Simulated natural sponge based on hydrophilic polyurethane

Claim 1

A method for preparation of new improved hydrophilic crosslinked polyurethane foams which simulate natural sponges which comprises reacting a first component comprising isocyanate capped polyoxyethylene polyol having a reaction functionality greater than two, said polyol being substantially void of reactive hydroxy groups and having a molecular weight of from about 200 to about 20,000, with a second component comprising aqueous reactant, the ratio of moles H 2 O/moles NCO groups being about 6.5 to about 390 in said second and first components respectively, said aqueous reactant having dissolved therein a liquid defoaming agent and non-ionic surface-active agent, the non-ionic surface-active agent having a high hydrophilic/lipophilic balance in the range of about HLB 14 to about HLB 18, whereas the liquid defoaming agent has a low hydrophilic/lipophilic balance of about HLB 5.5 to about HLB 8, and wherein the concentration of the liquid defoaming agent in the aqueous water phase prior to the foaming reaction is from about 0.3% to about 3.0% by weight of the aqueous phase, and the concentration of the non-ionic surface-active agent in the aqueous water phase prior to the foaming reaction is from about 0.05% to about 0.3% by weight of the aqueous phase.

Claim 2

A method for preparation of new improved hydrophilic crosslinked polyurethane foams which simulate natural sponges which comprises reacting a first component comprising isocyanate capped polyoxyethylene polyol having a reaction functionality greater than two, said polyol being substantially void of reactive hydroxy groups and having a molecular weight of from about 200 to about 20,000, with a second component comprising aqueous reactant, the ratio of moles H 2 O/moles NCO groups being about 6.5 to about 390 in said second and first components respectively, said aqueous reactant having dissolved therein a liquid defoaming agent and non-ionic surface-active agent, the non-ionic surface-active agent having a high hydrophilic/lipophilic balance in the range of about HLB 14 to about HLB 18, whereas the liquid defoaming agent has a low hydrophilic/lipophilic balance of about HLB 5.5 to about HLB 8, and wherein the concentration of the liquid defoaming agent in the aqueous water phase prior to the foaming reaction is from about 0.3% to about 3.0% by weight of the aqueous phase, and the concentration of the non-ionic surface-active agent in the aqueous water phase prior to the foaming reaction is from about 0.05% to about 0.3% by weight of the aqueous phase.

Claim 6

A method for preparation of new improved hydrophilic crosslinked polyurethane foams which simulate natural sponges which comprises reacting a first component comprising isocyanate capped polyoxyethylene polyol having a reaction functionality equal to two, said polyol being substantially void of reactive hydroxy groups and having a molecular weight of from about 200 to about 20,000, a second component comprising aqueous reactant, said aqueous reactant having dissolved therein a liquid defoaming agent and a non-ionic surface-active agent and a third component comprising a crosslinking agent having a reaction functionality greater than two and selected from the group consisting of polyol, polyisocyanate, polythiol and polyamine, the ratio of moles H 2 O/moles NCO groups being about 6.5 to about 390 in said second and first components, respectively, the non-ionic surface-active agent having a high hydrophilic/lipophilic balance in the range of about HLB 14 to about HLB 18, whereas the liquid defoaming agent has a low hydrophilic/lyophilic balance of about HLB 5.5 to about HLB 8, and wherein the concentration of the liquid defoaming agent in the aqueous water phase prior to the foaming reaction is from about 0.3% to about 3.0% by weight of the aqueous phase, and the concentration of the non-ionic surface-active agent in the aqueous water phase prior to the foaming reaction is from about 0.05% to about 0.3% by weight of the aqueous phase.

Claim 7

A method for preparation of new improved hydrophilic crosslinked polyurethane foams which simulate natural sponges which comprises reacting a first component comprising isocyanate capped polyoxyethylene polyol having a reaction functionality equal to two, said polyol being substantially void of reactive hydroxy groups and having a molecular weight of from about 200 to about 20,000, a second component comprising aqueous reactant, said aqueous reactant having dissolved therein a liquid defoaming agent and a non-ionic surface-active agent and a third component comprising a crosslinking agent having a reaction functionality greater than two and selected from the group consisting of polyol, polyisocyanate, polythiol and polyamine, the ratio of moles H 2 O/moles NCO groups being about 6.5 to about 390 in said second and first components, respectively, the non-ionic surface-active agent having a high hydrophilic/lipophilic balance in the range of about HLB 14 to about HLB 18, whereas the liquid defoaming agent has a low hydrophilic/lyophilic balance of about HLB 5.5 to about HLB 8, and wherein the concentration of the liquid defoaming agent in the aqueous water phase prior to the foaming reaction is from about 0.3% to about 3.0% by weight of the aqueous phase, and the concentration of the non-ionic surface-active agent in the aqueous water phase prior to the foaming reaction is from about 0.05% to about 0.3% by weight of the aqueous phase.