Fire proofing compositions
Assignee: Nullifire Ltd
•
Filing: 1977-03-09
•
Granted: 1979-07-03
•
Expires: 1997-03-09
Abstract
Abstract Intumescent coating composition for use in the spray-coating of beams and other structural members to protect them against the effect of fire and containing an epoxy resin film-forming binder and melamine phosphate spumific agent, in a weight ratio of less than 7.5:1, are improved by the inclusion therein of 1 to 15 percent by weight of inorganic fibres having a silica content of less than about 50 percent by weight of an aluminium oxide content preferably greater than about 50 percent by weight.
Inventors
- 👤 John B. Lloyd-Lucas
- 👤 Christopher Lloyd-Lucas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 20:03
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/18; C09D5/185; C09D7/00; C09D7/40; C09D7/60; C09D7/61; C09D7/70; C08; C08K; C08K7/00; C08K7/02; C08K7/04; C08K7/08; Y; Y10; Y10S; Y10S260/00; Y10S260/24
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
83 words
An intumescent coating composition comprising a film-forming epoxy resin binder and a spumific agent in a weight ratio of less than 7.5:1 and, uniformably dispersed therethrough, from about 1 to about 15 percent by weight, based on the weight of the other components of the composition, of inorganic fibres having a silica content, expressed as SiO 2 , of less than 50 percent by weight, and an aluminum oxide content, expressed as Al 2 O 3 , of at least 13% by weight.
Claim 2
Dependent Claim
83 words
An intumescent coating composition comprising a film-forming epoxy resin binder and a spumific agent in a weight ratio of less than 7.5:1 and, uniformably dispersed therethrough, from about 1 to about 15 percent by weight, based on the weight of the other components of the composition, of inorganic fibres having a silica content, expressed as SiO 2 , of less than 50 percent by weight, and an aluminum oxide content, expressed as Al 2 O 3 , of at least 13% by weight.
Claim 3
Dependent Claim
24 words
A composition according to claim 1 wherein the spumific agent is melamine phosphate and the composition includes a curing agent for the epoxy resin.
Claim 4
Dependent Claim
27 words
A composition according to claim 2 wherein the inorganic fibres have a length of less than one millimeter and a diameter of not greater than 0.01 millimeters.
Claim 5
Dependent Claim
13 words
A composition according to claim 2, wherein the inorganic fibres are mineral fibres.
Claim 6
Dependent Claim
29 words
A composition according to claim 2 wherein the inorganic fibres have an aluminium oxide content, expressed as Al 2 O 3 , greater than about 50 percent by weight.
Claim 7
Dependent Claim
13 words
A composition according to claim 5 wherein the inorganic fibres are ceramic fibres.
Claim 8
Dependent Claim
31 words
A composition according to claim 6 wherein the fibres have an SiO 2 content of about 38 percent and an Al 2 O 3 content of about 62 percent by weight.
Claim 9
Dependent Claim
17 words
A composition according to claim 1 wherein the epoxy resin is a diglycidylether containing the grouping ##STR2##
Claim 10
Dependent Claim
15 words
A composition according to claim 8 wherein n has a value in the range 0-1.0.
Claim 11
Dependent Claim
41 words
A composition according to claim 2 wherein the portion of the melamine phosphate is replaced by an equivalent weight of melamine borate, the melamine borate being present to an extent not exceeding 20 percent by weight of the total melamine salt.
Claim 12
Dependent Claim
35 words
A composition according to claim 1 including a filler; the content by weight of the filler plus inorganic fibre being less than about 15 percent of the total weight of the components in the composition.
Claim 13
Dependent Claim
11 words
A composition according to claim 11 wherein the filler is cristobolite.
Claim 14
Dependent Claim
12 words
A composition according to claim 12 wherein the filler comprises glass micro-spheres.
Claim 15
Dependent Claim
86 words
An intumescent coating composition comprising an epoxy resin and a melamine phosphate in a weight ratio of less than 7.5:1 and containing, uniformly dispersed therethrough, from about 1 to about 15 percent by weight of inorganic fibres having a silica content expressed as SiO 2 of less than about 50 percent by weight, and an aluminum oxide content, expressed as Al 2 O 3 , of at least 13% by weight, said composition being capable of being cured by the addition of a curing agent thereto.
Claim 16
Dependent Claim
86 words
An intumescent coating composition comprising an epoxy resin and a melamine phosphate in a weight ratio of less than 7.5:1 and containing, uniformly dispersed therethrough, from about 1 to about 15 percent by weight of inorganic fibres having a silica content expressed as SiO 2 of less than about 50 percent by weight, and an aluminum oxide content, expressed as Al 2 O 3 , of at least 13% by weight, said composition being capable of being cured by the addition of a curing agent thereto.
Claim 17
Dependent Claim
13 words
A composition according to claim 14 wherein the inorganic fibres are mineral fibres.
Claim 18
Dependent Claim
38 words
A composition according to claim 15 wherein the fibres have an SiO 2 content of about 47.5 percent by weight and an aluminium oxide content, expressed as Al 2 O 3 , of about 13 percent by weight.
Claim 19
Dependent Claim
29 words
A composition according to claim 14 wherein the inorganic fibres have an aluminium oxide content, expressed as Al 2 O 3 , greater than about 50 percent by weight.
Claim 20
Dependent Claim
13 words
A composition according to claim 17 wherein the inorganic fibres are ceramic fibres.
Claim 21
Dependent Claim
31 words
A composition according to claim 18 wherein the fibres have an SiO 2 content of about 38 percent and an Al 2 O 3 content of about 62 percent by weight.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-07-02 | 1983-01-01 | 1983-07-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-07-02 | 1987-01-01 | 1987-07-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-07-02 | 1991-01-01 | 1991-07-03 | $7700.00 | Window Closed / Lapsed |