Abstract Hollow fibers of acrylonitrile polymers having water-permeability greater than 0.2 ml/cm 2 .min.atm and useful as an inexpensive superior ultrafilter, comprising (1) a porous layer or layers existing on the outer or/and inner sides of said hollow fibers, the average sizes of pores contained in said porous layer or layers and existing on each of assumptive cylindrical surfaces concentric with the central axis of said hollow fibers, having such a gradient that the average sizes of pores contained in the porous layer existing on the outer side become smaller toward the outer surface of said hollow fibers while the average sizes of pores contained in the porous layer existing on the inner side become smaller toward the inner surface of said hollow fibers, and (2) a reticulate porous layer adjacent to said porous layer or layers (1) and containing therein at least one succession of voids having diameters of at least 10-50 μ, are prepared by dissolving an acrylonitrile polymer in an aqueous solution of nitric acid of 65-95% by weight concentration and extruding the resulting spinning solution through a die for hollow fibers, into a coagulation bath containing water or an aqueous solution of nitric acid of 30% by weight or less concentration.
A method for producing gel-like hollow fibers of acrylonitrile polymers for use as ultrafilters which comprises (a) dissolving an acrylonitrile polymer containing at least 60% by weight of acrylonitrile units in an aqueous solution of 65-95% by weight nitric acid at a temperature of from 0° C. to -5° C. to prepare a spinning solution, (b) extruding in the substantial absence of stretching the resulting solution through spinneretts, each having a ring-form orifice, into a coagulation bath having a concentration of up to 30% by weight nitric acid and a temperature from 4°-50° C. and, while extruding, feeding a liquid as an internal coagulant into the central portion of the ring-form orifice to form hollow fibers having (1) an outer layer having a porous structure, (2) a middle layer having voids and (3) an inner layer having a porous structure, (c) subsequently washing the hollow fibers in the substantial absence of stretching, and (d) recovering the resulting gel-like hollow fibers.
Claim 2
Independent Claim
160 words
A method for producing gel-like hollow fibers of acrylonitrile polymers for use as ultrafilters which comprises (a) dissolving an acrylonitrile polymer containing at least 60% by weight of acrylonitrile units in an aqueous solution of 65-95% by weight nitric acid at a temperature of from 0° C. to -5° C. to prepare a spinning solution, (b) extruding in the substantial absence of stretching the resulting solution through spinneretts, each having a ring-form orifice, into a coagulation bath having a concentration of up to 30% by weight nitric acid and a temperature from 4°-50° C. and, while extruding, feeding a liquid as an internal coagulant into the central portion of the ring-form orifice to form hollow fibers having (1) an outer layer having a porous structure, (2) a middle layer having voids and (3) an inner layer having a porous structure, (c) subsequently washing the hollow fibers in the substantial absence of stretching, and (d) recovering the resulting gel-like hollow fibers.
Claim 3
Dependent Claim
26 words
The method according to claim 1 wherein nitric acid is present in the coagulation bath in a concentration in the range of from 0-20% by weight.