Catheter made of a thermoplastic material having improved softness and low friction
Assignee: Allegiance Corp
•
Filing: 1978-04-28
•
Granted: 1980-04-22
•
Expires: 1998-04-28
Abstract
Abstract A catheter, preferably a balloon-type catheter, is disclosed in which the catheter shaft is made of a thermoplastic material and thus may be extrudable, the shaft consisting essentially of (a) from 40 to 70 percent by weight of an elastic composition which comprises: from 50 to 99.5 percent by weight of a block copolymer having thermoplastic rubber characteristics with a central, rubbery polyolefin block and terminal blocks of polystyrene, and optionally including up to about 45 percent by weight of polypropylene, plus from 0.5 to 10 percent by weight of a cross-linked organic silicone elastomer; and (b) from 30 to 60 percent by weight of a hydrophobic oil-type plasticizer to provide the desired degree of softness to said elastic composition.
Inventors
- 👤 Lawrence F. Becker
- 👤 Henry M. Gajewski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 11:45
CPC Classifications
A; A61; A61M; A61M25/00; A61M25/10; A61M25/1027; A61M25/1029; A61L; A61L29/00; A61L29/04; A61L29/041; A61L29/049; A61L29/14; A61L29/141; A61M25/1034; A61M25/1036
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
162 words
A catheter which comprises a tubular shaft, said shaft consisting essentially of (a) from 40 to 70 percent by weight of an elastic composition which comprises: from 50 to 99.5 percent by weight of a block copolymer having thermoplastic rubber characteristics with a central rubbery polyolefin block and terminal blocks of a polystyrene; said block copolymer exhibiting a Brookfield viscosity at 25° C. of 10 to 2000 cps., when measured using a 10 percent by weight solids solution in toluene, said composition including from 0 to 45 percent by weight of polypropylene, and from 0.5 to 10 percent by weight of a crosslinked, organic silicone elastomer which is the reaction product of an organopolysiloxane containing from one to five percent by weight of siloxane units which contain silicon-bonded vinyl groups, and an organopolysiloxane material containing silicon-bonded hydrogen; and (b) from 30 to 60 percent by weight of a hydrophobic oil-type plasticizer to provide the desired degree of softness to said elastic composition.
Claim 2
Dependent Claim
162 words
A catheter which comprises a tubular shaft, said shaft consisting essentially of (a) from 40 to 70 percent by weight of an elastic composition which comprises: from 50 to 99.5 percent by weight of a block copolymer having thermoplastic rubber characteristics with a central rubbery polyolefin block and terminal blocks of a polystyrene; said block copolymer exhibiting a Brookfield viscosity at 25° C. of 10 to 2000 cps., when measured using a 10 percent by weight solids solution in toluene, said composition including from 0 to 45 percent by weight of polypropylene, and from 0.5 to 10 percent by weight of a crosslinked, organic silicone elastomer which is the reaction product of an organopolysiloxane containing from one to five percent by weight of siloxane units which contain silicon-bonded vinyl groups, and an organopolysiloxane material containing silicon-bonded hydrogen; and (b) from 30 to 60 percent by weight of a hydrophobic oil-type plasticizer to provide the desired degree of softness to said elastic composition.
Claim 3
Dependent Claim
34 words
The catheter of claim 1 in which said shaft consists essentially of 55 to 65 percent by weight of said elastic composition and 35 to 45 percent by weight of said hydrophobic oil-type plasticizer.
Claim 4
Dependent Claim
56 words
The catheter of claim 1, in which said elastic composition also includes from 0.5 to 3 percent by weight of a fatty acid amide having an average of 16 to 50 carbon atoms per molecule, whereby the combination of the cured silicone elastomer and fatty acid amide ingredient provides the catheter with substantially reduced surface friction.
Claim 5
Dependent Claim
41 words
The catheter of claim 1 in which said organic silicone elastomer is the reaction product of a dimethylpolysiloxane containing from 1 to 5 percent by weight of siloxane units which contain silicon-bonded vinyl groups, and a methylpolysiloxane material containing silicon-bonded hydrogen.
Claim 6
Dependent Claim
36 words
The catheter of claim 1 in which the formulation for said shaft contains from 1 to 10 percent by weight of polypropylene having a melt flow of essentially 50 to 100, as tested under ASTM D1238-70.
Claim 7
Dependent Claim
15 words
The catheter of claim 1 which carries an inflatable balloon member sealed on said shaft.
Claim 8
Dependent Claim
25 words
The balloon-type catheter of claim 6 in which said block copolymer of the shaft and balloon member has a central, rubbery polyolefin block of poly(ethylene-butylene).
Claim 9
Dependent Claim
155 words
A plastic formulation which comprises (a) from 50 to 70 percent by weight of an elastic combination which comprises: 50 to 99.5 percent by weight of a block copolymer having thermoplastic rubbery characteristics with a central rubbery polyolefin block and terminal blocks of a polystyrene; said block copolymer exhibiting a Brookfield viscosity at 25° C. of 10 to 2000 cps. when measured using a 10 percent by weight solids solution in toluene, said composition including from 0 to 45 percent by weight of polypropylene, and from 0.5 to 5 percent by weight of a crosslinked organic silicone elastomer which is the reaction product of an organopolysiloxane containing from one to five percent by weight of siloxane units which contain silicon-bonded vinyl groups, and a methyl polysiloxane material containing silicon-bonded hydrogen; and (b) from 30 to 50 percent by weight of a hydrophobic oil-type plasticizer to provide the desired degree of softness to said elastic composition.
Claim 10
Dependent Claim
155 words
A plastic formulation which comprises (a) from 50 to 70 percent by weight of an elastic combination which comprises: 50 to 99.5 percent by weight of a block copolymer having thermoplastic rubbery characteristics with a central rubbery polyolefin block and terminal blocks of a polystyrene; said block copolymer exhibiting a Brookfield viscosity at 25° C. of 10 to 2000 cps. when measured using a 10 percent by weight solids solution in toluene, said composition including from 0 to 45 percent by weight of polypropylene, and from 0.5 to 5 percent by weight of a crosslinked organic silicone elastomer which is the reaction product of an organopolysiloxane containing from one to five percent by weight of siloxane units which contain silicon-bonded vinyl groups, and a methyl polysiloxane material containing silicon-bonded hydrogen; and (b) from 30 to 50 percent by weight of a hydrophobic oil-type plasticizer to provide the desired degree of softness to said elastic composition.
Claim 11
Dependent Claim
32 words
The composition of claim 8 in which from 55 to 65 percent by weight of said elastic composition and 35 to 45 percent by weight of said hydrophobic oil-type plasticizer are present.
Claim 12
Dependent Claim
52 words
The composition of claim 8 which also includes from 0.5 to 3 percent by weight of a fatty acid amide having an average of 16 to 50 carbon atoms per molecule, whereby the combination of the cured silicone elastomer and fatty acid amide ingredient provides the catheter with substantially reduced surface friction.
Claim 13
Dependent Claim
41 words
The composition of claim 8 in which said organic silicone elastomer is the reaction product of a dimethylpolysiloxane containing from 1 to 5 percent by weight of siloxane units which contain silicon-bonded vinyl groups, and a methylpolysiloxane material containing silicon-bonded hydrogen.
Claim 14
Dependent Claim
33 words
The catheter of claim 8 in which said composition contains from 1 to 10 percent by weight of polypropylene having a melt flow of essentially 50 to 100 as tested under ASTM D1238-70.
Claim 15
Dependent Claim
18 words
The composition of claim 8 in which said block copolymer has a central, rubbery polyolefin block of poly(ethylene-butylene).
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-22 | 1983-10-22 | 1984-04-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-22 | 1987-10-22 | 1988-04-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-22 | 1991-10-22 | 1992-04-22 | $7700.00 | Window Closed / Lapsed |