Addition copolymers of lactide and glycolide and method of preparation
Assignee: Ethicon Inc
•
Filing: 1977-06-24
•
Granted: 1979-02-06
•
Expires: 1997-06-24
Abstract
Abstract Relatively high molecular weight, fiber-forming, crystalline copolymers of lactide and glycolide are prepared in a two-stage polymerization process. In the first stage there is prepared a random copolymer of a major proportion of an optically active lactide with a minor proportion of glycolide or d,l-lactide. In the second stage, a major amount of glycolide and a minor amount of lactide monomers are admixed with the copolymer of the first stage and the polymerization resumed until there is obtained a high molecular weight addition copolymer of lactide and glycolide containing from about 50 to 75 wt percent of units derived from glycolide. The polymer is fiber-forming and useful in the preparation of absorbable surgical sutures.
Inventors
- 👤 Yuzi Okuzumi
- 👤 A. Darline Mellon
- 👤 David Wasserman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 00:33
CPC Classifications
A; A61; A61L; A61L17/00; A61L17/06; A61L17/10; A61L17/12; C; C08; C08G; C08G63/00; C08G63/02; C08G63/06; C08G63/08
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
97 words
An absorbable surgical suture comprising at least one drawn and oriented filament of a crystalline copolymer of lactide and glycolide containing from about 50 to 75 percent glycolide, said suture having a crystallinity of at least 15 percent, an inherent viscosity of at least 1.0 as determined on a 0.1 percent solution in HFIP at 25° C., a straight tensile and and knot strength of at least 40,000 psi and 30,000 psi respectively, straight tensile strength retention in vivo of at least 40 percent after 14 days, and substantially complete absorption in vivo within about 120 days.
Claim 2
Dependent Claim
97 words
An absorbable surgical suture comprising at least one drawn and oriented filament of a crystalline copolymer of lactide and glycolide containing from about 50 to 75 percent glycolide, said suture having a crystallinity of at least 15 percent, an inherent viscosity of at least 1.0 as determined on a 0.1 percent solution in HFIP at 25° C., a straight tensile and and knot strength of at least 40,000 psi and 30,000 psi respectively, straight tensile strength retention in vivo of at least 40 percent after 14 days, and substantially complete absorption in vivo within about 120 days.
Claim 3
Dependent Claim
45 words
A suture of claim 1 wherein said crystalline copolymer is an addition product of (a) a random copolymer of lactide and glycolide containing from 60 to 90 percent lactide, and (b) a mixture of lactide and glycolide monomers containing from 70 to 90 percent glycolide.
Claim 4
Dependent Claim
10 words
A suture of claim 2 wherein the lactide is L(-)-lactide.
Claim 5
Dependent Claim
45 words
A suture of claim 1 wherein said crystalline copolymer is an addition product of (a) a random copolymer of L(-)-lactide and d,l-lactide containing from 60 to 90 percent L(-)-lactide, and (b) a mixture of L(-)-lactide and glycolide monomers containing from 70 to 90 percent glycolide.
Claim 6
Dependent Claim
169 words
A synthetic absorbable suture comprising at least one drawn and oriented filament of a crystalline copolymer of lactide and glycolide containing from 50 to 75 wt percent glycolide, said copolymer being prepared by a process which comprises: (a) preparing a random copolymer comprising a major portion of an optically active lactide and a minor portion of a monomer selected from the group consisting of glycolide and d,l-lactide, and (b) admixing with said random copolymer additional monomers comprising from 70 to 90 wt percent glycolide and 10 to 30 wt percent of an optically active lactide, the quantity of glycolide being sufficient to provide from 50 to 75 wt percent glycolide in the polymer-monomer mixture, and (c) polymerizing said polymer-monomer mixture to obtain said crystalline copolymer of lactide and glycolide, said copolymer having an inherent viscosity determined as a 0.1 percent solution in hexafluoroisopropanol at 25° C. of at least about 1.20, a melting point of at least about 160° C. and a crystallinity of at least about 15 percent.
Claim 7
Dependent Claim
169 words
A synthetic absorbable suture comprising at least one drawn and oriented filament of a crystalline copolymer of lactide and glycolide containing from 50 to 75 wt percent glycolide, said copolymer being prepared by a process which comprises: (a) preparing a random copolymer comprising a major portion of an optically active lactide and a minor portion of a monomer selected from the group consisting of glycolide and d,l-lactide, and (b) admixing with said random copolymer additional monomers comprising from 70 to 90 wt percent glycolide and 10 to 30 wt percent of an optically active lactide, the quantity of glycolide being sufficient to provide from 50 to 75 wt percent glycolide in the polymer-monomer mixture, and (c) polymerizing said polymer-monomer mixture to obtain said crystalline copolymer of lactide and glycolide, said copolymer having an inherent viscosity determined as a 0.1 percent solution in hexafluoroisopropanol at 25° C. of at least about 1.20, a melting point of at least about 160° C. and a crystallinity of at least about 15 percent.
Claim 8
Dependent Claim
39 words
The suture of claim 5 wherein said random copolymer comprises from 60 to 90 wt percent of optically active lactide and from 10 to 40 wt percent of another monomer selected from the group consisting of glycolide and d,l-lactide.
Claim 9
Dependent Claim
18 words
The suture of claim 6 wherein the optically active lactide is L(-)-lactide and the other monomer is glycolide.
Claim 10
Dependent Claim
26 words
The suture of claim 7 wherein the random copolymer comprises from 65 to 75 wt percent of L(-)-lactide and from 25 to 35 mole percent glycolide.
Claim 11
Dependent Claim
18 words
The suture of claim 6 wherein the optically active lactide is L(-)-lactide and the other monomer is d,l-lactide.
Claim 12
Dependent Claim
26 words
The suture of claim 9 wherein the random copolymer comprises from 65 to 75 wt percent of L(-)-lactide and from 25 to 35 wt percent d,l-lactide.
Claim 13
Dependent Claim
21 words
The suture of claim 5 wherein the optically active lactide admixed with the random copolymer according to Step (b) is L(-)-lactide.
Claim 14
Dependent Claim
37 words
The suture of claim 11 wherein the mixture of L(-)-lactide and glycolide admixed with the random copolymer according to Step (b) comprises from 80 to 90 wt percent glycolide and from 10 to 20 wt percent L(-)-lactide.
Claim 15
Dependent Claim
177 words
A surgical prosthesis comprising a fabric manufactured at least in part from synthetic absorbable fibers comprising drawn and oriented filaments of a crystalline copolymer of lactide and glycolide containing from 50 to 75 wt percent glycolide, said copolymer being prepared by a process which comprises: (a) preparing a random copolymer comprising a major portion of an optically active lactide and a minor portion of a monomer selected from the group consisting of glycolide and d,l-lactide, and (b) admixing with said random copolymer additional monomers comprising from 70 to 90 wt percent glycolide and 10 to 30 wt percent of an optically active lactide, the quantity of glycolide being sufficient to provide from 50 to 75 wt percent glycolide in the polymer-monomer mixture, and (c) polymerizing said polymer-monomer mixture to obtain said crystalline copolymer of lactide and glycolide, said copolymer having an inherent viscosity determined as a 0.1 percent solution in hexafluoroisopropanol at 25° C. of at least about 1.20, a melting point of at least about 160° C., and a crystallinity of at least about 15 percent.
Claim 16
Dependent Claim
177 words
A surgical prosthesis comprising a fabric manufactured at least in part from synthetic absorbable fibers comprising drawn and oriented filaments of a crystalline copolymer of lactide and glycolide containing from 50 to 75 wt percent glycolide, said copolymer being prepared by a process which comprises: (a) preparing a random copolymer comprising a major portion of an optically active lactide and a minor portion of a monomer selected from the group consisting of glycolide and d,l-lactide, and (b) admixing with said random copolymer additional monomers comprising from 70 to 90 wt percent glycolide and 10 to 30 wt percent of an optically active lactide, the quantity of glycolide being sufficient to provide from 50 to 75 wt percent glycolide in the polymer-monomer mixture, and (c) polymerizing said polymer-monomer mixture to obtain said crystalline copolymer of lactide and glycolide, said copolymer having an inherent viscosity determined as a 0.1 percent solution in hexafluoroisopropanol at 25° C. of at least about 1.20, a melting point of at least about 160° C., and a crystallinity of at least about 15 percent.
Claim 17
Dependent Claim
172 words
A surgical prosthesis comprising a solid surgical aid cast or machined from an absorbable polymer comprising a crystalline copolymer of lactide and glycolide containing from 50 to 75 wt percent glycolide, said copolymer being prepared by a process which comprises: (a) preparing a random copolymer comprising a major portion of an optically active lactide and a minor portion of a monomer selected from the group consisting of glycolide and d,l-lactide, and (b) admixing with said random copolymer additional monomers comprising from 70 to 90 wt percent glycolide and 10 to 30 wt percent of an optically active lactide, the quantity of glycolide being sufficient to provide from 50 to 75 wt percent glycolide in the polymer-monomer mixture, and (c) polymerizing said polymer-monomer mixture to obtain said crystalline copolymer of lactide and glycolide, said copolymer having an inherent viscosity determined as a 0.1 percent solution in hexafluoroisopropanol at 25° C. of at least about 1.20, a melting point of at least about 160° C., and a crystallinity of at least about 15 percent.
Claim 18
Dependent Claim
172 words
A surgical prosthesis comprising a solid surgical aid cast or machined from an absorbable polymer comprising a crystalline copolymer of lactide and glycolide containing from 50 to 75 wt percent glycolide, said copolymer being prepared by a process which comprises: (a) preparing a random copolymer comprising a major portion of an optically active lactide and a minor portion of a monomer selected from the group consisting of glycolide and d,l-lactide, and (b) admixing with said random copolymer additional monomers comprising from 70 to 90 wt percent glycolide and 10 to 30 wt percent of an optically active lactide, the quantity of glycolide being sufficient to provide from 50 to 75 wt percent glycolide in the polymer-monomer mixture, and (c) polymerizing said polymer-monomer mixture to obtain said crystalline copolymer of lactide and glycolide, said copolymer having an inherent viscosity determined as a 0.1 percent solution in hexafluoroisopropanol at 25° C. of at least about 1.20, a melting point of at least about 160° C., and a crystallinity of at least about 15 percent.
References Cited (Backward Citations)
US3297033A
Cited
US3442871A
Cited
US3422181A
Cited
US3636956A
Cited
US3867190A
Cited
US3839297A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-05 | 1982-08-07 | 1983-02-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-05 | 1986-08-07 | 1987-02-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-05 | 1990-08-07 | 1991-02-06 | $7700.00 | Window Closed / Lapsed |