Abstract
Abstract A process for the production of tiles made of ceramic material and having substantially planar front and back faces, comprising the steps of advancing a raw tile based on "clay material", with the term having the meaning as set forth in the description, dried and covered on one face with the glaze, which is also dried, in a heat treatment chamber with both faces at least substantially exposed to direct transmission of heat by convection, the tile in the heat treatment chamber going through a first fast heating phase until it reaches a temperature slightly lower than maximum firing temperature, and through a successive firing phase during which it is kept at a range of temperatures between the final heating temperature and the maximum firing temperature, the tile finally being cooled.
Inventors
- 👤 Pietro Marazzi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 17:37
CPC Classifications
C; C04; C04B; C04B33/00; C04B33/32; C04B33/34
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
307 words
A process for the production of ceramic tiles, each having a front face and a rear face, comprising the steps of preparing a raw tile consisting of a dry, unfired tile body with a dried glaze coating on one face of the body, and with the body consisting predominantly of clay and containing more than 40% by weight of raw clay, an aggregate calcium oxide and magnesium oxide content of less than 30% by weight and aluminum oxide content of less than 30% by weight wherein said raw clay is free of amounts of talcum and wollastonite exceeding 50% by weight, and an iron oxide content of less than 10% by weight; advancing the raw tile at a speed of the order of 1.5-2 meters per minute through a heat treatment chamber; in a heating step having a duration of 4-8, minutes, contacting both faces of the tile body concurrently with flowing hot gases as the tile body advances through the treatment chamber to raise both faces concurrently and, by substantially only direct convection heating, substantially to firing surface temperature; in a subsequent firing step having a duration of 11-20 minutes, contacting both faces of the tile body concurrently with the flowing hot gases as the tile body continues to be advanced through the treatment chamber to maintain both surfaces substantially at the firing surface temperature concurrently, by substantially only direct convection heating, to fire the tile body and the glaze of the raw tile; and, following completion of the firing step, finally cooling the fired tile in a cooling step having a duration slightly shorter than that of the firing step; whereby the sum of the duration of the heating and firing steps is not in excess of about 28 minutes and the overall heating, firing, and cooling time is not in excess of 48 minutes.
Claim 2
Dependent Claim
307 words
A process for the production of ceramic tiles, each having a front face and a rear face, comprising the steps of preparing a raw tile consisting of a dry, unfired tile body with a dried glaze coating on one face of the body, and with the body consisting predominantly of clay and containing more than 40% by weight of raw clay, an aggregate calcium oxide and magnesium oxide content of less than 30% by weight and aluminum oxide content of less than 30% by weight wherein said raw clay is free of amounts of talcum and wollastonite exceeding 50% by weight, and an iron oxide content of less than 10% by weight; advancing the raw tile at a speed of the order of 1.5-2 meters per minute through a heat treatment chamber; in a heating step having a duration of 4-8, minutes, contacting both faces of the tile body concurrently with flowing hot gases as the tile body advances through the treatment chamber to raise both faces concurrently and, by substantially only direct convection heating, substantially to firing surface temperature; in a subsequent firing step having a duration of 11-20 minutes, contacting both faces of the tile body concurrently with the flowing hot gases as the tile body continues to be advanced through the treatment chamber to maintain both surfaces substantially at the firing surface temperature concurrently, by substantially only direct convection heating, to fire the tile body and the glaze of the raw tile; and, following completion of the firing step, finally cooling the fired tile in a cooling step having a duration slightly shorter than that of the firing step; whereby the sum of the duration of the heating and firing steps is not in excess of about 28 minutes and the overall heating, firing, and cooling time is not in excess of 48 minutes.
Claim 3
Dependent Claim
25 words
A process as claimed in claim 1, wherein the clay includes calcium and magnesium oxides in a total amount substantially not exceeding 20% by weight.
Claim 4
Dependent Claim
22 words
A process as claimed in claim 1, wherein the clay comprises aluminum oxide in an amount substantially not exceeding 20% by weight.
Claim 5
Dependent Claim
40 words
A process as claimed in claim 1, wherein the clay includes the following components: SiO 2 55-70%, Al 2 O 3 15-20%, Fe 2 O 3 2-8%, CaO 1-10%, MgO 1-10%, K 2 O 1-6%, and Na 2 O 1-5%.
Claim 6
Dependent Claim
21 words
A process as claimed in claim 1, wherein the clay has a total weight loss not exceeding 15% under process conditions.
Claim 7
Dependent Claim
73 words
A process as claimed in claim 1, in which the heating step has a duration time of about 4-6 minutes and the firing step has a duration time of about 11-15 minutes, for tiles 4-5 mm thick, and, for tiles thicker than 4-5 mm, the heating step and firing step duration times are increased, but to a value less than that proportional to the increased thickness of such tiles thicker than 4-5 mm.
Claim 8
Dependent Claim
66 words
A process as claimed in claim 1, wherein one speed of movement of the tiles through the treatment chamber is maintained at 1.5-2 meters/minute, for tiles 4-5 mm thick, and, for tiles thicker than 4-5 mm, the speed of the tiles through the treatment chamber is reduced, but to a magnitude greater than that proportional to the increased thickness of such tiles thicker than 4-5 mm.
Claim 9
Dependent Claim
24 words
A process as claimed in claim 1, in which the iron oxide in the dry, unfired tile body is not in excess of 8%.
Claim 10
Dependent Claim
57 words
A process as claimed in claim 1, including the step of supporting and advancing each raw tile through the treatment chamber by spaced rotating cylindrical supporting surfaces having a spacing such that each raw tile is continuously supported on at least two, and no more than three, successive cylindrical supporting surfaces while traveling through the treatment chamber.
Claim 11
Dependent Claim
58 words
A process as claimed in claim 1, including drying the clay by flowing hot gases immediately prior to heating the raw tile and the glaze in the treatment chamber while advancing the raw tile and the glaze, during such drying, at the same speed as the raw tile and the glaze is later advanced through the treatment chamber.
Claim 12
Dependent Claim
17 words
A process as claimed in claim 10, wherein the drying of the glaze lasts about 5-7 minutes.
Claim 13
Dependent Claim
30 words
A process as claimed in claim 1, in which firing of the tile is effected at a temperature of 800°-1200° C. as measured in the treatment chamber near the tile.
Claim 14
Dependent Claim
21 words
A process as claimed in claim 12, wherein firing of the tile is effected at a temperature of 1,000° C.-1,100° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-14 | 1983-07-16 | 1984-01-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-14 | 1987-07-16 | 1988-01-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-14 | 1991-07-16 | 1992-01-15 | $7700.00 | Window Closed / Lapsed |