Assignee: Battelle Development Corp
•
Filing: 1976-11-30
•
Granted: 1978-11-07
•
Expires: 1996-11-30
Abstract
Abstract The invention comprises methods and apparatus for forming filamentary material directly from a pendant drop of molten material, and provides for a significant improvement in the quench rate. A typical method of making filamentary material according to the invention, comprises the steps of: (a) heating a solid material, typically, a metal or metal alloy, so as to form a pendant molten drop of the material which is at a temperature within 25 percent of its equilibrium melting point in °K, said molten material having a surface tension of 10 to 2500 dynes/cm. and a viscosity of 0.001 to 1.0 poise at said temperature; (b) rotating a hollow cylindrical member about its longitudinal axis at a peripheral speed in excess of 3 feet per second, said member having a circumferential, heat-extracting lip projecting from its inner periphery, and said lip having a narrow peripheral edge of arcute cross section; and, (c) bringing the surface of said pendant molten material drop and said peripheral edge of the lip into contact so as to withdraw a solidifying filament from the drop while maintaining the form and stability of the drop. Typically, said lip is located at one end of said cylindrical member. The heat-extracting lip may typically be substantially V-shaped, with the apical region of the V-shape comprising said narrow peripheral edge of the lip; and typically, said edge may possess at least one indentation disposed to attenuate said filamentary material into discontinuous fiber.
Inventors
- 👤 Robert E. Maringer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 01:15
CPC Classifications
B; B22; B22D; B22D11/00; B22D11/005; B22D11/06; B22D11/0611; B22D11/062
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
150 words
A method of making filamentary material, comprising the steps of: (a) heating a solid material so as to form a pendant molten drop of the material which is at a temperature within 25 percent of its equilibrium melting point in ° K, said molten material having a surface tension of 10 to 2500 dynes/cm. and a viscosity of 0.001 to 1.0 poise at said temperature; (b) rotating a hollow cylindrical member about its longitudinal axis at a peripheral speed in excess of 3 feet per second, said member having a circumferential, heat-extracting lip projecting from its inner periphery, and said lip having a narrow peripheral edge of arcuate cross section; and, (c) bringing the surface of said pendant molten drop and said peripheral edge of the heat-extracting lip into contact so as to spontaneously withdraw a solidifying filament from the drop while maintaining the form and stability of the drop.
Claim 2
Independent Claim
150 words
A method of making filamentary material, comprising the steps of: (a) heating a solid material so as to form a pendant molten drop of the material which is at a temperature within 25 percent of its equilibrium melting point in ° K, said molten material having a surface tension of 10 to 2500 dynes/cm. and a viscosity of 0.001 to 1.0 poise at said temperature; (b) rotating a hollow cylindrical member about its longitudinal axis at a peripheral speed in excess of 3 feet per second, said member having a circumferential, heat-extracting lip projecting from its inner periphery, and said lip having a narrow peripheral edge of arcuate cross section; and, (c) bringing the surface of said pendant molten drop and said peripheral edge of the heat-extracting lip into contact so as to spontaneously withdraw a solidifying filament from the drop while maintaining the form and stability of the drop.
Claim 3
Dependent Claim
17 words
The method of claim 1, wherein said lip is located at one end of said cylindrical member.
Claim 4
Dependent Claim
20 words
The method of claim 1, wherein said drop is formed by melting one end of a rod of solid material.
Claim 5
Dependent Claim
27 words
The method of claim 1, wherein said heat-extracting lip is substantially V-shaped, with the apical region of the V-shape comprising said narrow peripheral edge of the lip.
Claim 6
Dependent Claim
40 words
The method of claim 4, wherein the radius of curvature of said arcuate edge is in the range from about 0.0005 inch to 0.10 inch and the filamentary material has an effective cross sectional area less than 0.003 square inches.
Claim 7
Dependent Claim
37 words
The method of claim 1, wherein said edge possesses at least one indentation disposed to attenuate said filamentary material into discontinuous fiber, with each fiber having a length approximating the distance along the edge between said indentations.
Claim 8
Dependent Claim
33 words
The method of claim 2, wherein subsequent to its release from said edge the filamentary material is directed by a guide means into said hollow cylindrical member and away from said heat-extracting lip.
Claim 9
Dependent Claim
20 words
The method of claim 2, wherein the filamentary material is collected on a spindle extending into the hollow cylindrical member.
Claim 10
Dependent Claim
10 words
The method of claim 8, wherein said spindle is rotating.
Claim 11
Dependent Claim
50 words
The method of claim 2, wherein the end of the hollow cylindrical member having no heat-extracting lip is enclosed, thereby forming a cup-like structure, and said member is rotated about a shaft attached to the outer periphery of said enclosed end and extending along the longitudinal axis of said member.
Claim 12
Dependent Claim
15 words
The method of claim 1, wherein said solid material is a metal or metal alloy.
Claim 13
Independent Claim
158 words
A method of making filamentary material comprising the steps of: (a) providing a pendant drop of molten material protruding from an orifice, said material being at a temperature within 25 percent of its equilibrium melting point in ° K and having a surface tension of 10 to 2500 dynes/cm and a viscosity of 0.001 poise at said temperature and said drop having a shape determined by the surface tension of said molten material; (b) rotating a hollow cylindrical member about its longitudinal axis at a peripheral speed in excess of 3 feet per second, said member having a circumferential, heat-extracting lip projecting from its inner periphery, and said lip having a narrow peripheral edge of arcuate cross section; and, (c) bringing the surface of said pendant molten drop and said peripheral edge of the heat-extracting lip into contact so as to spontaneously withdraw a solidifying filament from the drop while maintaining the form and stability of the drop.
Claim 14
Independent Claim
158 words
A method of making filamentary material comprising the steps of: (a) providing a pendant drop of molten material protruding from an orifice, said material being at a temperature within 25 percent of its equilibrium melting point in ° K and having a surface tension of 10 to 2500 dynes/cm and a viscosity of 0.001 poise at said temperature and said drop having a shape determined by the surface tension of said molten material; (b) rotating a hollow cylindrical member about its longitudinal axis at a peripheral speed in excess of 3 feet per second, said member having a circumferential, heat-extracting lip projecting from its inner periphery, and said lip having a narrow peripheral edge of arcuate cross section; and, (c) bringing the surface of said pendant molten drop and said peripheral edge of the heat-extracting lip into contact so as to spontaneously withdraw a solidifying filament from the drop while maintaining the form and stability of the drop.
Claim 15
Dependent Claim
15 words
The method of claim 12, wherein said molten material is a metal or metal alloy.
Claim 16
Dependent Claim
37 words
The method of claim 12, wherein said edge possesses at least one indentation disposed to attenuate said filamentary material into discontinuous fiber, with each fiber having a length approximating the distance along the edge between said indentations.
References Cited (Backward Citations)
US2825108A
Cited
US3838185A
Cited
US3904344A
Cited
US3861450A
Cited
US3896203A
Cited
US3863700A
Cited
US3843762A
Cited
US3881540A
Cited
US3881542A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-06 | 1982-05-08 | 1982-11-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-06 | 1986-05-08 | 1986-11-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-06 | 1990-05-08 | 1990-11-07 | $7700.00 | Window Closed / Lapsed |