Mixture of hydroxypropylcellulose and poly(maleic anhydride/alkene-1) as a hydrocolloid gelling agent

Claim 2

A hydraulic fluid composition which comprises an aqueous solution containing (1) between about 0.05 and 5 weight percent, based on the weight of water, of a mixture of hydroxypropylcellulose (average M.S. between about 2 and 5) and maleic anhydride/alkene-1 copolymer as a gelling agent, wherein the alkene-1 contains between 2 and about 6 carbon atoms, the gelling agent components are in a relative ratio between about 95:5 and 5:95 weight percent, and the specific viscosity of the copolymer component is between about 0.1 and 10; and (2) between about 0.01 and 25 weight percent, based on the weight of gelling agent, of a breaker additive for subsequent reduction of solution viscosity.

Claim 3

A hydraulic fracturing fluid composition comprising (1) an aqueous medium; (2) between about 0.05 and 5 weight percent, based on the weight of water, of a synergistic viscosity mixture of hydroxypropylcellulose (average M.S. between about 2 and 5) and maleic anhydride/alkene-1 copolymer as a gelling agent, wherein the alkene-1 contains between 2 and about 6 carbon atoms, the gelling agent components are in a relative ratio between about 95:5 and 5:95 weight percent, and the specific viscosity of the copolymer component is between about 0.1 and 10; (3) between about 0.01 and 25 weight percent, based on the weight of gelling agent, of a breaker additive for subsequent autonomous reduction of the gelling properties of the mixture of hydroxypropylcellulose and maleic anhydride/alkene-1 copolymer; and (4) a propping agent.

Claim 4

A hydraulic fracturing fluid composition comprising (1) an aqueous medium; (2) between about 0.05 and 5 weight percent, based on the weight of water, of a synergistic viscosity mixture of hydroxypropylcellulose (average M.S. between about 2 and 5) and maleic anhydride/alkene-1 copolymer as a gelling agent, wherein the alkene-1 contains between 2 and about 6 carbon atoms, the gelling agent components are in a relative ratio between about 95:5 and 5:95 weight percent, and the specific viscosity of the copolymer component is between about 0.1 and 10; (3) between about 0.01 and 25 weight percent, based on the weight of gelling agent, of a breaker additive for subsequent autonomous reduction of the gelling properties of the mixture of hydroxypropylcellulose and maleic anhydride/alkene-1 copolymer; and (4) a propping agent.

Claim 5

A hydraulic fracturing fluid composition in accordance with claim 2 wherein the maleic anhydride/alkene-1 copolymer component in the gelling agent is maleic anhydride/isobutylene copolymer.

Claim 6

A hydraulic fracturing fluid composition in accordance with claim 2 wherein the breaker additive is an acid or ester compound.

Claim 7

A hydraulic fracturing fluid composition in accordance with claim 2 wherein the breaker additive is an oxidizing compound.

Claim 8

A hydraulic fracturing fluid composition in accordance with claim 2 wherein the propping agent is sand.

Claim 9

A thickened aqueous composition having a pH in the range of between about 6 and 11, and containing between about 0.05 and 5 weight percent, based on the weight of water, of a synergistic hydrocolloid mixture of hydroxypropylcellulose (average M.S. between about 2 to 5) and maleic anhydride/alkene-1 copolymer as a gelling agent, wherein the alkene-1 contains between 2 and about 6 carbon atoms, the gelling agent components are in a relative ratio between about 95:5 and 5:95 weight percent, and the specific viscosity of the copolymer component is between about 0.1 and 10.

Claim 10

A thickened aqueous composition having a pH in the range of between about 6 and 11, and containing between about 0.05 and 5 weight percent, based on the weight of water, of a synergistic hydrocolloid mixture of hydroxypropylcellulose (average M.S. between about 2 to 5) and maleic anhydride/alkene-1 copolymer as a gelling agent, wherein the alkene-1 contains between 2 and about 6 carbon atoms, the gelling agent components are in a relative ratio between about 95:5 and 5:95 weight percent, and the specific viscosity of the copolymer component is between about 0.1 and 10.

Claim 11

An aqueous composition in accordance with claim 7 wherein the hydroxypropylcellulose component in the gelling agent has a molecular weight of at least about 800,000.

Claim 12

An aqueous composition in accordance with claim 7 wherein the maleic anhydride/alkene-1 copolymer component in the gelling agent is maleic anhydride/isobutylene copolymer containing the copolymerized monomers in about an equimolar ratio.

Claim 13

An aqueous composition in accordance with claim 7 wherein the maleic anhydride/alkene-1 copolymer is a high molecular weight maleic anhydride/isobutylene copolymer having a specific viscosity of at least 2.5 as determined in a solution of one gram of copolymer in one hundred milliliters of MEK at 25° C.

Claim 14

A process for increasing the viscosity of an aqueous medium which comprises incorporating therein between about 0.05 and 5 weight percent, based on the weight of water, of a synergistic viscosity mixture of hydroxypropylcellulose (average M.S. between about 2 and 5) and maleic anhydride/alkene-1 copolymer as a gelling agent; wherein the alkene-1 contains between about 2 and 6 carbon atoms, the gelling agent components are in a relative ratio between about 95:5 and 5:95 weight percent, and the specific viscosity of the copolymer component is between about 0.1 and 10.

Claim 15

A process for increasing the viscosity of an aqueous medium which comprises incorporating therein between about 0.05 and 5 weight percent, based on the weight of water, of a synergistic viscosity mixture of hydroxypropylcellulose (average M.S. between about 2 and 5) and maleic anhydride/alkene-1 copolymer as a gelling agent; wherein the alkene-1 contains between about 2 and 6 carbon atoms, the gelling agent components are in a relative ratio between about 95:5 and 5:95 weight percent, and the specific viscosity of the copolymer component is between about 0.1 and 10.

Claim 16

A process in accordance with claim 11 wherein the maleic anhydride/alkene-1 component of the gelling agent is maleic anhydride/isobutylene copolymer.

Claim 17

A process in accordance with claim 11 wherein the incremental synergistic increase in viscosity is at least 100 percent greater than the calculated additive viscosity contributions of the hydroxypropylcellulose and maleic anhydride/alkene-1 components of the gelling agent.