Mouldable and extrudable polyether-ester-amide block copolymers
Assignee: ATO Chimie SA
•
Filing: 1978-10-03
•
Granted: 1980-10-28
•
Expires: 1998-10-03
Abstract
Abstract The invention relates to a method of preparing polyether-ester-amide block copolymers having recurrent units of the general formula: ##STR1## wherein A is a polyamide sequence and B a linear or branched polyoxyalkylene glycol sequence, the alkylene radical of which comprises at least two carbon atoms, and wherein n indicates that there is a great number of recurrent units. The plastic materials prepared by the novel method have mechanical properties which allow them to be used in technological transformation operations for the manufacture or moulded or extruded articles such as films, sheaths, fibres for textiles products, etc. They may also be used for making bonded or welded linings. The novel method comprises reacting in the fused state at an elevated temperature and under high vacuum a dicarboxylic polyamide, the COOH groups of which are located at the chain ends, with a polyoxyalkylene glycol hydroxylated at the chain ends, in the presence of a catalyst constituted by a tetraalkylorthotitanate having the general formula Ti(OR) 4 , wherein R is a linear or branched aliphatic hydrocarbon radical having 1 to 24 carbon atoms, such a methyl, isopropyl, butyl, ethylhexyl, dodecyl, hexadodecyl.
Inventors
- 👤 Paul Foy
- 👤 Camille Jungblut
- 👤 Gerard E. Deleens
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 06:47
CPC Classifications
C; C08; C08G; C08G69/00; C08G69/44
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
258 words
A mouldable and extrudable polyetherester-amide block copolymer having the formula: ##STR3## wherein A is a linear saturated aliphatic amide sequence formed from a lactam or amino acid having a hydrocarbon chain containing 4 to 14 carbon atoms, or from a dicarboxylic acid and a diamine, wherein said diacid is in alphatic carboxylic diacid having 4 to 40 carbon atoms; said amide having an average molecular weight between 800 and 5000; and B is a polyether sequence formed from linear or branched aliphatic polyoxyalkylene glycols, mixtures thereof or copolyethers derived therefrom, said polyethers having a molecular weight of from 400 to 3000; wherein the proportion by weight of polyoxyalkylene glycol with respect to the total weight of polyether-ester-amide is from 5 to 50%; and n indicates a sufficient number of repeating units so that said polyether-ester-amide has an intrinsic viscosity of from 0.8 to 2.05; said polyether-ester-amide being obtained by reacting in the fused state a dicarboxylic saturated polyamide having carboxylic chain ends and an average molecular weight of 300 to 15,000 with a linear or branched aliphatic polyoxyalkylene glycol having hydroxylic chain ends and an average molecular weight of 200 to 6,000, said reaction being carried out under high vacuum at a temperature between 100° and 400° C. in the presence of a catalyst comprising a tetra-alkylortho-titanate having the formula Ti(OR) 4 , wherein R is a linear or branched aliphatic hydrocarbon radical having from 1 to 24 carbon atoms, the amount of said catalyst with respect to the reactive mixture is between 0.01 and 5% by weight.
Claim 2
Dependent Claim
258 words
A mouldable and extrudable polyetherester-amide block copolymer having the formula: ##STR3## wherein A is a linear saturated aliphatic amide sequence formed from a lactam or amino acid having a hydrocarbon chain containing 4 to 14 carbon atoms, or from a dicarboxylic acid and a diamine, wherein said diacid is in alphatic carboxylic diacid having 4 to 40 carbon atoms; said amide having an average molecular weight between 800 and 5000; and B is a polyether sequence formed from linear or branched aliphatic polyoxyalkylene glycols, mixtures thereof or copolyethers derived therefrom, said polyethers having a molecular weight of from 400 to 3000; wherein the proportion by weight of polyoxyalkylene glycol with respect to the total weight of polyether-ester-amide is from 5 to 50%; and n indicates a sufficient number of repeating units so that said polyether-ester-amide has an intrinsic viscosity of from 0.8 to 2.05; said polyether-ester-amide being obtained by reacting in the fused state a dicarboxylic saturated polyamide having carboxylic chain ends and an average molecular weight of 300 to 15,000 with a linear or branched aliphatic polyoxyalkylene glycol having hydroxylic chain ends and an average molecular weight of 200 to 6,000, said reaction being carried out under high vacuum at a temperature between 100° and 400° C. in the presence of a catalyst comprising a tetra-alkylortho-titanate having the formula Ti(OR) 4 , wherein R is a linear or branched aliphatic hydrocarbon radical having from 1 to 24 carbon atoms, the amount of said catalyst with respect to the reactive mixture is between 0.01 and 5% by weight.
Claim 3
Dependent Claim
38 words
The polyether-ester-amide of claim 1 wherein the lactam or amino acid having a hydrocarbon chain of 4 to 14 carbon atoms is selected from the group consisting of caprolactam, oenantholactam, dodecalactam, undecanolactam, dodecanolactam, 11-amino-undecanoic acid, and 12-aminododecanoic acid.
Claim 4
Dependent Claim
38 words
The polyether-ester-amide of claim 1 wherein the polyamide is formed from a dicarboxylic acid and diamine wherein the diamine is hexamethylene diamine or nonamethylene diamine and the acid is adipic acid, azelaic acid, sebacic acid, or 1,12-dodecanedioic acid.
Claim 5
Dependent Claim
36 words
The polyether-ester-amide of claim 1 wherein the polyamide sequence is formed from a carboxylic acid selected from the group consisting of succinic acid, adipic acid, suberic acid, azelaic acid, sebacic acid, undecanedioic acid and dodecanedioic acid.
Claim 6
Dependent Claim
29 words
The polyether-ester-amide of claim 1 wherein the polyoxyalkylene glycol is selected from the group consisting of polyethylene glycol, polyoxypropylene glycol, polyoxytetramethylene glycol, mixtures thereof and a copolyether derived therefrom.
Claim 7
Dependent Claim
41 words
The polyether-ester-amide of claim 1 wherein the polyamide sequence is formed from an 11-dicarboxylic polyamide prepared by the polycondensation of 11-aminoundecanoic acid and adipic acid and the polyoxyalkylene glycol is polyoxyethylene glycol and the polyester-amide has an intrinsic viscosity of 1.2.
Claim 8
Dependent Claim
34 words
The polyether-ester-amide of claim 1 wherein the amide sequence is formed from the polycondensation product of 11-aminoundecanoic acid and adipic acid, and the polyalkylene glycol is polyoxyethylene glycol; wherein the intrinsic viscosity is 0.80.
Claim 9
Dependent Claim
35 words
The polyether-ester-amide of claim 1 wherein the polyamide sequence is formed from the condensation product of 11-aminoundecanoic acid and adipic acid, and the polyoxyalkylene glycol is polyoxypropylene glycol; the viscosity of the polyester-amide is 1.5.
Claim 10
Dependent Claim
37 words
The polyether-ester-amide of claim 1 wherein the polyamide sequence is formed from condensation of 12-aminododecanoic acid and adipic acid and the polyoxyalkylene sequence is formed from polytetramethylene glycol, and the intrinsic viscosity of the polyether-ester-amide is 1.3.
Claim 11
Dependent Claim
31 words
The polyether-ester-amide of claim 1 wherein the polyamide sequence is obtained by the condensation of 11-aminoundecanoic acid in the presence of adipic acid and the polyalkylene glycol is copolyethylene glycolpolypropylene glycol.
Claim 12
Dependent Claim
12 words
An extruded product consisting of essentially of the polyether-esteramide of claim 1.
References Cited (Backward Citations)
US3265762A
Cited
US3549724A
Cited
US3636135A
Cited
US3660356A
Cited
US3766146A
Cited
US3839245A
Cited
US3862262A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-28 | 1984-04-28 | 1984-10-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-28 | 1988-04-28 | 1988-10-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-28 | 1992-04-28 | 1992-10-28 | $7700.00 | Window Closed / Lapsed |