Preparation of melamine derivatives
Assignee: Sanofi Aventis Deutschland GmbH
•
Filing: 1978-02-06
•
Granted: 1979-03-06
•
Expires: 1998-02-06
Abstract
Abstract A process for the preparation of a substantially monomeric methylolmelamine etherified by methanol which contains per mol of melamine, more than 5 mols of formaldehyde and more than 4 mols of methyl-etherified methylol groups which has a viscosity of less than 10 Pa.s at 25° C. at a solids content of at least 95%, said process comprising reacting melamine and formaldehyde in a molar ratio of from 1 : 6.2 to 1 : 8, at a temperature of from 40 to 60° C., in the presence of a basic catalyst in a reaction mixture which contains from 10 to 40% by weight of water and from 40 to 20% by weight of methanol thereby producing a suspension of methylolmelamine, and then etherifying the methylol melamine in the presence of from 15 to 30 mols of methanol per mol of melamine, at a temperature of from 25 to 50° C., in the presence of a strong acid.
Inventors
- 👤 Hans Honel
- 👤 Karlfried Keller
- 👤 Walter Michel
- 👤 Manfred Schon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 13:28
CPC Classifications
C; C07; C07D; C07D251/00; C07D251/02; C07D251/12; C07D251/26; C07D251/40; C07D251/54; C07D251/64
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
158 words
A process for the preparation of a substantially monomeric methylolmelamine etherified by methanol which contains per mol of melamine, more than 5 mols of formaldehyde and more than 4 mols of methyl-etherified methylol groups which has a viscosity of less than 10 pascalseconds at 25° C. at a solids content of at least 95%, said process comprising reacting melamine and formaldehyde a molar ratio of from 1:6.2 to 1:8, at a temperature of from 40° to 60° C., in the presence of a basic catalyst in a reaction mixture which contains from 10 to 40% by weight of water and from 40 to 20% by weight of methanol thereby producing a suspension of methylolmelamine, and then without separating methylol melamine from the suspension etherifying the methylol melamine in the presence of from 15 to 30 mols of methanol per mol of melamine, at a temperature of from 25° to 50° C., in the presence of a strong acid.
Claim 2
Dependent Claim
158 words
A process for the preparation of a substantially monomeric methylolmelamine etherified by methanol which contains per mol of melamine, more than 5 mols of formaldehyde and more than 4 mols of methyl-etherified methylol groups which has a viscosity of less than 10 pascalseconds at 25° C. at a solids content of at least 95%, said process comprising reacting melamine and formaldehyde a molar ratio of from 1:6.2 to 1:8, at a temperature of from 40° to 60° C., in the presence of a basic catalyst in a reaction mixture which contains from 10 to 40% by weight of water and from 40 to 20% by weight of methanol thereby producing a suspension of methylolmelamine, and then without separating methylol melamine from the suspension etherifying the methylol melamine in the presence of from 15 to 30 mols of methanol per mol of melamine, at a temperature of from 25° to 50° C., in the presence of a strong acid.
Claim 3
Dependent Claim
22 words
A process according to claim 1, wherein melamine and formaldehyde are reacted together in a molar ratio of from 1:6.5 to 1:7.
Claim 4
Dependent Claim
21 words
A process according to claim 2 wherein melamine and formaldehyde are reacted at a temperature of from 45 to 55° C.
Claim 5
Dependent Claim
21 words
A process according to claim 1 wherein the etherification is carried out at a temperature of from 30° to 40° C.
Claim 6
Dependent Claim
58 words
A substantially monomeric methylolamine etherified by methanol which contains, per mol of melamine, more than 5 mols of formaldehyde and more than 4 mols of methyletherified methylol groups and which has a viscosity of less than 10 pa.s at 25° C. at a solids content of at least 95%, when prepared by the process according to claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-03-05 | 1982-09-04 | 1983-03-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-03-05 | 1986-09-04 | 1987-03-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-03-05 | 1990-09-04 | 1991-03-06 | $7700.00 | Window Closed / Lapsed |