Production of piezoelectric PVDF films
Assignee: AT&T Inc
•
Filing: 1979-03-20
•
Granted: 1980-12-23
•
Expires: 1999-03-20
Abstract
Abstract A method of producing piezoelectric and pyroelectric polyvinylidene fluoride (PVDF) films is shown. A stretched PVDF film having a predominantly β-type crystal structure is rolled for thickness reduction. The rolling orients a substantial percentage of b axes of β crystals normal to the film surface, as determined by X-ray diffraction patterns. An optional annealing step is shown, wherein the rolled film is heated, optionally while under pressure. Improvement in the piezoelectric constant of 25 percent or more is typical.
Inventors
- 👤 Tsuey T. Wang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 14:44
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/18; H; H10; H10N; H10N30/00; H10N30/01; H10N30/09; H10N30/098; C08J2327/00; C08J2327/02; C08J2327/12; C08J2327/16; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/31504; Y10T428/3154
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
79 words
A method of making a polyvinylidene fluoride film by steps comprising uniaxially stretching a polyvinylidene fluoride film having a predominantly α-type crystal structure to form a polyvinylidene fluoride film having a predominantly β-type crystal structure, and poling the film in an electric field, the invention characterized by the further steps comprising passing the stretched film one or more times along the stretch direction through rolling means so as to reduce the thickness of the film prior to said poling.
Claim 2
Independent Claim
79 words
A method of making a polyvinylidene fluoride film by steps comprising uniaxially stretching a polyvinylidene fluoride film having a predominantly α-type crystal structure to form a polyvinylidene fluoride film having a predominantly β-type crystal structure, and poling the film in an electric field, the invention characterized by the further steps comprising passing the stretched film one or more times along the stretch direction through rolling means so as to reduce the thickness of the film prior to said poling.
Claim 3
Dependent Claim
37 words
A method of making a polyvinylidene fluoride film according to the method of claim 1, further characterized in that said rolling reduces the thickness of the film at least 15 percent below its thickness prior to rolling.
Claim 4
Independent Claim
47 words
A method of making polyvinylidene fluoride film according to the method of claims 1 or 2, further characterized by steps comprising annealing the film after the rolling step and prior to the poling step by heating said film to a temperature of at least 70 degrees C.
Claim 5
Independent Claim
31 words
The method of claims 1 or 2 further characterized in that the ratio of the stretched length to the unstretched length of said film prior to rolling is at least 3.
Claim 6
Independent Claim
32 words
The method of claims 1 or 2 further characterized by steps comprising maintaining the film in the stretched state at an elevated temperature for a period of time prior to said rolling.
Claim 7
Independent Claim
57 words
The method of claims 1 or 2 further characterized in that an X-ray diffraction pattern of said film after said rolling, produced by 1.542 Angstrom radiation directed along the easy-tear axis of the film, comprises six substantially equally spaced diffraction spots at a Bragg angle of approximately 10.4 degrees, said spots corresponding to 110 and 200 reflections.
Claim 8
Dependent Claim
40 words
The method of claim 6 further characterized in that the ratio of the maximum X-ray intensity of at least one of said 110 reflections to the maximum intensity of at least one of said 200 reflections is at least 1.1.
Claim 9
Dependent Claim
40 words
The method of claim 6 further characterized in that the ratio of the maximum X-ray intensity of at least one of said 110 reflections to the maximum intensity of at least one of said 200 reflections is at least 1.4.
Claim 10
Dependent Claim
12 words
A polyvinylidene fluoride film produced according to the method of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-23 | 1984-06-23 | 1984-12-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-23 | 1988-06-23 | 1988-12-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-23 | 1992-06-23 | 1992-12-23 | $7700.00 | Window Closed / Lapsed |