Pressure-sensitive adhesive and vinyl acetate-ethylene copolymer emulsion useful as base material therefor
Assignee: Sumitomo Chemical Co Ltd
•
Filing: 1977-04-20
•
Granted: 1978-12-05
•
Expires: 1997-04-20
Abstract
Abstract A pressure-sensitive adhesive containing a base material therefore comprising an aqueous emulsion of vinyl acetate-ethylene copolymer having an ethylene content of 15 to 40% by weight, preferably 20 to 35% by weight, the benzene-insoluble part of less than 30% by weight, preferably less than 20% by weight, and an intrinsic viscosity of the benzene-soluble part of 0.4 to 1.4 dl/g, preferably 0.6 to 1.0 dl/g, (at 30 DEG C) which is prepared by the emulsion copolymerization of vinyl acetate and ethylene and optionally at least one unsaturated monovinyl monomer in the presence of a protective colloid and a polyoxyethylenic nonionic sulfactant, or a base material comprising a blend of said aqueous emulsion of vinyl acetate-ethylene copolymer as set forth above and an emulsion of an acrylic ester copolymer; and the aqueous emulsion of vinyl acetate-ethylene copolymer useful as the base material for the pressure-sensitive adhesive.
Inventors
- 👤 Takeo Oyamada
- 👤 Choji Tomizawa
- 👤 Masahiro Domoto
- 👤 Shizuo Narisawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 17:29
CPC Classifications
C; C08; C08F; C08F218/00; C08F218/02; C08F218/04; C08F218/08; C09; C09J; C09J131/00; C09J131/02; C09J131/04; C08L; C08L2666/00; C08L2666/02; C08L2666/14; C08L71/00; C08L71/02; C09J2301/00; C09J2301/30; C09J2301/302; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31855; Y10T428/31938
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
139 words
A pressure-sensitive adhesive containing a base material therefor comprising an aqueous emulsion of vinyl acetate-ethylene copolymer having an ethylene content of 20 to 35% by weight, the benzene-insoluble part of less than 20% by weight and an intrinsic viscosity of the benzene-soluble part of 0.6 to 1.0 dl/g (at 30° C.) which is prepared by the emulsion copolymerization of vinyl acetate monomer and ethylene monomer in the presence of 0.1 to 1% by weight of a protective colloid and 1 to 8% by weight of a polyoxyethylenic nonionic surfactant, based on the total weight of the monomers, at a temperature of 30-60° C. and under a pressure of 30 to 100 kg/cm 2 , wherein at least 50% by weight of the vinyl acetate monomer is added uniformly and continuously to the emulsion polymerization system during the emulsion polymerization.
Claim 2
Dependent Claim
139 words
A pressure-sensitive adhesive containing a base material therefor comprising an aqueous emulsion of vinyl acetate-ethylene copolymer having an ethylene content of 20 to 35% by weight, the benzene-insoluble part of less than 20% by weight and an intrinsic viscosity of the benzene-soluble part of 0.6 to 1.0 dl/g (at 30° C.) which is prepared by the emulsion copolymerization of vinyl acetate monomer and ethylene monomer in the presence of 0.1 to 1% by weight of a protective colloid and 1 to 8% by weight of a polyoxyethylenic nonionic surfactant, based on the total weight of the monomers, at a temperature of 30-60° C. and under a pressure of 30 to 100 kg/cm 2 , wherein at least 50% by weight of the vinyl acetate monomer is added uniformly and continuously to the emulsion polymerization system during the emulsion polymerization.
Claim 3
Dependent Claim
78 words
The pressure-sensitive adhesive according to claim 1, wherein the vinyl acetate-ethylene copolymer is a copolymer prepared by copolymerizing together with vinyl acetate and ethylene 0.1 to 5% by weight (based on the weight of the vinyl acetate-ethylene copolymer) of at least one unsaturated monovinyl monomer selected from the group consisting of an unsaturated monovinyl monomer having a glycidyl group, an unsaturated monovinyl monomer having an N-methylol or alkoxy group and an unsaturated monovinyl monomer having a carboxyl group.
Claim 4
Dependent Claim
58 words
The pressure-sensitive adhesive according to claim 1, wherein the base material for the pressure-sensitive adhesive comprises a blend of 5 to 35 parts by weight (as the solid component) of the vinyl acetate-ethylene copolymer emulsion as set forth in claim 1 and 100 parts by weight (as the solid component) of an emulsion of an acrylic ester copolymer.
Claim 5
Dependent Claim
58 words
The pressure-sensitive adhesive according to claim 1, wherein the base material for the pressure-sensitive adhesive comprises a blend of 10 to 25 parts by weight (as the solid component) of the vinyl acetate-ethylene copolymer emulsion as set forth in claim 1 and 100 parts by weight (as the solid component) of an emulsion of an acrylic ester copolymer.
Claim 6
Dependent Claim
60 words
The pressure-sensitive adhesive of claim 1, wherein the protective colloid is a nonionic water-soluble high molecular weight compound selected from the group consisting of a polyvinyl alcohol, a partially hydrolyzed polyvinyl alcohol having a saponification degree of at least 60 mole % and a degree of polymerization of 300 to 2,700, methyl cellulose, ethyl cellulose, hydroxyethyl cellulose, and carboxymethyl cellulose.
Claim 7
Dependent Claim
50 words
The pressure sensitive adhesive of claim 1, wherein the polyoxyethylenic nonionic surfactant is selected from the group consisting of polyoxyethylene lauryl ether, polyoxyethylene octylphenol ether, polyoxyethylene nonylphenol ether, polyoxyethylene sorbitan monolaurate, polyoxyethylene sorbitan monooleate and polyoxyethylene polyoxypropylene block copolymers having an ethylene oxide addition of 10 to 80 mol %.
References Cited (Backward Citations)
US3404113A
Cited
US3440200A
Cited
US3475363A
Cited
US3457209A
Cited
US3708388A
Cited
US3707518A
Cited
US3637428A
Cited
US3692723A
Cited
US3637615A
Cited
US3671382A
Cited
US3806484A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-12-04 | 1982-06-05 | 1982-12-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-12-04 | 1986-06-05 | 1986-12-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-12-04 | 1990-06-05 | 1990-12-05 | $7700.00 | Window Closed / Lapsed |