Memory metal article
Assignee: Memry Corp
•
Filing: 1978-01-17
•
Granted: 1979-04-17
•
Expires: 1998-01-17
Abstract
Abstract The effective transition temperature from martensite to austenite in a dimensionally heat-recoverable memory metal member can be temporarily raised by applying a stress and maintaining the applied stress at a temperature below the raised transition temperature so that the memory metal remains substantially in the martensitic state. When it is desired to utilize the member the stress is removed at a temperature above the original transition temperature. The applied stress is advantageously maintained by a disburdenable keeper. In an especially preferred embodiment the keeper comprises an aluminium tube positioned within a band or tube made from a brass memory alloy, the combined article being suitable as a connector for hydraulic pipes and the like.
Inventors
- 👤 Robin J. T. Clabburn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:56
CPC Classifications
C; C22; C22F; C22F1/00; C22F1/006; F; F16; F16B; F16B2200/00; F16B2200/77; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49826; Y10T29/49863
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
77 words
A method of making a heat-recoverable memory metal member which comprises applying a stress to the member in its deformed dimensionally heat-unstable state so as temporarily to increase the A s value of the memory metal from T 1 to T 2 , and whilst maintaining an applied stress, storing the article at such a temperature less than T 2 and at such a maintained applied stress that the memory metal remains substantially in the martensitic state.
Claim 2
Independent Claim
77 words
A method of making a heat-recoverable memory metal member which comprises applying a stress to the member in its deformed dimensionally heat-unstable state so as temporarily to increase the A s value of the memory metal from T 1 to T 2 , and whilst maintaining an applied stress, storing the article at such a temperature less than T 2 and at such a maintained applied stress that the memory metal remains substantially in the martensitic state.
Claim 3
Dependent Claim
32 words
A method as claimed in claim 1, wherein the applied stress is applied at the same time as the stress applied to deform the memory metal member to its dimensionally heat-unstable state.
Claim 4
Dependent Claim
26 words
A method as claimed in claim 1, wherein the applied stress is applied after the memory metal member has been deformed to its dimensionally heat-unstable state.
Claim 5
Dependent Claim
18 words
A method as claimed in claim 1, wherein a disburdenable keeper is used to provide the applied stress.
Claim 6
Dependent Claim
14 words
A method as claimed in claim 4, wherein the keeper is destructible or deformable.
Claim 7
Dependent Claim
16 words
A method as claimed in claim 5, wherein the keeper is made from a fusible material.
Claim 8
Dependent Claim
17 words
A method as claimed in claim 5, wherein the keeper is made from a chemically degradable material.
Claim 9
Dependent Claim
29 words
A method as claimed in claim 5, wherein the keeper is insufficiently strong to withstand the recovery forces generated on heating the memory metal member to T 2 .
Claim 10
Dependent Claim
19 words
A method as claimed in claim 1, wherein the memory metal member is a radially expanded band or tube.
Claim 11
Dependent Claim
25 words
A method as claimed in claim 9, wherein a keeper in the form of a band or tube is positioned inside the memory metal member.
Claim 12
Dependent Claim
27 words
A method as claimed in claim 1, wherein the memory metal member is a hollow member having a discontinuity in its cross-section in the plane of recovery.
Claim 13
Dependent Claim
15 words
A method as claimed in claim 11, wherein a keeper is positioned inside said discontinuity.
Claim 14
Dependent Claim
24 words
A method as claimed in claim 1, wherein the memory metal member is stored at a temperature between M s and T 2 .
Claim 15
Dependent Claim
24 words
A method as claimed in claim 1, wherein the memory metal member is stored at a temperature between T 1 and T 2 .
Claim 16
Independent Claim
74 words
A method of making a heat-recoverable article which comprises imparting a thermally recoverable deformation to a memory metal member at a temperature below the normal transition temperature of the metal, the applied deforming stress also being sufficient to raise the transition temperature of the memory metal above the temperature at which the article is to be stored, maintaining the applied stress and storing the article at a temperature less than the raised transition temperature.
Claim 17
Independent Claim
74 words
A method of making a heat-recoverable article which comprises imparting a thermally recoverable deformation to a memory metal member at a temperature below the normal transition temperature of the metal, the applied deforming stress also being sufficient to raise the transition temperature of the memory metal above the temperature at which the article is to be stored, maintaining the applied stress and storing the article at a temperature less than the raised transition temperature.
Claim 18
Dependent Claim
17 words
A method as claimed in claim 15, wherein the applied stress is maintained using a disburdenable keeper.
Claim 19
Dependent Claim
28 words
A method as claimed in claim 16, wherein the keeper is insufficiently strong to withstand the recovery forces generated on heating the article to the raised transition temperature.
Claim 20
Dependent Claim
31 words
A method as claimed in claim 17, wherein the memory metal member is a radially recoverable band or tube and the keeper is a deformable band or tube positioned inside it.
Claim 21
Dependent Claim
15 words
A method as claimed in claim 15, wherein the memory metal is a nickel-titanium alloy.
Claim 22
Dependent Claim
14 words
A method as claimed in claim 15, wherein the memory metal is a brass.
Claim 23
Dependent Claim
28 words
A heat-recoverable article which comprises a dimensionally heat-recoverable memory metal member held in stress in a predominantly martensitic state with a raised transition temperature by a disburdenable keeper.
Claim 24
Dependent Claim
28 words
A heat-recoverable article which comprises a dimensionally heat-recoverable memory metal member held in stress in a predominantly martensitic state with a raised transition temperature by a disburdenable keeper.
Claim 25
Dependent Claim
35 words
A heat-recoverable article as claimed in claim 21, wherein the memory metal member is a band or tube made from a brass and the keeper is a band or tube of aluminium positioned within it.
Claim 26
Independent Claim
99 words
A method of making a connection using a device comprising a memory metal member, wherein a stress is applied to the member in its dimensionally heat-recoverable form so as temporarily to increase the A s temperature of the memory metal from T 1 to T 2 and, whilst maintaining a stress the article is stored at a temperature less than T 2 , the memory metal remaining substantially in the martensitic state during storage, and wherein immediately before connection the stress is removed at a temperature greater than T 1 so that the member recovers to make the connection.
Claim 27
Independent Claim
99 words
A method of making a connection using a device comprising a memory metal member, wherein a stress is applied to the member in its dimensionally heat-recoverable form so as temporarily to increase the A s temperature of the memory metal from T 1 to T 2 and, whilst maintaining a stress the article is stored at a temperature less than T 2 , the memory metal remaining substantially in the martensitic state during storage, and wherein immediately before connection the stress is removed at a temperature greater than T 1 so that the member recovers to make the connection.
Claim 28
Dependent Claim
16 words
A method as claimed in claim 23, wherein the stress is applied by a disburdenable keeper.
Claim 29
Dependent Claim
30 words
A method as claimed in claim 24, wherein the stress is removed by heating the article to T 2 so that the memory metal member recovers and deforms the keeper.
Claim 30
Dependent Claim
35 words
A method as claimed in claim 23, wherein the connection is made between two generally tubular substrates, the memory metal being in the form of a band or tube sized to fit about said substrates.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-16 | 1982-10-16 | 1983-04-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-16 | 1986-10-16 | 1987-04-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-16 | 1990-10-16 | 1991-04-17 | $7700.00 | Window Closed / Lapsed |