol component (C) is greater than the number of active hydrogen equivalents contributed by polyol component (B) said solubility parameters being determined by the method of Small.

Claim 22

A polyol mixture suitable for reacting with an organic compound containing a plurality of NCO and/or NCS groups or mixture of such compounds so as to form a polyurethane having at least two thermal transition temperatures, as determined by thermomechanical analysis, between -100° C. and the decomposition temperature of the polyurethane and a flexural modulus factor (-20° F./158° F.) of not greater than 3.4; said polyol mixture comprising: (A) a first polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an average active hydrogen equivalent weight of from about 50 to about 4000 and an average active hydrogen functionality of from about 2 to about 8; (B) a second polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an average active hydrogen equivalent weight of from about 50 to about 4000 and an active hydrogen functionality of from about 2 to about 8; (C) a third polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an active hydrogen equivalent weight of from about 20 to about 4000 and an average active hydrogen functionality of from about 2 to about 6; (1) at least two of the polyol components (A), (B) and (C) have different relative reactivities, at the temperature of reaction, with component (D) and the relative reactivity of polyol component (B) being equal to or greater than that of polyol components (A) and (C); (2) the solubility parameter of each of the polyols in polyol components (A), (B) and (C) is different from each other by a value greater than 0.49 when the number of active hydrogen equivalents contributed by polyol component (C) is greater than the number of active hydrogen equivalents contributed by polyol component (B) said solubility parameters being determined by the method of Small.

Claim 23

The polyol mixture of claim 18 wherein: (1) said first polyol component has an active hydrogen equivalent weight of from about 70 to about 3000 and a functionality of from about 2 to about 4; (2) said second polyol component has an active hydrogen equivalent weight of from about 65 to about 1000 and a functionality of from about 3 to about 4; (3) said third polyol component has an active hydrogen equivalent weight of from about 30 to about 120 and a functionality of from about 2 to about 4; and (4) the relative reactivities for all three of said first, second and third polyol components are different.

Claim 24

The polyol mixture of claim 19 wherein: (1) said first polyol component has an active hydrogen equivalent weight of from about 85 to about 2500; (2) said second polyol component has an active hydrogen equivalent weight of from about 65 to about 500; (3) said third polyol component has an active hydrogen equivalent weight of from about 50 to about 100 and a functionality of from about 2 to about 3; and (4) the relative reactivities for said first, second and third polyol components are in the order of second>third>first.

Claim 25

The polyol mixture of claim 20 wherein the solubility parameter of said first, second and third polyol components differ from each other by a value of at least 1.

Claim 26

The polyol mixture of claim 21 wherein each of said first, second and third polyol components contain only active hydrogens derived from --OH, ##STR3## or --NH 2 groups.

Claim 27

The polyol mixture of claim 22 wherein each of said first, second and third polyol components contain active hydrogens derived only from OH groups.

Claim 28

A process for the preparation of a polyurethane having a flexural modulus factor (-20° F./158° F.) of not greater than 3.4 and at least two thermal transition temperatures, as determined by thermomechanical analysis, between -100° C. and the decomposition temperature of the polyurethane, which process comprises admixing and reacting the components of a composition comprising: (A) a first polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an average active hydrogen equivalent weight of from about 50 to about 4000 and an average active hydrogen functionality of from about 2 to about 8; (B) a second polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an average active hydrogen equivalent weight of from about 50 to about 4000 and an active hydrogen functionality of from about 2 to about 8; (C) a third polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an active hydrogen equivalent weight of from about 20 to about 4000 and an average active hydrogen functionality of from about 2 to about 6; and (D) an organic compound having a plurality of NCO and/or NCS groups or mixture of such compounds; wherein (1) at least two of the polyol components (A), (B) and (C) have different relative reactivities, at the temperature of reaction, with component (D) and the relative reactivity of polyol component (B) being equal to or greater than that of polyol components (A) and (C); (2) the solubility parameter of each of the polyols in polyol components (A), (B) and (C) is different from each other by a value greater than 0.49 when the number of active hydrogen equivalents contributed by polyol component (C) is greater than the number of active hydrogen equivalents contributed by polyol component (B), said solubility parameters being determined by the method of Small; (3) the NCO and/or NCS:active hydrogen equivalent ratio is from about 0.75:1 to about 1.5:1.

Claim 29

A process for the preparation of a polyurethane having a flexural modulus factor (-20° F./158° F.) of not greater than 3.4 and at least two thermal transition temperatures, as determined by thermomechanical analysis, between -100° C. and the decomposition temperature of the polyurethane, which process comprises admixing and reacting the components of a composition comprising: (A) a first polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an average active hydrogen equivalent weight of from about 50 to about 4000 and an average active hydrogen functionality of from about 2 to about 8; (B) a second polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an average active hydrogen equivalent weight of from about 50 to about 4000 and an active hydrogen functionality of from about 2 to about 8; (C) a third polyol or mixture of polyols having a plurality of hydrogen atoms reactive with an NCO and/or an NCS group, an active hydrogen equivalent weight of from about 20 to about 4000 and an average active hydrogen functionality of from about 2 to about 6; and (D) an organic compound having a plurality of NCO and/or NCS groups or mixture of such compounds; wherein (1) at least two of the polyol components (A), (B) and (C) have different relative reactivities, at the temperature of reaction, with component (D) and the relative reactivity of polyol component (B) being equal to or greater than that of polyol components (A) and (C); (2) the solubility parameter of each of the polyols in polyol components (A), (B) and (C) is different from each other by a value greater than 0.49 when the number of active hydrogen equivalents contributed by polyol component (C) is greater than the number of active hydrogen equivalents contributed by polyol component (B), said solubility parameters being determined by the method of Small; (3) the NCO and/or NCS:active hydrogen equivalent ratio is from about 0.75:1 to about 1.5:1.

Claim 30

The process of claim 24 wherein: (1) said first polyol component has an active hydrogen equivalent weight of from about 70 to about 3000 and a functionality of from about 1 to about 4; (2) said second polyol component has an active hydrogen equivalent weight of from about 65 to about 1000 and a functionality of from about 3 to about 4; (3) said third polyol component has an active hydrogen equivalent weight of from about 30 to about 120 and a functionality of from about 2 to about 4; (4) the NCO and/or NCS:active hydrogen ratio is from about 0.75:1 to about 1.25:1; and (5) the relative reactivities for all three of said first, second or third polyol components are different, and (6) component (D) is an aromatic compound.

Claim 31

The process of claim 25 wherein: (1) said first polyol component has an active hydrogen equivalent weight of from about 85 to about 2500; (2) said second polyol component has an active hydrogen equivalent weight of from about 65 to about 500; (3) said third polyol component has an active hydrogen equivalent weight of from about 50 to about 100 and a functionality of from about 2 to about 3; (4) the NCO and/or NCS:active hydrogen equivalent ratio is from about 0.95:1 to about 1.25:1; and (5) the relative reactivities for said first, second or third polyol components are in the order of second>third>first.

Claim 32

The process of claim 26 wherein (1) the solubility parameter of said first, second and third polyol components differ from each other by a value of at least 1, and (2) the NCO and/or NCS:active hydrogen equivalent ratio is from about 1.01:1 to about 1.10:1.

Claim 33

The process of claim 27 wherein (1) each of said first, second and third polyol components contain only active hydrogens derived from --OH, ##STR4## or --NH 2 groups; and (2) component (D) is a compound or mixture of compounds having only a plurality of NCO groups.

Claim 34

The process of claim 28 wherein each of said first, second and third polyol components contain only active hydrogens derived from OH groups.

Claim 35

The process of claims 24, 25, 26, 27, 28 or 29 wherein the resultant polyurethane has a flexural modulus factor (-20° F./158° F.) of less than about 3.

Claim 36

The process of claims 24, 25, 26, 27, 28 or 29 wherein the resultant polyurethane has a flexural modulus factor (-20° F./158° F.) of less than about 2.75.

Claim 37

The process of claims 24, 25, 26, 27, 28 or 29 wherein the resultant polyurethane has a flexural modulus factor (-20° F./158° F.) of less than about 2.0.

Claim 38

The process of claim 30 wherein the resultant polyurethane contains at least three thermal transition temperatures.

Claim 39

The process of claim 31 wherein the resultant polyurethane contains at least three thermal transition temperatures.

Claim 40

The process of claim 32 wherein the resultant polyurethane contains at least three thermal transition temperatures.

Claim 41

The composition of claim 5 wherein the flexural modulus factor (-20° F./158° F.) is less than about 3 and the organic compound is an aromatic polyisocyanate.

Claim 42

The composition of claim 5 wherein the flexural modulus factor (-20° F./158° F.) is less than about 2.75 and the organic compound is an aromatic polyisocyanate.

Claim 43

The composition of claim 5 wherein the flexural modulus factor (-20° F./158° F.) is less than about 2.0 and the organic compound is an aromatic polyisocyanate.

Claim 44

The composition of claims 5, 36, 37 or 38 wherein the solubility parameter of each of the polyols is different by a value of at least 1 regardless of the number of active hydrogen equivalents contributed by each polyol.