Shaped press-forged normally frangible inorganic crystals
Assignee: Solon Technologies Inc
•
Filing: 1978-02-06
•
Granted: 1979-10-16
•
Expires: 1998-02-06
Abstract
Abstract A polycrystalline shaped article useful as a light-transmitting body or scintillation phosphor is formed from an essentially moncrystalline melt-grown macrocrystal ingot by pressing the ingot between opposed surfaces with no radial restraint, at a temperature below its melting point and under sufficient pressure to transform the ingot, in situ, into a fully dense, homogeneous, polycrystalline mass of unrestricted width.
Inventors
- 👤 King H. Rosette
- 👤 Herbert Packer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:29
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/10; G02B6/102; C; C30; C30B; C30B29/00; C30B29/10; C30B29/12; C30B33/00; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/29
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
65 words
A shaped, polycrystalline optical body of alkali metal halide or alkaline earth metal halide, composed of crystals oriented with axes in a radial direction, with the crystals in the center portion of said body having an average size substantially larger than the size of the crystals near the periphery thereof, said body having essentially the same optical properties as a single crystal of said halide.
Claim 2
Dependent Claim
65 words
A shaped, polycrystalline optical body of alkali metal halide or alkaline earth metal halide, composed of crystals oriented with axes in a radial direction, with the crystals in the center portion of said body having an average size substantially larger than the size of the crystals near the periphery thereof, said body having essentially the same optical properties as a single crystal of said halide.
Claim 3
Dependent Claim
78 words
A polycrystalline optical body consisting essentially of ionic crystallites selected from an alkali metal halide and an alkaline earth metal halide, said body having optical integrity essentially indistinguishable from that of the starting material, and said crystallites having radially diminishing grain size, the majority of individual crystallites having an orientation radially generally angularly disposed to the force direction said body having no axial grain orientation, and said body having greater strength than a single crystal of said halide.
Claim 4
Dependent Claim
78 words
A polycrystalline optical body consisting essentially of ionic crystallites selected from an alkali metal halide and an alkaline earth metal halide, said body having optical integrity essentially indistinguishable from that of the starting material, and said crystallites having radially diminishing grain size, the majority of individual crystallites having an orientation radially generally angularly disposed to the force direction said body having no axial grain orientation, and said body having greater strength than a single crystal of said halide.
Claim 5
Dependent Claim
30 words
The polycrystalline optical body of claim 2 wherein said optical body is derived from an optically integral polycrystalline extrudate of said single crystal of said halide which includes a dopand.
Claim 6
Dependent Claim
49 words
The polycrystalline optical body of claim 3 wherein said dopand is an element selected from Groups I, II, III, IV, V and VII of the Periodic Table, and said element is present in an amount in the range from about 1 part per million to about 10 mole percent.
Claim 7
Dependent Claim
13 words
The body of claim 2 forged from a melt-grown optically integral, macrocrystal ingot.
Claim 8
Dependent Claim
46 words
The body of claim 5 in which the ingot was press-forged between opposed spaced-apart surfaces to provide a deformation ratio of at least 1.5 without cleaving said macrocrystal at a temperature below its melting point but greater than one-half its melting point measured in degrees Centigrade.
Claim 9
Dependent Claim
21 words
The body of claim 6 in which said crystallites are present prior to contact of said body with any radial restraint.
Claim 10
Dependent Claim
38 words
The body of claim 5 comprising a window transparent to a laser beam, said window permitting the transmittance of said beam with less than 0.1 percent absorption, or no more absorption than is displayed by said melt-grown ingot.
Claim 11
Dependent Claim
18 words
The polycrystalline optical body of claim 8 wherein said melt-grown ingot of said ionic salt includes a dopand.
Claim 12
Dependent Claim
49 words
The polycrystalline optical body of claim 9 wherein said dopand is an element selected from Groups I, II, III, IV, V and VII of the Periodic Table, and said element is present in an amount in the range from about 1 part per million to about 10 mole percent.
Claim 13
Dependent Claim
18 words
The body of claim 7 which is transparent to ultraviolet radiation shorter than about 1 micron in wavelength.
Claim 14
Dependent Claim
69 words
A shaped, polycrystalline body of an alkali metal halide or alkaline earth metal halide transparent to wavelengths in the ultraviolet range and having a sharply defined scatter pattern for a laser beam, said body being composed of crystals oriented with axes in a radial direction, with crystals in the central portion of said body having an average size substantially larger than the size of crystals near said body's periphery.
Claim 15
Dependent Claim
69 words
A shaped, polycrystalline body of an alkali metal halide or alkaline earth metal halide transparent to wavelengths in the ultraviolet range and having a sharply defined scatter pattern for a laser beam, said body being composed of crystals oriented with axes in a radial direction, with crystals in the central portion of said body having an average size substantially larger than the size of crystals near said body's periphery.
References Cited (Backward Citations)
US3114601A
Cited
US3359066A
Cited
US3312759A
Cited
US3459503A
Cited
US3365271A
Cited
US3794704A
Cited
US4038201A
Cited
US3883214A
Cited
US3894795A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-15 | 1983-04-16 | 1983-10-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-15 | 1987-04-16 | 1987-10-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-15 | 1991-04-16 | 1991-10-16 | $7700.00 | Window Closed / Lapsed |