Oxidation resistant barrier coated copper based substrate and method for producing the same
Assignee: 555794 ONTARIO Inc
•
Filing: 1978-06-22
•
Granted: 1980-02-19
•
Expires: 1998-06-22
Abstract
Abstract Copper based substrates for use at high temperatures in oxidizing atmospheres are made up of a copper core overlaid with a protective nickel oxide barrier layer formed in situ and an external protective layer of nickel. The process for forming the protective nickel oxide barrier layer comprises the steps of subjecting the copper core to oxidation to form a cuprous oxide surface layer over the copper core, reducing the surface of the cuprous oxide layer to regenerate copper to regain conductivity, plating a surface layer of nickel over the copper layer, and annealing the coated copper core to scavenge at least some of the oxygen from the cuprous oxide layer and react it at the interface with the plated nickel layer to form the protective nickel oxide barrier layer. The oxidation reduction steps may be carried continuously on a copper core which is moved through a reactor having an oxidation zone fed with oxygen, a reduction zone fed with hydrogen and a stabilizer zone separating the oxidation and reduction zones and fed with an inert gas. The reactor is maintained at a temperature such as to allow the oxidation and reduction reactions.
Inventors
- 👤 Clermont A. Roy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 14:56
CPC Classifications
C; C23; C23C; C23C26/00; Y; Y10; Y10T; Y10T428/00; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/294; Y10T428/2942; Y10T428/2944
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
37 words
A copper substrate comprising a copper core, a protective nickel oxide barrier formed in situ directly in contact with the copper core and a protective layer of nickel directly in contact with the nickel oxide barrier layer.
Claim 2
Dependent Claim
37 words
A copper substrate comprising a copper core, a protective nickel oxide barrier formed in situ directly in contact with the copper core and a protective layer of nickel directly in contact with the nickel oxide barrier layer.
Claim 3
Dependent Claim
23 words
A copper substrate as defined in claim 1, wherein the nickel oxide barrier layer is between 1.2 microns and 6 microns in thickness.
Claim 4
Dependent Claim
23 words
A copper substrate as defined in claim 1, wherein the protective layer of nickel is between 2 microns and 24 microns in thickness.
Claim 5
Dependent Claim
20 words
A copper substrate as defined in claim 3, wherein the protective layer of nickel is about 18 microns in thickness.
Claim 6
Dependent Claim
100 words
A process for forming a protective nickel oxide barrier layer over a copper core comprising the steps of: (a) subjecting the copper core to oxidation to form a cuprous oxide surface layer over the copper core; (b) reducing the surface of the cuprous oxide layer to regenerate copper to regain electrical conductivity; (c) plating a surface layer of nickel over the free copper layer; and (d) annealing the coated copper wire to scavenge at least some of the oxygen from the cuprous oxide layer and react it with the plated nickel layer to form the protective nickel oxide barrier layer.
Claim 7
Dependent Claim
100 words
A process for forming a protective nickel oxide barrier layer over a copper core comprising the steps of: (a) subjecting the copper core to oxidation to form a cuprous oxide surface layer over the copper core; (b) reducing the surface of the cuprous oxide layer to regenerate copper to regain electrical conductivity; (c) plating a surface layer of nickel over the free copper layer; and (d) annealing the coated copper wire to scavenge at least some of the oxygen from the cuprous oxide layer and react it with the plated nickel layer to form the protective nickel oxide barrier layer.
Claim 8
Dependent Claim
63 words
A process as defined in claim 5, wherein the oxidation/reduction steps are carried out continuously on a copper core which is moved at a speed between 5 and 10 cm/min through a reactor having an oxidation zone fed with oxygen, a reduction zone fed with hydrogen and a stabilizer zone separating said oxidation and reduction zones which is fed with an inert gas.
Claim 9
Dependent Claim
49 words
A process as defined in claim 6, wherein oxidation is carried out at a temperature between 755° C. and 1000° C., with an oxygen flow through the oxidation zone between 1 cc/min and 6 cc/min to produce a cuprous oxide layer between 6 microns and 10 microns in thickness.
Claim 10
Dependent Claim
41 words
A process as defined in claim 7, wherein oxidation is carried out at a temperature between 750° C. and 1000° C. with an oxygen flow of about 2 cc/min to produce a cuprous oxide layer of about 8 microns in thickness.
Claim 11
Dependent Claim
58 words
A process as defined in claim 6, wherein reduction is carried out in the reduction zone at a temperature between 500° C. and 1000° C., with an hydrogen flow through the reduction zone between 0.6 cc/min and 1.5 cc/min to produce a free copper layer between 0.7 microns and 1.5 microns in thickness over the cuprous oxide layer.
Claim 12
Dependent Claim
44 words
A process as defined in claim 9, wherein reduction is carried out at a temperature between 700° C. and 1000° C., with an hydrogen flow of about 0.85 cc/min to produce a regenerated copper layer of about 1.2 microns over the cuprous oxide layer.
Claim 13
Dependent Claim
30 words
A process as defined in claim 6, wherein an inert gas is mixed with the oxygen and hydrogen to provide a total pressure equal to or slightly above atmospheric pressure.
Claim 14
Dependent Claim
30 words
A process as defined in claim 6, wherein the inert gas flow to the oxidation and reduction zones is about 300 cc/min and to the stabilizer zone about 500 cc/min.
Claim 15
Dependent Claim
18 words
A process as defined in claim 6, wherein the bath is air agitated and maintained under continuous filtration.
Claim 16
Dependent Claim
19 words
A process as defined in claim 5, wherein the nickel plate layer is between 2 microns and 30 microns.
Claim 17
Dependent Claim
72 words
A process as defined in claim 14, wherein the nickel plate layer is applied from an electrolytic Watts bath composed of nickel chloride, nickel sulphate and boric acid in solution in water, the plating current density being between 0.2 amp/cm 2 and 0.32 amp/cm 2 with voltage values between 6 volts to 12 volts, the bath pH being between 3.5 and 4.5 and the bath temperature between 55° C. and 65° C.
Claim 18
Dependent Claim
22 words
A process as defined in claim 5, wherein the annealing step is carried out in air or under inert gas or vacuum.
Claim 19
Dependent Claim
88 words
A process as defined in claim 16, wherein annealing includes a first initial heat treatment of from 6 to 1.5 days at between 100° C. and 200° C., a second heat treatment step from about 200° C. to about 400° C. over a period of 12 to 24 hrs followed by a rise in temperature between 400° C. and 1000° C. over a period of from 5 hrs to 1.5 hrs, and finally a third cooling step down to room temperature lasting between 1 hr and 0.2 hr.
Claim 20
Dependent Claim
78 words
A process as defined in claim 16, wherein annealing includes a first initial heat treatment of about 2 days at about 200° C., a second heat treatment step from about 200° C. to about 400° C. over a period of about 24 hrs followed by a rise in temperature between 400° C. and 1000° C. over a period of about 1 hr and a third cooling step down to ambient temperature over a period of about 0.5 hr.
Claim 21
Dependent Claim
40 words
A process as defined in claims 17 or 18 wherein the third step is initiated immediately upon achieving a temperature in the range of 400° C. to 1000° C. which results in initiation of nucleation of the nickel oxide barrier.
Claim 22
Dependent Claim
29 words
A process as defined in claims 17 or 18, wherein the high temperature treatment is continued for several hours to develop or complete the formation of the NiO barrier.
Claim 23
Dependent Claim
60 words
A copper substrate comprising a copper core, a cuprous oxide layer directly in contact with the copper core, a copper layer directly in contact with the cuprous oxide layer, a protective nickel oxide barrier layer formed in situ directly in contact with the copper layer and a protective layer of nickel directly in contact with the nickel oxide barrier layer.
Claim 24
Dependent Claim
60 words
A copper substrate comprising a copper core, a cuprous oxide layer directly in contact with the copper core, a copper layer directly in contact with the cuprous oxide layer, a protective nickel oxide barrier layer formed in situ directly in contact with the copper layer and a protective layer of nickel directly in contact with the nickel oxide barrier layer.
Claim 25
Dependent Claim
23 words
The copper substrate as defined in claim 21, wherein the nickel oxide barrier layer is between 1.2 microns and 6 microns in thickness.
Claim 26
Dependent Claim
23 words
A copper substrate as defined in claim 21, wherein the protective layer of nickel is between 2 microns and 24 microns in thickness.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-02-18 | 1983-08-20 | 1984-02-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-02-18 | 1987-08-20 | 1988-02-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-02-18 | 1991-08-20 | 1992-02-19 | $7700.00 | Window Closed / Lapsed |