Acrylic-type pressure sensitive adhesives by means of ultraviolet radiation curing

Claim 2

A process for the preparation of a normally tacky pressure-sensitive adhesive comprising subjecting a suitable mass of a radiation-sensitized solventless liquid mixture containing as a major proportion thereof at least one acrylic acid ester of an alkyl alcohol, said alcohol containing from 4 to 14 carbon atoms, and at least one monomer copolymerizable therewith to radiation in the near ultraviolet region at a rate or irradiation in the 3000-4000 A wavelength range of not more than 7 milliwatts per square centimeter of the mass exposed, said radiation allowably also containing incidental radiation energy, the amount of said incidental radiation energy having wavelengths shorter than 3000 A being limited to not more than about 10% of the amount of energy in the 3000-4000 A range.

Claim 3

A process for the preparation of a normally tacky pressure-sensitive adhesive comprising subjecting a suitable mass of up to about 1.9 centimeters thickness of a radiation-sensitized solventless liquid mixture containing as a major proportion thereof at least one acrylic acid ester of an alkyl alcohol, said alcohol containing from 4 to 14 carbon atoms, and at least one monomer copolymerizable therewith to radiation in the near ultraviolet region at a rate of irradiation in the 3000-4000 A wavelength range of from 0.1 to 7 milliwatts per square centimeter of the mass exposed, said radiation allowably also containing incidental radiation energy, the amount of said incidental radiation energy having wavelengths shorter than 3000 A being limited to not more than about 10% of the amount of energy in the 3000-4000 A range, until at least about 95% of the monomer present in the mass has been polymerized, whereby a tacky, flexible pressure-sensitive adhesive having peel adhesion to glass greater than about 0.8 kilograms per centimeter and shear strength greater than 50 minutes is formed.

Claim 4

A process for the preparation of a normally tacky pressure-sensitive adhesive comprising subjecting a suitable mass of up to about 1.9 centimeters thickness of a radiation-sensitized solventless liquid mixture containing as a major proportion thereof at least one acrylic acid ester of an alkyl alcohol, said alcohol containing from 4 to 14 carbon atoms, and at least one monomer copolymerizable therewith to radiation in the near ultraviolet region at a rate of irradiation in the 3000-4000 A wavelength range of from 0.1 to 7 milliwatts per square centimeter of the mass exposed, said radiation allowably also containing incidental radiation energy, the amount of said incidental radiation energy having wavelengths shorter than 3000 A being limited to not more than about 10% of the amount of energy in the 3000-4000 A range, until at least about 95% of the monomer present in the mass has been polymerized, whereby a tacky, flexible pressure-sensitive adhesive having peel adhesion to glass greater than about 0.8 kilograms per centimeter and shear strength greater than 50 minutes is formed.

Claim 5

A process for the preparation of a normally tacky pressure-sensitive adhesive comprising the steps of (1) preparing a suitably radiation-sensitized, solventless, liquid mixture comprising (a) 70-98 parts of units of at least one alkyl acrylate of which the alkyl group contains from 4 to 14 carbon atoms and (b) 2-30 parts of units of at least one modifying monomer copolymerizable therewith the sum of (a) and (b) amounting to 100 parts by weight, and (c) 0.01-5 parts of a photoinitiator, and (2) subjecting the mixture in a mass having a thickness of not more than about 1.9 cm. to radiation having wave lengths of 3000-4000 A at a rate of irradiation of from 0.1 to 7 milliwatts per square centimeter of the mass exposed, said radiation allowably also containing incidental radiation energy, the amount of said incidental radiation energy having wave lengths shorter than 3000 A being limited to not more than about 10% of the amount of energy in the 3000-4000 A range, until at least about 95% of the monomer has been polymerized, whereby a tacky, flexible pressure-sensitive adhesive having peel adhesion to glass greater than about 0.8 kilograms per centimeter and shear strength greater than 50 minutes is formed.

Claim 6

A process for the preparation of a normally tacky pressure-sensitive adhesive comprising the steps of (1) preparing a suitably radiation-sensitized, solventless, liquid mixture comprising (a) 70-98 parts of units of at least one alkyl acrylate of which the alkyl group contains from 4 to 14 carbon atoms and (b) 2-30 parts of units of at least one modifying monomer copolymerizable therewith the sum of (a) and (b) amounting to 100 parts by weight, and (c) 0.01-5 parts of a photoinitiator, and (2) subjecting the mixture in a mass having a thickness of not more than about 1.9 cm. to radiation having wave lengths of 3000-4000 A at a rate of irradiation of from 0.1 to 7 milliwatts per square centimeter of the mass exposed, said radiation allowably also containing incidental radiation energy, the amount of said incidental radiation energy having wave lengths shorter than 3000 A being limited to not more than about 10% of the amount of energy in the 3000-4000 A range, until at least about 95% of the monomer has been polymerized, whereby a tacky, flexible pressure-sensitive adhesive having peel adhesion to glass greater than about 0.8 kilograms per centimeter and shear strength greater than 50 minutes is formed.

Claim 7

A process according to claim 3 wherein the mixture contains 85-92 parts of (a) and 8-15 parts of (b), the sum of the two being 100 parts by weight.

Claim 8

A process according to claim 3 wherein the modifying monomer is acrylic acid.

Claim 9

A process for the manufacture of a pressure-sensitive adhesive tape comprising (1) coating a flexible tape backing with up to about 125 micron layer of a viscous suitably radiation-sensitized solventless syrup containing at least one acrylic acid ester of an alkyl alcohol, said alcohol containing from 4 to 14 carbon atoms, and at least one monomer copolymerizable therewith, (2) subjecting the layer to radiation in the near ultraviolet region at a rate of irradiation of 3000-4000 A wavelength of not more than 7 milliwatts per square centimeter of the layer exposed, said radiation allowably also containing incidental radiation energy, the amount of said incidental radiation energy having wavelengths shorter than 3000 A being limited to not more than about 10% of the amount of energy in the 3000-4000 A range.

Claim 10

A process for the manufacture of a pressure-sensitive adhesive tape comprising (1) coating a flexible tape backing with up to about 125 micron layer of a viscous suitably radiation-sensitized solventless syrup containing at least one acrylic acid ester of an alkyl alcohol, said alcohol containing from 4 to 14 carbon atoms, and at least one monomer copolymerizable therewith, (2) subjecting the layer to radiation in the near ultraviolet region at a rate of irradiation of 3000-4000 A wavelength of not more than 7 milliwatts per square centimeter of the layer exposed, said radiation allowably also containing incidental radiation energy, the amount of said incidental radiation energy having wavelengths shorter than 3000 A being limited to not more than about 10% of the amount of energy in the 3000-4000 A range.

Claim 11

A process for the manufacture of a pressure-sensitive adhesive tape comprising (1) coating a flexible tape backing with up to about 125 micron layer of a viscous suitably radiation-sensitized solventless syrup containing at least one acrylic acid ester of an alkyl alcohol, said alcohol containing from 4 to 14 carbon atoms, and at least one monomer copolymerizable therewith, (2) subjecting the layer to radiation in the near ultraviolet region at a rate of irradiation of 3000-4000 A wave length of from 0.1 to 7 milliwatts per square centimeter of the layer exposed, said radiation allowably also containing incidental radiation energy, the amount of said incidental radiation energy having wave lengths shorter than 3000 A being limited to not more than about 10% of the amount of energy in the 3000-4000 A range, until at least about 95% of the monomer has been polymerized, whereby the syrup is converted to a tacky, flexible pressure-sensitive adhesive having peel adhesion to glass greater than about 0.8 kilograms per centimeter and shear strength greater than 50 minutes.

Claim 12

A process for the manufacture of a pressure-sensitive adhesive tape comprising (1) coating a flexible tape backing with up to about 125 micron layer of a viscous suitably radiation-sensitized solventless syrup containing at least one acrylic acid ester of an alkyl alcohol, said alcohol containing from 4 to 14 carbon atoms, and at least one monomer copolymerizable therewith, (2) subjecting the layer to radiation in the near ultraviolet region at a rate of irradiation of 3000-4000 A wave length of from 0.1 to 7 milliwatts per square centimeter of the layer exposed, said radiation allowably also containing incidental radiation energy, the amount of said incidental radiation energy having wave lengths shorter than 3000 A being limited to not more than about 10% of the amount of energy in the 3000-4000 A range, until at least about 95% of the monomer has been polymerized, whereby the syrup is converted to a tacky, flexible pressure-sensitive adhesive having peel adhesion to glass greater than about 0.8 kilograms per centimeter and shear strength greater than 50 minutes.

Claim 13

A process for the manufacture of a pressure-sensitive adhesive tape comprising (1) coating a flexible tape backing with up to about a 125 micron layer of a prepolymerized syrup of a suitably radiation-sensitized solventless mixture comprising (a) 70-98 parts of units of at least one alkyl acrylate of which the alkyl group contains from 4 to 14 carbon atoms and (b) 2-30 parts of units of at least one modifying monomer copolymerizable therewith the sum of (a) and (b) amounting to 100 parts by weight, and (c) 0.01-5 parts of a photoiniator, and (2) subjecting the layer to radiation in the near ultraviolet region at a rate of irradiation of 3000-4000 A wave length of from 0.1 to 7 milliwatts per square centimeter of the layer exposed, said radiation allowably also containing incidental radiation energy, the amount of said incidental radiation energy having wave lengths shorter than 3000 A being limited to not more than about 10% of the amount of energy in the 3000-4000 A range, until at least about 95% of the monomer has been polymerized, whereby the syrup is converted to a tacky, flexible pressure-sensitive adhesive having peel adhesion to glass greater than about 0.8 kilograms per centimeter and shear strength greater than 50 minutes.

Claim 14

A process for the manufacture of a pressure-sensitive adhesive tape comprising (1) coating a flexible tape backing with up to about a 125 micron layer of a prepolymerized syrup of a suitably radiation-sensitized solventless mixture comprising (a) 70-98 parts of units of at least one alkyl acrylate of which the alkyl group contains from 4 to 14 carbon atoms and (b) 2-30 parts of units of at least one modifying monomer copolymerizable therewith the sum of (a) and (b) amounting to 100 parts by weight, and (c) 0.01-5 parts of a photoiniator, and (2) subjecting the layer to radiation in the near ultraviolet region at a rate of irradiation of 3000-4000 A wave length of from 0.1 to 7 milliwatts per square centimeter of the layer exposed, said radiation allowably also containing incidental radiation energy, the amount of said incidental radiation energy having wave lengths shorter than 3000 A being limited to not more than about 10% of the amount of energy in the 3000-4000 A range, until at least about 95% of the monomer has been polymerized, whereby the syrup is converted to a tacky, flexible pressure-sensitive adhesive having peel adhesion to glass greater than about 0.8 kilograms per centimeter and shear strength greater than 50 minutes.

Claim 15

A process according to claim 8 wherein the mixture contains 85-92 parts of (a) and 8-15 parts of (b), the sum of the two being 100 parts by weight.

Claim 16

A process according to claim 8 wherein the modifying monomer is acrylic acid.

Claim 17

A process for the preparation of a normally tacky pressure-sensitive adhesive comprising (1) subjecting a suitable low viscosity liquid mixture of at least one acrylic acid ester of an alkyl alcohol, said alcohol containing from 4 to 14 carbon atoms and at least one monomer copolymerizable therewith to prepolymerizing conditions to form a relatively viscous syrup in which from about 5 to 10 percent of the monomers have been converted to polymer, (2) forming a radiation-sensitive means of up to about 1.9 centimeters thickness comprising the syrup, and (3) subjecting the mass to radiation in the near ultraviolet region at a rate of irradiation in the 3000-4000 A wavelength range of from 0.1 to 7 milliwatts per square centimeter of the mass exposed, said radiation allowably also containing incidental radiation energy, the amount of said incidental radiation energy having wavelengths shorter than 3000 A being limited to not more than about 10% of the amount of energy in the 3000-4000 A range, until at least about 95% of the monomer has been polymerized, whereby a tacky, flexible pressure-sensitive adhesive having peel adhesion to glass greater than about 0.8 kilograms per centimeter and shear strength greater than 50 minutes is formed.

Claim 18

A process for the preparation of a normally tacky pressure-sensitive adhesive comprising (1) subjecting a suitable low viscosity liquid mixture of at least one acrylic acid ester of an alkyl alcohol, said alcohol containing from 4 to 14 carbon atoms and at least one monomer copolymerizable therewith to prepolymerizing conditions to form a relatively viscous syrup in which from about 5 to 10 percent of the monomers have been converted to polymer, (2) forming a radiation-sensitive means of up to about 1.9 centimeters thickness comprising the syrup, and (3) subjecting the mass to radiation in the near ultraviolet region at a rate of irradiation in the 3000-4000 A wavelength range of from 0.1 to 7 milliwatts per square centimeter of the mass exposed, said radiation allowably also containing incidental radiation energy, the amount of said incidental radiation energy having wavelengths shorter than 3000 A being limited to not more than about 10% of the amount of energy in the 3000-4000 A range, until at least about 95% of the monomer has been polymerized, whereby a tacky, flexible pressure-sensitive adhesive having peel adhesion to glass greater than about 0.8 kilograms per centimeter and shear strength greater than 50 minutes is formed.

Claim 19

A process for the preparation of a normally tacky pressure-sensitive adhesive comprising (1) subjecting a suitable low viscosity liquid mixture comprising (a) 70-98 parts of at least one alkyl acrylate monomer of which the alkyl group contains from 4 to 14 carbon atoms and (b) 2-30 parts of at least one modifying monomer copolymerizable therewith the sum of (a) and (b) amounting to 100 parts by weight, to prepolymerizing conditions to form a relatively viscous syrup in which from about 5 to 10 percent of the monomers have been converted to polymer, (2) forming a radiation-sensitive mass of up to about 1.9 centimeters thickness comprising the syrup, and (3) subjecting the mass to radiation in the near ultraviolet region at a rate of irradiation in the 3000-4000 A wavelength range of from 0.1 to 7 milliwatts per square centimeter of the mass exposed, said radiation allowably also containing incidental radiation energy, the amount of said incidental radiation energy having wave lengths shorter than 3000 A being limited to not more than about 10% of the amount of energy in the 3000-4000 A range, until at least about 95% of the monomer has been polymerized, whereby a tacky, flexible pressure-sensitive adhesive having peel adhesion to glass greater than about 0.8 kilograms per centimeter and shear strength greater than 50 minutes is formed.

Claim 20

A process for the preparation of a normally tacky pressure-sensitive adhesive comprising (1) subjecting a suitable low viscosity liquid mixture comprising (a) 70-98 parts of at least one alkyl acrylate monomer of which the alkyl group contains from 4 to 14 carbon atoms and (b) 2-30 parts of at least one modifying monomer copolymerizable therewith the sum of (a) and (b) amounting to 100 parts by weight, to prepolymerizing conditions to form a relatively viscous syrup in which from about 5 to 10 percent of the monomers have been converted to polymer, (2) forming a radiation-sensitive mass of up to about 1.9 centimeters thickness comprising the syrup, and (3) subjecting the mass to radiation in the near ultraviolet region at a rate of irradiation in the 3000-4000 A wavelength range of from 0.1 to 7 milliwatts per square centimeter of the mass exposed, said radiation allowably also containing incidental radiation energy, the amount of said incidental radiation energy having wave lengths shorter than 3000 A being limited to not more than about 10% of the amount of energy in the 3000-4000 A range, until at least about 95% of the monomer has been polymerized, whereby a tacky, flexible pressure-sensitive adhesive having peel adhesion to glass greater than about 0.8 kilograms per centimeter and shear strength greater than 50 minutes is formed.