US4242384A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Spray coating of acrylic resin comprising polymeric microparticles
Assignee: Imperial Chemical Industries Ltd
•
Filing: 1978-07-07
•
Granted: 1980-12-30
•
Expires: 1998-07-07
Abstract
Abstract A process for coating a substrate, especially an automobile body, by spray application whereby improved resistance to "sagging" or "running" on application can be obtained without reduction of the thickness of film which is applied; the process is characterized by the use of a coating composition comprising a film-forming acrylic resin, a volatile organic liquid diluent, a pigment other than a metallic flake pigment, and specified polymer microparticles which are stably dispersed in the combination of the resin and the diluent.
Inventors
- 👤 Malcolm S. Andrew
- 👤 Alan J. Backhouse
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 19:18
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/14; B05D7/16; C; C09; C09D; C09D133/00; C09D133/04; C09D133/06; C08; C08L; C08L2205/00; C08L2205/14; C08L2205/18; C08L51/00; C08L51/003; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31678; Y10T428/31692; Y10T428/31699
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
267 words
A process for the production of a surface coating upon a substrate which comprises (i) applying by spray to the substrate surface a composition comprising (A) a film-forming acrylic resin which is derived from one or more alkyl esters of acrylic acid or methacrylic acid, (B) a volatile organic liquid diluent in which the polymer (A) is carried, and (C) a pigment, other than a metallic flake pigment, which is dispersed in the combination of the film-forming resin (A) and the diluent (B), and (ii) subsequently evaporating the volatile diluent to form a polymer film upon the surface, characterised in that the composition applied to the substrate further comprises (D) microparticles having a diameter of from 0.01 to 10 microns composed of a polymer which has a glass-liquid transition temperature greater than 0° C., and which are insoluble in and stably dispersed in the combination of the resin (A) and the diluent (B), the microparticles being obtained by (a) polymerisation of monomer in an inert liquid in which the resulting polymer is insoluble and under conditions such that the polymer is obtained in a state of stable dispersion and (b) subsequent polymerisation, in the same inert liquid and in the presence of the particles formed in stage (a), of ethylenically unsaturated monomer giving rise to a second acrylic polymer or copolymer which is compatible with the acrylic resin (A) and is soluble in the combination of the resin (A) and the diluent (B), and the microparticles (D) being present in an amount of at least 3% of the aggregate weight of the resin (A) and the microparticles.
Claim 2
Dependent Claim
267 words
A process for the production of a surface coating upon a substrate which comprises (i) applying by spray to the substrate surface a composition comprising (A) a film-forming acrylic resin which is derived from one or more alkyl esters of acrylic acid or methacrylic acid, (B) a volatile organic liquid diluent in which the polymer (A) is carried, and (C) a pigment, other than a metallic flake pigment, which is dispersed in the combination of the film-forming resin (A) and the diluent (B), and (ii) subsequently evaporating the volatile diluent to form a polymer film upon the surface, characterised in that the composition applied to the substrate further comprises (D) microparticles having a diameter of from 0.01 to 10 microns composed of a polymer which has a glass-liquid transition temperature greater than 0° C., and which are insoluble in and stably dispersed in the combination of the resin (A) and the diluent (B), the microparticles being obtained by (a) polymerisation of monomer in an inert liquid in which the resulting polymer is insoluble and under conditions such that the polymer is obtained in a state of stable dispersion and (b) subsequent polymerisation, in the same inert liquid and in the presence of the particles formed in stage (a), of ethylenically unsaturated monomer giving rise to a second acrylic polymer or copolymer which is compatible with the acrylic resin (A) and is soluble in the combination of the resin (A) and the diluent (B), and the microparticles (D) being present in an amount of at least 3% of the aggregate weight of the resin (A) and the microparticles.
Claim 3
Dependent Claim
34 words
A process according to claim 1, wherein the acrylic resin is a polymer or copolymer of one or more alkyl esters of acrylic acid or methacrylic acid, optionally together with other ethylenically unsaturated monomers.
Claim 4
Dependent Claim
28 words
A process according to claim 1 or claim 2, wherein the acrylic resin is of the thermosetting, cross-linking type and the composition contains in addition a cross-linking agent.
Claim 5
Dependent Claim
14 words
A process according to claim 1, wherein the microparticulate polymer is an acrylic polymer.
Claim 6
Dependent Claim
14 words
A process according to claim 1, wherein the microparticulate polymer is a condensation polymer.
Claim 7
Dependent Claim
76 words
A process according to claim 1, wherein the microparticles are obtained by dispersion polymerisation of monomers, in an organic liquid in which the resulting polymer is insoluble, in the presence of an amphipathic steric stabilising agent, the molecule of which contains a polymeric component which is solvatable by the liquid in which the dispersion is made and another component which is relatively non-solvatable by that liquid and is capable of associating with the polymer particles produced.
Claim 8
Dependent Claim
37 words
A process according to claim 6, wherein the amphipathic stabilising agent is a graft copolymer comprising a polymer backbone, which is the non-solvatable or "anchor" component, and a plurality of solvatable polymer chains pendant from the backbone.
Claim 9
Dependent Claim
30 words
A process according to claim 7, wherein the polymer backbone is an acrylic polymer chain derived predominantly from methyl methacrylate and the pendant chains are residues of poly (12-hydroxy-stearic acid).
Claim 10
Dependent Claim
38 words
A process according to claim 6, wherein the monomers from which the auxiliary polymer is formed are such that during their polymerisation covalent linkages are developed between the chains of the auxiliary polymer and those of the microparticles.
Claim 11
Dependent Claim
32 words
A process according to claim 1, wherein the polymer microparticles are present in a proportion of from 2% to 30% of the aggregate weight of the acrylic resin (A) and the microparticles.
References Cited (Backward Citations)
GB1242054A
Cited
GB1319781A
Cited
US3832217A
Cited
GB1451948A
Cited
US3862062A
Cited
US3953643A
Cited
US4061835A
Cited
US4115472A
Cited
US4025474A
Cited
US4064294A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-30 | 1984-06-30 | 1984-12-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-30 | 1988-06-30 | 1988-12-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-30 | 1992-06-30 | 1992-12-30 | $7700.00 | Window Closed / Lapsed |