High strength, corrosion resistant tubular products and methods of making the same
Assignee: Latrobe Steel Co
•
Filing: 1977-04-11
•
Granted: 1979-04-24
•
Expires: 1997-04-11
Abstract
Abstract Tubular metal products and methods of making tubular metal products for use in sour gas wells, which are characterized by resistance to hydrogen sulfide embrittlement at temperatures up to about 600 DEG F., are provided based upon an alloy having the composition up to about 0.035% maximum carbon, up to about 0.15% maximum silicon, up to about 0.15% maximum manganese, up to about 0.010% maximum sulfur, up to about 0.015% maximum phosphorus, about 19.0% to about 21.0% chromium, about 33.0% up to 37.0% nickel, about 9.0% to about 10.5% molybdenum, up to about 1.00% titanium, up to about 0.015% boron, up to about 2% iron and the balance cobalt, said tubular product having been strengthened by explosive shock loading which may be followed by heat treatment to further strengthen the tubular product. A small amount of cold work between the explosive shock strengthening treatment and heat treatment may be used to control the size and shape of the product and provide additional strengthening if needed. This same practice may be applied to other alloys of the nickel-base, iron-nickel base, cobalt-nickel base, cobalt base and iron-nickel-cobalt base groups which are responsive to cold working to produce higher strengths and reduce sulfide stress cracking.
Inventors
- 👤 Ales Simkovich
- 👤 Leonard A. Pugliese
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-22 16:09
CPC Classifications
C; C22; C22C; C22C19/00; C22C19/07; C22F; C22F3/00; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49805; Y10T29/49806
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
126 words
A non-laminar tubular metal product for use in sour gas wells characterized by resistance to hydrogen sulfide embrittlement at temperatures up to about 600° F., the entire product consisting essentially of an alloy having the composition up to about 0.035% maximum carbon, up to about 0.15% maximum silicon, up to about 0.15% maximum manganese, up to about 0.010% maximum sulfur, up to about 0.015% maximum phosphorus, about 19.0% to about 21.0% chromium, about 33.0% up to 37.0% nickel, about 9.0% to about 10.5% molybdenum, up to about 1.0% titanium, up to about 0.015% boron, up to about 2% iron and the balance cobalt, said tubular product having been subject to explosive shock strengthening treatment to effect non-directional cold working of the entire body of the tube.
Claim 2
Dependent Claim
126 words
A non-laminar tubular metal product for use in sour gas wells characterized by resistance to hydrogen sulfide embrittlement at temperatures up to about 600° F., the entire product consisting essentially of an alloy having the composition up to about 0.035% maximum carbon, up to about 0.15% maximum silicon, up to about 0.15% maximum manganese, up to about 0.010% maximum sulfur, up to about 0.015% maximum phosphorus, about 19.0% to about 21.0% chromium, about 33.0% up to 37.0% nickel, about 9.0% to about 10.5% molybdenum, up to about 1.0% titanium, up to about 0.015% boron, up to about 2% iron and the balance cobalt, said tubular product having been subject to explosive shock strengthening treatment to effect non-directional cold working of the entire body of the tube.
Claim 3
Dependent Claim
18 words
A tubular metal product as claimed in claim 1 which has been heat treated after explosive shock strengthening.
Claim 4
Dependent Claim
89 words
A tubular metal product as claimed in claim 1 wherein the alloy composition is up to about 0.020% maximum carbon, lowest possible amount of silicon but not more than 0.15%, lowest possible amount of manganese but not more than 0.15%, lowest possible amount of sulfur but not more than 0.005%, lowest possible amount of phosphorus but not more than 0.010%, about 20.50% chromium, about 35.25% nickel, about 9.80% molybdenum, about 0.75% titanium, about 0.010% boron, lowest possible amount of iron but not more than 1% and the balance cobalt.
Claim 5
Dependent Claim
18 words
A tubular metal product as claimed in claim 3 which has been heat treated after explosive shock strengthening.
Claim 6
Dependent Claim
24 words
A tubular metal product as claimed in claim 1 wherein said product has been cold work strengthened by conventional means after explosive shock strengthening.
Claim 7
Dependent Claim
26 words
A tubular metal product as claimed in claim 2 wherein said product has been cold work strengthened after explosive shock strengthening and prior to heat treatment.
Claim 8
Dependent Claim
27 words
A tubular metal product as claimed in claim 5 wherein said product has been cold work strengthened sufficiently to improve product geometry or increase strength or both.
Claim 9
Dependent Claim
31 words
A tubular metal product as claimed in claim 1 wherein said product has been explosive shock strengthened at peak pressures in the range of about 250,000 to 1,500,000 p.s.i. peak pressure.
Claim 10
Dependent Claim
30 words
A tubular metal product as claimed in claim 1 wherein said product has been explosive shock strengthened at peak pressures in the range about 500,000 to 750,000 p.s.i. peak pressure.
Claim 11
Independent Claim
134 words
A method for producing a non-laminar tubular metal product suitable for use in sour gas wells and characterized by resistance to hydrogen sulfide embrittlement at temperatures up to about 600° F. comprising the steps of: (a) forming a non-laminar tubular metal member entirely from an alloy consisting essentially of up to about 0.035% maximum carbon, up to about 0.15% maximum silicon, up to about 0.15% maximum manganese, up to about 0.010% maximum sulfur, up to about 0.015% maximum phosphorus, about 19.0% to about 21.0% chromium, about 33.0% to 37.0% nickel, about 9.0% to about 10.5% molybdenum, up to about 1.0% titanium, up to about 0.015% boron, up to about 2% iron and the balance cobalt, and (b) explosive shock strengthening said product to effect non-directional cold working of the entire body of the tube.
Claim 12
Independent Claim
134 words
A method for producing a non-laminar tubular metal product suitable for use in sour gas wells and characterized by resistance to hydrogen sulfide embrittlement at temperatures up to about 600° F. comprising the steps of: (a) forming a non-laminar tubular metal member entirely from an alloy consisting essentially of up to about 0.035% maximum carbon, up to about 0.15% maximum silicon, up to about 0.15% maximum manganese, up to about 0.010% maximum sulfur, up to about 0.015% maximum phosphorus, about 19.0% to about 21.0% chromium, about 33.0% to 37.0% nickel, about 9.0% to about 10.5% molybdenum, up to about 1.0% titanium, up to about 0.015% boron, up to about 2% iron and the balance cobalt, and (b) explosive shock strengthening said product to effect non-directional cold working of the entire body of the tube.
Claim 13
Dependent Claim
17 words
The method as claimed in claim 10 wherein the product is heat treated following explosive shock strengthening.
Claim 14
Dependent Claim
88 words
A method as claimed in claim 10 wherein the alloy consists essentially of up to about 0.020% maximum carbon, lowest possible amount of silicon but not more than 0.15%, lowest possible amount of manganese but not more than 0.15%, lowest possible amount of sulfur but not more than 0.005%, lowest possible amount of phosphorus but not more than 0.010%, about 20.50% chromium, about 35.25% nickel, about 9.80% molybdenum, about 0.75% titanium, about 0.010% boron, lowest possible amount of iron but not more than 1% and the balance cobalt.
Claim 15
Dependent Claim
17 words
The method as claimed in claim 11 wherein the product is heat treated following explosive shock strengthening.
Claim 16
Dependent Claim
19 words
A method as claimed in claim 10 wherein the tubular product is cold work strengthened after explosive shock strengthening.
Claim 17
Dependent Claim
23 words
A method as claimed in claim 11 wherein the product is cold work strengthened after explosive shock strengthening and prior to heat treating.
Claim 18
Dependent Claim
23 words
A method as claimed in claim 14 wherein the tubular product is cold work strengthened sufficiently to improve product geometry and/or increase strength.
Claim 19
Dependent Claim
26 words
A method as claimed in claim 10 wherein the explosive shock strengthening step is carried out in the range of 250,000 to 1,500,000 p.s.i. peak pressure.
Claim 20
Dependent Claim
27 words
A method as claimed in claim 10 wherein the explosive shock strengthening step is carried out in the range of about 500,000 to 750,000 p.s.i. peak pressure.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-23 | 1982-10-23 | 1983-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-23 | 1986-10-23 | 1987-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-23 | 1990-10-23 | 1991-04-24 | $7700.00 | Window Closed / Lapsed |